• Journal of Powder Materials
• /
• v.11 no.1
• /
• pp.69-73
• /
• 2004

The sintering characteristics of commercial 7xxx series Al-Zn-Mg-Cu alloy have been investigated. Sintering system of this blended elemental powder has aspects of both transient and supersolidus liquid phase sintering. Transient liquids occur when the constitution point during sintering lies in a solid phase region but where the sintering temperature is greater than either the melting point of one of the constituent or a eutectic temperature. Supersolidus liquid phase sintering occurs when a preblended powder is heated to a temperature between the solidus and liquids. However, these reaction were restrained their inter diffusion due to the appearance of the oxide film. Thus, 7xxx series Al alloy is extremely sensitive to process variables, including particle size, holding time and sintering temperature. Therefore, above phenomenons were observed formation and behaviour of the liquid by using SEM and DSC.

• Transactions of Materials Processing
• /
• v.13 no.1
• /
• pp.53-58
• /
• 2004

The microstructural changes of Al-Zn-Mg-Cu alloy containing Sc during hot extrusion and post heat treatment were investigated. Two kinds of Al-Sc alloys with different alloying elements (B1, B2) were hot extruded to make T-shape bars at extrusion temperature of $380^{\circ}C$, then the bars were solution treated at $480^{\circ}C$ for 2hrs followed by artificial aging at $120^{\circ}C$ for 24hrs. The interior microstructure of as extruded bar consisted of elongated grains, however, fine equiaxed grains were also observed around surface. The microstructural gradient suggested that different restoration process could proceed during the hot extrusion. For B1 and B2, different grain growth behaviors were found around the surface during the post heat treatment. Rapid grain growth behavior was observed for B1 around the surface, however, it was not observed for B2. Orientation pinning, which was related with the evolution of preferred orientation, and precipitation were thought to be responsible for the rapid grain growth.

• Journal of Welding and Joining
• /
• v.19 no.4
• /
• pp.429-436
• /
• 2001

The effect of welding condition on the microstructures of the weld metal in A7N01 welded by $CO_2$ laser was investigated. The number of ripples was increased with decreasing power and increasing welding speed. In the bead without ripple lines, the subgrain microstructures distribution from the fusion line toward the center of the bead were in the order of cellular, dendritic and equiaxed dendrite. However, in the bead with ripple lines, cellular and dendritic were formed between the fusion boundary and the ripple line. Inaddition, those structures were also observed between the ripple line. Equiaxed dendrites were formed only at the center line region. Cellular and dendritics formed near the ripple line were larger than those formed near the fusion boundary. The cooling rates estimated by the dendrite arm spacing were in the range of 200 to 1150oC/s. Cooling rate was increased with decreasing the power and increasing the welding speed. Mg and Zn segregated at the boundaries of cellulars and dendritics, Mg was segregated more than Zn. The segregation of Mg and Zn decreased with increasing cooling rate. Hardness of the weld metal was lower than that of the base metal in all welding conditions and increased as the cooling rate increased.

• Journal of Korea Foundry Society
• /
• v.34 no.3
• /
• pp.87-93
• /
• 2014

Thixo-extrusion of semi-solid 7075 aluminum alloy and the mechanical properties of its extrudates were investigated. The semisolid alloy was prepared by a cooling slope cast. In other to perform thixo-extrusion, semi-solid 7075 aluminum alloy billets were reheated at the reheating conditions reported in a previous study. The maximum extrusion pressure in thixo-extrusion was 615MPa. This was lower than that of conventional hot extrusion ($P_{max}=940MPa$) at the same extrusion conditions due to the increased fluidity of the alloy billet in the semi-solid state. The values of Rockwell hardness (scale B) at the extrusion direction of the as thixoextruded bar were 48~53HRB and the difference in Rockwell hardness between the transverse direction and the extrusion direction was 5HRB or less. The results show that thxio-extrusion of semi-solid 7075 Al alloy improves the workability and anisotropic with the extrusion direction compared with hot extrusion of the conventional alloy.

• Korean Journal of Materials Research
• /
• v.20 no.2
• /
• pp.65-71
• /
• 2010

In this study, the effect of Sn and Mg on microstructure and mechanical properties of Cu-Fe-P alloy were investigated by using scanning electron microscope, transmission electron microscope, tensile strength, electrical conductivity, thermal softening, size and distribution of the precipitation phases in order to satisfy characteristic for lead frame material. It was observed that Cu-0.14wt%Fe-0.03wt%P-0.05wt%Si-0.1wt%Zn with Sn and Mg indicates increasing tensile strength compare with PMC90 since Sn restrained the growth of the Fe-P precipitation phase on the matrix. However, the electrical conductivity was decreased by adding addition of Sn and Mg because Sn was dispersed on the matrix and restrained the growth of the Fe-P precipitation. The size of 100 nm $Mg_3P_2$ precipitation phase was observed having lattice parameter $a:12.01{\AA}$ such that [111] zone axis. According to the results of the study, the tensile strength and the electrical conductivity satisfied the requirements of lead frame; so, there is the possibility of application as a substitution material for lead frame of Cu alloy.

• Korean Journal of Materials Research
• /
• v.6 no.10
• /
• pp.1043.1-1048
• /
• 1996

알루미나 매트릭스 복합재료를 AIZnMg(7075)-합금의 직접적인 용융산화를 통하여 제조하였다. 충전재료는 17$\mu\textrm{m}$ 크기의 모서리가 둥근 연마재용 SiC 입자를 사용하였다. 산화촉진재 SiO2를 사용한 경우와 사용하지 않은 경우를 비교하였다. 매트릭스 형성 매카니즘과 반응거동을 온도와 SiO2사용량을 중심으로 연구하였으며, 얻어진 AI2O3/SiC/금속 복합재료의 미세구조를 관찰하였다.

• Journal of Korea Foundry Society
• /
• v.32 no.2
• /
• pp.98-103
• /
• 2012

Recently, development of Al-based alloys for high mechanical performance has been an important issue in automotive industry. The present study focused on the design of a high strength Al-based alloy for rheo-diecasting. The research was based on thermodynamic calculation and experimentals to optimize the alloy compositions. Two important considerations were carried out: i) to obtain uniform slurry with fine and globular microstructures for rheo-diecasting, ii) to be strengthend by T6 heat treatment. In order to evaluate the effect of Si content on the slurry microstructure and castability, thermodynamic calculation and fluidity test were carried out. The effects of various alloying components, such as Mg, Cu and Zn, on age hardenability were also investigated. The mechanical properties of the rheo-diecasting products using the newly developed alloy are 324MPa in tensile strength, 289MPa in yield strength, and 11.2% in elongation after T6 heat treatment.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.2
• /
• pp.68-72
• /
• 2015

The corrosion behavior of metals and alloys for the safety of offshore structures in seawater was investigated for the application of sacrificial anodes. The experiments were focused on the polarization behaviors and the surface morphology of each metal after experiments. Pure Zn, pure Al (Al1050), Al alloys (Al5052, Al6061), Mg alloys (AZ31, AZ91D) and steel (SCM440) were assessed in 3.5% sodium chloride solution by means of potentiodynamic polarization to verify the galvanic corrosion potential ($E_{couple}$). Potentiostat plots were plotted to compare the surface and corrosion current density ($i_{couple}$) of metals as sacrificial anodes in seawater to protect steel alloy as a cathode. Al alloys showed the best performance as a sacrificial anode, on the other hand, Mg alloys showed overprotection behavior. The surface morphologies of sacrificial anodes were observed by FESEM and compared.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.226-226
• /
• 2009

일반적으로 알루미늄이나 아연 등과 같은 이온화 경향이 큰 금속들은 그 자체의 활성적인 특성으로 인해 강재와 같은 이온화 경향이 낮은 금속재의 표면에 도금 또는 코팅함으로서 사용 환경 중 자체 내식성 보유와 더불어 손상 결함시 희생양극적인 역할 등의 잇점으로 많이 사용되고 있다. 본 연구에서는 DC 스퍼터링법에 의해 표면조직이 치밀한 여러 가지의 Zn-Mg 합금박막을 제작하였다. 이들 박막은 종래의 Zn도금에 비해 부식환경 중 장기간 갈바닉쌍을 형성하여 모재 금속에 대한 보호막 기능을 우수하게 하는 것으로 나타났다.

• The Korean Journal of Malacology
• /
• v.30 no.4
• /
• pp.353-361
• /
• 2014

In order to investigate the effects of copper alloy on abalone physiology, we studied survival rate, respiration, excretion rate, and heavy metal accumulation in each organ of adults and spats. The survival rate of spats and adults showed 27-60% and 63-83% respectively, higher survival rate in adults. In particular, 100% of copper panel led to lowest survival rate and there was no sharp distinction according to copper alloy composition. The respiration rate and excretion rate of ammonia nitrogen was $1.81mgO_2/g$ D.W./h and 0.43 mg $NH_4-N/g$ D.W./h respectively at 100% of copper panel. In other words, there was a high significant difference at the level, but no significant difference at other test levels (P < 0.05). The atomic ratio (0: N) hit the lowest at the 100% of copper panel showing 3.79 and no significant differences were seen among other test groups with 6.57-7.18 of a very low range. This means that the species might have undergone nutritional stress. In case of copper accumulation, the 100% copper panel group showed the highest level in hepatopancreas and muscle showing 6.91 mg/kg and 1.60 mg/kg respectively but the rest of groups showed similar levels. Zinc accumulation raised at Cu-Zn alloy panel had high significance showing 18.50 mg/kg and 1.10 mg/kg in hepatopancreas and muscle respectively (P < 0.05). To sum up, a cage net made of 100% pure copper is expected to have a negative effect on abalone in light of survival rate, heavy metal accumulation, and atomic ratio (0: N). Moreover, given that the substratum used for the high adhesive species and nutritious stress that is represented through the atomic ratio need to be considered, the copper alloy net is thought not to be suitable for abalone aquaculture.