• Journal of the Korean institute of surface engineering
• /
• v.54 no.4
• /
• pp.184-193
• /
• 2021

This study demonstrates formation behavior and morphological changes of PEO (Plasma Electrolytic Oxidation) films on AZ91 Mg alloy as a function of pre-treatment time in 1 M HF solution at 25 ± 1 ℃. The electrochemical behavior and morphological changes of AZ91 Mg alloy in the pre-treatment solution were also investigated with pre-treatment time. The PEO films were formed on the pre-treated AZ91 Mg alloy specimen by the application of anodic current 100 mA/cm² of 300 Hz AC in 0.1 M NaOH + 0.4 M Na₂SiO₃ solution. Vigorous generation of hydrogen bubbles were observed upon immersion in the pre-treatment solution and its generation rate decreased with immersion time. It was also found that 𝛽-Mg₁₇Al₁₂ in AZ91 Mg alloy was dissolved and a protective thin film of MgF₂ was formed on the AZ91 Mg alloy surface during the pre-treatment process in the 1 M HF solution. PEO film did not grow on the AZ91 Mg alloy specimen when the surface was not pre-treated and irregular PEO films with nodular defects were formed for the specimens pre-treated up to 1 min. Uniform PEO films were formed when the AZ91 Mg alloy specimen was pre-treated more than 3 min. The growth rate of PEO films on AZ91 Mg alloy increased significantly with increasing pre-treatment time.

• Korean Journal of Materials Research
• /
• v.17 no.12
• /
• pp.648-653
• /
• 2007

Plasma electrolytic oxidation (PEO) treatment was performed on cast Mg-6 wt%Al alloy solution-treated at 693K for 16h and aged at 498K. The surface roughness, thickness, micro-hardness, wear and corrosion properties of coatings on solution-treated and aged Mg-6 wt%Al alloy were investigated. The coatings on aged Mg-6 wt%Al alloy had thinner layer and lower micro-hardness and wear resistance than the solution-treated Mg-6 wt%Al alloy. As the aging time increased, the thickness of coatings decreased while the surface roughness was almost no changed. In addition, the micro-hardness and wear property of coatings decreased with increasing the aging time unlike the uncoated Mg-6 wt%Al alloy showing the peak micro-hardness and the best wear property after aging for 16 h. However, the coatings on Mg-6 wt%Al alloy peak-aged for 16h revealed the best corrosion resistance in 3.5% NaCl solution, which was explained based on the microstructural characteristics.

• Journal of the Korean Ceramic Society
• /
• v.35 no.3
• /
• pp.303-309
• /
• 1998

The fabrication of Al2O3/Al composite by pressureless infiltration was investigated by the change of Mg and Si content in Al alloy infiltration process and infiltration atmosphere. The effect of alloying elements infiltration atmosphere and interfacial reactants between Al alloy matrix and Al2O3 particles were in-vestigated in terms of bendingstrength and harness test,. The fabrication of Al2O3/Al composite by the vestigated in terms of bending strength and hardness test. The fabrication of Al2O3/Al composite by the pressureless infiltration was done in nitrogen atmosphere with Mg in Al alloy. It was successfully fabricated at $700^{\circ}C$ according to Mg contents in Al alloy and infiltration condition. Because Mg in the Al alloy and ni-trogen atmosphere of infiltratio condition produced Mg-N compound(Mg3N2) it decreased the wetting an-gle between molten Al alloy and Al2O3 particles by coating on surface of Al2O3 particles. The fracture strength of Al2O3/Al-Mg composite was 800MPa and Al2O3/Al-Si-Mg composite was 400MPa. Si in Al alloy decreased the interfacial strength between Al alloy matrix and Al2O3 particles.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.144-149
• /
• 2000

Variables affecting the passivation capability of Cu(Mg) alloy films, which were sputter deposited from a Cu (4.5 at. %) target, have been investigated. The results show that the passivation capability of a Cu(Mg) alloy film is a function of annealing temperature, $O_2$ pressure, and Mg content in the film. Increasing the annealing temperature up to $500^{\circ}C$ favors formation of a dense MgO layer on the surface which has a growth limited thickness of 150 $\AA$. Decreasing the $O_2$ pressure enhances the preferential oxidation of Mg over Cu. Furthermore, increasing the Mg content in the Cu(Mg) film promotes formation of a dense MgO layer. Vacuum pre-annealing was found to be very effective in segregating Mg to the surface, facilitating the passivation capability of the Cu(Mg) alloy film even when the Mg content is low. In the current study, self-aligned MgO layers with low resistivity and an effective passivation capability over the Cu surface, have been obtained by manipulating these factors when Cu(Mg) thin films are annealed.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.5
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.194-195
• /
• 2005

(100-x)Zn xMg alloy films are prepared onto cold-rolled steel substrates; where x ranged from 0 to about 38 atomic %. The alloy films show microcrystalline and grain structures respectively, according to preparation conditions such as composition ratio of zinc and magnesium or gas pressures etc.. And X-ray diffraction analysis indicates not only the presence of Zn-Mg thin films with forced solid solution but also the one of $MgZn_2$ alloy films partly. In addition the influence of Mg/Zn composition ratio and morphology of the Zn-Mg alloy films on corrosion behavior is evaluated by electro-chemical anodic polarization tests in deaerated 3% NaCl solution. From this experimental results, all the prepared Zn-Mg alloy films showed obviously good corrosion resistance to compare with 99.99% Zn and 99.99% Mg Ingots for evaporation metal. It is thought that the Zn-Mg films with effective forced solid solution prepared by plasma enhanced PVD method, produces smaller and denser grain structure so that may improve the formation of homogeneous passive layer in corrosion environment.

• International Journal of Korean Welding Society
• /
• v.1 no.1
• /
• pp.63-70
• /
• 2001

The solidification cracking susceptibilities of Al-Mg alloy laser welds were assessed using self-restraint tapered specimen crack test. The dependence of cracking susceptibility of Al-Mg alloy laser welds on Mg contents was observed to be similar to that of arc welds in the same materials. The cracking susceptibility of Al-Mg alloy laser welds increased as Mg content increased up to 1.6-1.9 wt.% and then it decreased as Mg content increased further. The peak cracking susceptibility occurred at around 1.6 to 1.9 wt.% Mg for both autogenous and wire feed welds. It was also observed that the cracking susceptibility decreased as the grain size of Al-Mg alloy laser welds decreased, when Mg content was in the range higher than 1.9 wt.%.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.5
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• Journal of Korea Foundry Society
• /
• v.32 no.6
• /
• pp.269-275
• /
• 2012

Al-Mg-Si/Al hybrid alloy was prepared by Duo-casting and the mechanical behavior was evaluated based on their microstructure and mechanical properties. The hybrid aluminum alloy included the Al-Mg-Si alloy with fine eutectic structure, pure Al with the columnar and equiaxed crystals, and the macro-interface existing between Al-Mg-Si alloy and pure Al. The growth of columnar grains in pure Al occurred from the macro-interface. The tensile strength, 0.2% proof stress and bending strength of the hybrid aluminum alloy were almost similar to those of pure Al, and the elongation was much higher than the Al-Mg-Si alloy. The fracture of the hybrid alloy took place in pure Al side, indicating that the macro-interface was well bonded and the mechanical behavior strongly depends on the limited deformation in pure Al side.