• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.7
• /
• pp.504-509
• /
• 2018

The purpose of this study was to manufacture a high-performance titanium yellow pigment. Anatase type $TiO_2$ was the skeleton of the pigment and $Sb_2O_3$ is used as the color assistant for the coloring agent, $Cr_2O_3$. Mixed raw materials for the pigment were $TiO_2$(98%), $Sb_2O_3$(99.5%), and $Cr_2O_3$(99.5%). The raw materials were mixed by a dry process and crystallized by calcination at $1,000{\sim}1,200^{\circ}C$. The crystalline material was pulverized in a Jar Mill under $1{\mu}m$ by a wet process and dried for 12 hours at $100^{\circ}C$. The pigment was finally made by a fine grinding process. To determine the best temperature for calcination, 4 temperature sections ($1000^{\circ}C$, $1100^{\circ}C$, $1150^{\circ}C$, and $1200^{\circ}C$) were set up. The X-ray diffraction peak of the rutile crystalline structure was highest at $1,150^{\circ}C$. The yellow ceramic pigment, which has the rutile structure, was applied for coating materials. The synthesized pigments underwent a discoloration tests on the acid resistance, alkaline resistance, weather resistance and heat resistance. In addition, a detection test on harmful heavy metals ($Cr^{+6}$) was done. The resulting values (${\Delta}E$) of the weather resistance test (2000hr), acid resistance test, alkaline resistance test, and heat resistance test were 0.74, 0.16, 0.07 and 0.29. The resulting value for heavy metals testing was 34ppm.