• 한국전기전자재료학회논문지
• /
• 제28권3호
• /
• pp.160-164
• /
• 2015

In this study, $(1-x)Pb(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.09}(Zr_{0.5}Ti_{0.5})_{0.88}O_3+xCeMnO_3$ (x= 0~0.02) ceramics were prepared by Columbite precursor method. The phase structure, ferroelectric and piezoelectric properties were systematically investigated. It was found that PMW-PNN-PZT possessed superior electrical properties due to its composition close to the MPB (morphotropic phase boundary). Coercive electric field of 10.05 [kV/cm] and density of 7.88 [$g/cm^3$] were obtained when the substitution amount of $CeMnO_3$ is x=0.02. In contrast, specimens with x=0.01 showed the mechanical quality factor($Q_m$) of 1,091 and the electromechanical coupling factor($k_p$) of 0.613.

• 조명전기설비학회논문지
• /
• 제17권5호
• /
• pp.149-153
• /
• 2003

본 연구에서는 풀력측 전극비를 보다 증가시킬 목적으로 새로운 형상인 육각형 압전변압기를 제작하여 전극 패턴을 설계하고, 전기적 출력 특성을 검토하였다. 이 때 육각형 압전변압기의 한변의 길이가 각각 14[mm]와 17.5[mm]로 하였으며, 압전변압기에 적용된 세라믹의 성분계는 PZT-PMN-PSN이었으며, 기계적 품질계수가 1200, 전기기계결합계수는 55%, 압전정수 $d_{33}$은 320${\times}$$10^{-l2}$C/N, 손실계수는 0.3%이었다. 부하저항의 증가에 따라 승압비는 증가하였으며, 육각형 압전변압기의 한 변의 길이가 증가함에 따라서도 증가하는 경향을 보였다. 최대 효율은 10∼20[M$\Omega$]근처에서 약 93%가 얻어졌다.다.다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.193-195
• /
• 2005

[ $0.96[Bi_{0.5}(Na_{0.84}K_{0.16})_{0.5}TiO_3]+0.04SrTiO_3+0.3wt%Nb_2O_5+0.2wt%La_2O_3+xwt%ZnO$ ], were studied in order to develope the superior piezoelectric properties of Lead-free piezoelectric ceramics. With increasing amount of ZnO addition, density showed the maximum value of 5.79(g/$cm^3$) at 0wt% ZnO addition, and electromechanical coupling factor($k_p$) and dielectric constant decreased, and mechanical quality factor($Q_m$) increased and showed the maximum value of 280 at 0.4wt% ZnO addition.

• 한국전기전자재료학회논문지
• /
• 제16권12S호
• /
• pp.1195-1199
• /
• 2003

In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, dielectric and piezoelectric properties of PSN-PZT[0.91Pb(Sb$\sub$1/2/Nb$\sub$1/2/)$\sub$0.03/(Zr$\sub$0.495/Ti$\sub$0.505/)$\sub$0.97/O$_3$-0.04Pb(Ni$\sub$1/2/W$\sub$1/2/)O$_3$+0.05BiFeO$_3$+0.3wt％MnO$_2$+0.6wt％CuO〕 ceramics were investigated according to Zr/Ti ratio. As Zr/Ti ratio is increased, electromechanical coupling factor(k$\sub$p/) and dielectric constant increased and then decreased after the ratio of Zr/Ti=50/50. Also, mechanical qualify factor(Q$\sub$m/) decreased and then increased after the ratio of Zr/Ti=50/50.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 춘계학술발표대회
• /
• pp.33.2-33.2
• /
• 2009

Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.60-63
• /
• 1997

Dieletric ailed piezoelectric properties of Pb[$Zr_{0.45}$/ $Ti_{0.5-x}$/L $u_{x}$ (M $n_{1}$3//S $b_{2}$3)$_{0.05}$] $O_3$(0$\leq$x $\leq$0.03) were investigated. The partial substitution of $Ti^{4+}$ by a L $u^{3+}$ permitted improvement of the piezoelectric constant( $d_{33}$ ), electromechanical coupling factor ( $k_{p}$ ) and dielectric constant($\varepsilon$$_{33}$ /Sup T/). The dielectric loss(tan $\delta$ ) increased and mechanical quality factor(Qm) decreased with an increase of x were observed. A new piezoelectric material for actuator application was developed at x=0.02 with $d_{33}$ =370$\times$10$^{-2}$ /C/N, $k_{p}$ =58.5%, $\varepsilon$$_{33}$ $^{T}$ =1321, $Q_{m}$ =714 and tan $\delta$ =0.98%.%..%.%.

• 한국전기전자재료학회논문지
• /
• 제13권3호
• /
• pp.220-226
• /
• 2000

The piezoelectric material for piezoelectric transformer needs the high electromechanical coupling factor( $k_{p}$) the piezoelectric constant( $d_{33}$) and the mechanical quality factor( $Q_{m}$)in order to obtain high voltage step-up ratio and low temperature rising. In this study the piezoelectric transformers were fabricated using Pb［$Zr_{0.45}$/ $Ti_{0}$48//L $u_{0.02}$(M $n_{1}$3//S $b_{2}$3/)$_{0.05}$］ $O_3$(PMS-PZT) and Pb［Z $r_{0.25}$/ $Ti_{0.375}$(M $g_{1}$3//N $b_{2}$3/)$_{0.375}$］ $O_3$+0.5wt%Mn $O_2$(PMN-PZT) ceramics. The piezoelectric properties of PMS-PZT and PMN-PZT were measured. The voltage set-up ratios of the piezoelectric transformers using PMS-PZT and PMN-PZT were the value of 15, 20 respectively under 100$_{KΩ}$ in Rosen type transformer.r.ormer.r.r.r.r.r.r.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.292-293
• /
• 2007

In the study, in order to develop low temperature sintering ceramics for multilayer piezoelectric transformer, $(Pb,Ca,Sr)Ti(Mn,Sb)O_3$ ceramics were fabricated using $Na_2CO_3$, $Li_2CO_3$, $MnO_2$ and $Bi_2O_3$ as sintering aids and their dielectric and piezoelectric properties were investigated according to the amount of $Bi_2O_3$ addition. At the sintering temperature of $900^{\circ}C$, density, thickness vibration mode electromechanical coupling factor ($k_t$), thickness vibration mode mechanical quality factor ($Q_{mt}$) and dielecteic constant (${\varepsilon}_r$) showed the optimum value of $6.94[g/cm^3]$, 0.497, 3,162 and 209, respectively, for multilayer piezoelectric transformer application.

• 대한기계학회논문집
• /
• 제6권2호
• /
• pp.107-112
• /
• 1982

In order to analyze and investigate in the fatigue behavior of the notched specimens under the two level stressing, the U-notched specimens of structural carbon steel which is generally used is prepared. The obtained results are summarized as follows; (1) The fatigue limit of the U-notched specimens is lower than that of the unnotched. The fatifue notch factor (.betha.) of the U-notched specimens is 1.44 for mild steel and 1.52 for harden steel. The notch sensitivity (q) is 0.68 for mild steel and o.8 for harden steel. That is, these facts show that harden steel is more sensitive to the notch than mild steel. (2) The fatigue life time of the U-notched specimens under the overstressing is shorter than under the constant stressing, and the degree of fatigue life time decrease is different to each stress level; the degree for the high stress level is more than for the low stress level. (3) The fatigue life time of the U-notched specimes under the understressing is longer than under the constant stressing, and the degree of fatigue life time increase for the low stress level is more than for the high stress level.

• 센서학회지
• /
• 제16권2호
• /
• pp.120-125
• /
• 2007

The effect of $MnO_{2}$ as a sintering additive on the microstructures and the piezoelectric properties, especially mechanical quality factor, of 0.05 Pb$(Sb_{0.5}Nb_{0.5})O_{3}$-0.95 Pb$(Zr_{0.52}Ti_{0.48})O_{3}$ (PSN-PZT) piezoelectric ceramics was investigated. The samples were sintered at $1250^{\circ}C$ for 2 h. The crystal structure and surface morphology of the sample were examined using XRD and FE-SEM, respectively. A study on the influence of $MnO_{2}$ additives on the dielectric and piezoelectric properties showed that the $MnO_{2}$-added PSN-PZT system exhibited a high mechanical quality factor and well-situated piezoelectric properties. The optimized results of $d_{33}$ (319 pC/N), $k_{p}$ (55 %), and $Q_{m}$ (751.24) were obtained at 0.2 wt% $MnO_{2}$ added PSN-PZT piezoelectrics.