• Tribology and Lubricants
• /
• 제13권1호
• /
• pp.42-52
• /
• 1997

This paper deals with wear characteristics of ion-nitrided metal theoretically and experimentally in order to analysis of wear phenomena. Wear tests show that compound layer of ion-nitrided metal reduces wear rate when the applied wear load is mall. However, as th load becomes large, the existence of compound layer tends to increase wear rate. The residual stress at the surface of ion-nitrided metal is measured, and the internal stress distribution is calculated when the normal and tangential forces are applied to the surface of metal. Compressive residual stress is largeest at the compound layer, and decreases as the depth from the surface increases. Calculation shows that the maximum stress exists at a certain depth from the surface when normal and tangential force are applied, and that the larger the wear load is the deeper the location of maximum stress becomes. In the analysis, it is found that under small applied wear load the critical depth, where voids and cracks may be created and propagated, is located at the compound layer, as the adhesive wear, where hardness is an important factor, is created the existence of compound layer reduces the amount of wear. When the load becomes large the critical depth is located below the compound layer, and delamination, which may be explained by surface deformation, crack nucleation and propagation, is created, and the existence of compound layer increases wear rate.

• Tribology and Lubricants
• /
• 제9권1호
• /
• pp.38-44
• /
• 1993

The present study was undertaken to investigate the dry wear characteristics of die steel STD 11 for cold molding. The wear test was experimentally carried out under different conditions using a wear device, which was made in laboratory, and in which annular surfaces of wear testing specimens wear rubbed in dry sliding condition with varying the sliding speed, contact pressure, and sliding distance. The wear loss by variation of sliding speed was much in 0.3 m/sec and less in higher speed range above its sliding speed according to formation of the boundary lubrication film. The critical sliding speed with maximum value of the specific wear rate switched over to lower speed side according. as contact pressure increased. The critical sliding distance was increased with decrease in oxidation reaction velocity. The depth below subsurface showing maximum hardness (Hv) came out at the position, $60 \mu m$, of the maximum shear stress due to strain hardening.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2003년도 학술대회지
• /
• pp.313-323
• /
• 2003

The sliding wear behaviors of Zircaloy-4 nuclear fuel rod were investigated using two support springs with convex and concave shapes in room temperature air and water. The main focus is to compare the wear behavior of various test variables such as slip amplitude, environment, contact contours with different spring shape and a number of cycles. The results indicated that wear volume and maximum wear depth increased with slip amplitude in both air and water, but their trends tended to change according to the spring shapes and test environments. In air condition, the wear volume was controlled by wear debris behavior generated on worn surface. As a result, final wear volume and maximum wear depth decreased if a ratio of protruded wear volume to worn area $(D_p)$ would be saturated to specific value. This is because wear particle layer could accommodate large strain by accumulating and transforming wear particle layer. However, in water condition, metal-to metal contact was more dominant and wear volume was greatly affected by changed mechanical behavior between contact surfaces since wear debris should be generated after repeated plastic deformation and fracture. After wear test, worn surfaces were examined using optical microscope and SEM and details of wear mechanism were discussed using a ratio of wear volume to worn area $(D_e)$ at each test condition.

• 한국공작기계학회논문집
• /
• 제11권5호
• /
• pp.88-92
• /
• 2002

This research is about slurry wear of SM45C and SUS304, which using standard sand and KUM river sand. The results are as follows ; 1. Mass loss rates of both standard sand and KUM river sand were linearly increased as increasement of time and velocity. 2. The average diameter of sand from relatively, less wear rate and portion of larger particles. 3. Wear resistance was linear with time and velocity of liquid jet regardless of type of sand. Also, it was able to evaluate with the formula, $HV^2$/E calibrated with n, the velocity index. 4. The wear surface in liquid jet experiment was smooth. The maximum wear depth was observed at the location 2~4mm apart from the center in the condition of $90^{\circ}$ of collision angle 6mm of nozzle diameter, and 20mm of collision distance. The sectional shape in radial appeared as 'W'shape.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2001년도 춘계학술대회 논문집
• /
• pp.798-801
• /
• 2001

This research is about slurry wear of SM45C and SUS304, which using standard sand and KUM river sand. The results are as follows ; 1. Mass loss rates of both standard sand and KUM river sand were linearly increased as increasement of time and velocity. 2. The average diameter of sand from relatively, less wear rate and portion of larger particles. 3. Wear resistance was linear with time and velocity of liquid jet regardless of type of sand. Also it was able to evaluate with the formula, HV2/E calibrated with n, the velocity index. 4. The wear surface in liquid jet experiment was smooth. The maximum wear depth was observed at the location, 2~4mm apart from the center in the condition of 90$^{\circ}$of collision angle 6mm of nozzle diameter, and 20mm of collision distance. The sectional shape in radial appeared as 'W' shape.

• Tribology and Lubricants
• /
• 제23권3호
• /
• pp.130-133
• /
• 2007

Fuel cladding tubes in nuclear fuel assembly are held up by supporting grids because the tubes are long and slender. Fluid flows of high-pressure and high-temperature in the tubes cause oscillating motions between tubes and supports. This is called as FIV (flow induced vibration), which causes fretting wear in contact parts of tube and support. The fretting wear of tube and support can threaten the safety of nuclear power plant. Therefore, a research about the fretting wear characteristics of tube-support is required. The fretting wear tests were performed with supporting grids and cladding tubes, especially after corrosion treatment on tubes, in water. The tests were done using various applied loads with fixed amplitude. From the results of fretting tests, the wear amounts of tube materials can be predictable by obtaining the wear coefficient using the work rate model. Due to stick phenomena the wear depth was changed as increasing load and temperature. The maximum wear depth was decreased as increasing the water temperatures. At high temperatures there are the regions of some severe adhesion due to stick phenomena.

• Tribology and Lubricants
• /
• 제24권3호
• /
• pp.129-132
• /
• 2008

Fuel cladding tubes in nuclear fuel assembly are held up by supporting grids because the tubes are long and slender. Fluid flows of high-pressure and high-temperature in the tubes cause oscillating motions between tubes and supports. This is called as FIV (flow induced vibration), which causes fretting wear in contact parts of tube and support. The fretting wear of tube and support can threaten the safety of nuclear power plant. Therefore, a research about the fretting wear characteristics of tube-support is required. The fretting wear tests were performed with supporting grids and cladding tubes, especially after corrosion treatment on tubes, in water. The tests were done using various applied loads with fixed amplitude. From the results of fretting tests, the wear amounts of tube materials can be predictable by obtaining the wear coefficient using the work rate model. Due to stick phenomena the wear depth was changed as increasing load and temperature. The maximum wear depth was decreased as increasing the water temperatures. At high temperatures there are the regions of some severe adhesion due to stick phenomena.

• 열처리공학회지
• /
• 제22권6호
• /
• pp.361-367
• /
• 2009

The two-step gas nitriding was adopted to increase the depth of surface hardening in 3%Cr-Mo-V steel. The two-step gas nitriding consisted of Step I; $520^{\circ}C{\times}20\;hrs$ and Step II; $550^{\circ}{\times}70\;hrs$. The layer of two-step gas nitriding showed better uniformity and deeper nitriding layer than one-step gas-nitriding layer. The maximum surface hardness showed the value of 850 Hv. The maximum depth of nitrogen permeation showed $750\;{\mu}m$ (350 Hv). X-ray diffraction analysis showed that compound layer was mainly consisted of CrN and $\varepsilon-Fe_3N$ phases. These phases were presumed contributing to surface hardening and wear resistance. However, the corrosion resistance of gas-nitrided Cr-Mo-V steel were not improved in the solution of 1 N HCl and NaOH. Therefore, it is necessary that the continuous study for improvement of corrosion resistance hereafter.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1996년도 제23회 춘계학술대회
• /
• pp.122-127
• /
• 1996

In this paper, the effects of the film tinckness, pre-treatment and testing load on. the tribological characteristics have been studied. During the "Ring on-Disk" testing period silica-gel was used to remove the effect of humidity. As a result, increasing the film thickness revealed prolonged wear life, in the case or reasl the testing loads the dynamic friction coefficient was decreased gradually but in regarding the wear life, an intermideate contact pressure (4kgf/mm${2}$) revealed the maximum value. In regarding the surface protuberance friction an intermediate value of area fraction (60%) revealed maximum wear life. In this paper, the qualitative model in regarding the variation of the friction coefficient andworn depth was presented.presented.

• 한국생산제조학회지
• /
• 제4권2호
• /
• pp.18-24
• /
• 1995

In order to achieve the autimation and untended system of manufacturing process, it is necessary that the monitoring system check up the disorder of machine tool or the conditions of tool wear for the maximum use of cutting tool. In the metal cutting Process, AE signal is detected by AE sensor, then amplified and transmitted to an Locan-AT. The experiment was performed to SM25C and STS304 steels at uniform feedrate, cutting speed and depth of cut, The results of experimental data apparently showed emission intensity vary due to increasing of tool wear at the 165kHz, 200kHz in the SM25C and 140kHz, 165kHz, 200kHz, in the STS304 respectively Therefore, it is possible to predict the tool wear. This study is intended to suggest the way to the automation and untended system of machine tool through the system monitoring tool wear by using AE signal.