• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.5
• /
• pp.1-8
• /
• 2023

Marine and hydraulic structures are subject to durability damage not only due to the penetration of sea water but also due to the attachment of marine organisms. Therefore, in this study, we tried to develop an antifouling coating agent with self-cleaning function for marine concrete. It was confirmed that the antifouling coating agent mixed with AKD, cellulose nanofibers and BADGE had sufficient antifouling performance at a well hydrophobicity of around 140° in contact angle and an inclination angle of 15°. In the abrasion resistance test of the surface, only a maximum loss of 0.015 g occurred. In the durability test, as a result of the chloride ion permeation test, almost no chloride ion permeation occurred in the variable where the coating agent was applied, and carbonation and freeze-thaw damage also rarely occurred, so it was analyzed that it was effective in securing durability of concrete.

• Earthquakes and Structures
• /
• v.1 no.1
• /
• pp.129-146
• /
• 2010

This paper proposes an approximate procedure to estimate seismic displacement capacity - defined as yield displacement times the displacement ductility - of piles in marine oil terminals. It is shown that the displacement ductility of piles is relatively insensitive to most of the pile parameters within ranges typically applicable to most piles in marine oil terminals. Based on parametric studies, lower bound values of the displacement ductility of two types of piles commonly used in marine oil terminals - reinforced-concrete and hollow-steel - with either pin connection or full-moment-connection to the deck for two seismic design levels - Level 1 or Level 2 - and for two locations of the hinging in the pile - near the deck or below the ground - are proposed. The lower bound values of the displacement ductility are determined such that the material strain limits specified in the Marine Oil Terminal Engineering and Maintenance Standard (MOTEMS) are satisfied at each design level. The simplified procedure presented in this paper is intended to be used for preliminary design of piles or as a check on the results from the detailed nonlinear static pushover analysis procedure, with material strain control, specified in the MOTEMS.

• Computers and Concrete
• /
• v.6 no.1
• /
• pp.1-18
• /
• 2009

Chloride diffusivity of concrete is a crucial material parameter for service life determination and durability designing of marine concrete. Many research works on this issue have been conducted, varying from empirical solutions obtained experimentally to image analysis, based on multi-scale modeling. One of the simple approaches is to express the chloride diffusivity of concrete by a multi-factor function, however, the influences of various factors on the chloride diffusivity are ambiguous. Furthermore, the majority of these research works have not dealt with the carbonation process of concrete, although this process affects the chloride diffusivity of concrete significantly. The purpose of this study is to establish a simple approach to calculate the chloride diffusivity of (non)carbonated concrete. The chloride diffusivity of concrete should be defined, based on engineering and scientific knowledge of cement and concrete materials. In this paper, a lot of parameters affecting the chloride diffusivity, such as the diffusivity in pore solution, tortuosity, micro-structural properties of hardened cement paste, volumetric portion of aggregate, are taken into consideration in the calculation of the chloride diffusivity of noncarbonated concrete. For carbonated concrete, reduced porosity due to carbonation is calculated and used for calculating the chloride diffusivity. The results are compared with experimental data and previous research works.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.777-782
• /
• 2001

Occurrence of crack in the Half-loc of rubble mound breakwater under T.T.P (Tetrapod) can cause serious problems in structural safety. There, probing of such cracks in marine structures is an important process in evaluating the overall integrity of structures. Ultrasonic, SASW(Spectral-Analysis-of-Surface-Waves)and Impect-Echo methods were used for the inspection of pilot concrete and SFC (Steel Fiber Concrete) block in this study. The advantage and limitations of these methods for non-destructive inspection in concrete blocks are investigated. As a result, it has been verified that these methods proved to present effective solution for detecting the crack of the pilot concrete block.

• Computers and Concrete
• /
• v.6 no.5
• /
• pp.421-435
• /
• 2009

Chloride induced corrosion is a concern that governs the durability of concrete structures in marine environments, especially in tidal environments. During the service lives of concrete structures, internal cracks in the concrete cover may appear due to imposed loads, accelerating chloride penetration because of the simultaneous action of environmental and service structural loads. This paper investigated the effects of cyclic flexural loads on chloride diffusion characteristics of plain concretes, and proposed a model to predict the chloride penetration into plain concretes subjected to both tidal environments and different cyclic flexural load levels. Further, a new experiment was performed to verify the model. Results of the model using Finite Difference Method (FDM) showed that the durability of concretes in tidal environments was reduced as cyclic flexural load levels, SR, increased, and the modeling results fitted well with the experimental results.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.177-180
• /
• 2006

Reinforced concrete has been widely used as a semi-permanent construction materials. However, sea sand, deicing salt, and marine condition might induce the corrosion of embedded reinforcement due to the penetration of chlorides in concrete structures. This reinforcement corrosion causes serious problems on safety and serviceability of structures during lifetime. Also, reinforcement corrosion may cause the collapse of structures in worst case, so that the corrosion problem is more and more intensely growing. The purpose of this paper is to provide the fundamental data for the mechanical effect of corrosion through evaluation on bond characteristics of reinforced concrete using corroded bars.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.489-492
• /
• 2006

A chloride is an important deteriorating factor which governs the durability of the reinforced-concrete structures under marine environments. Also, the main penetration mechanism of chloride ion into concrete is a diffusion phenomenon and numerous methods have been proposed to determine the diffusion coefficient of chloride ion quickly. In this study, electrically accelerated experiments were carried out in order to evaluate diffusion coefficient of the chloride ion into concrete. The methods were diffusion cell test method in which the voltage of 15V(DC) was applied. The type of cement is blended cement in which the admixtures of blast-furnace slag and fly ash were used. In conclusion, the diffusion coefficient of chloride ion is much affected according to mineral admixtures and the diffusion coefficient of ternary blended cement showed very low values. it is presumably said that this result is due to highly densified pore structures by the aid of slag substitution and pozzolanic activity of fly ash.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.90-91
• /
• 2017

Concrete can be used semi-permanently unless the steel is corroded. However, the concrete exposed to the marine environment is exposed to sea breeze, so chloride ions penetrate into the concrete and the steel is corroded accordingly. In order to solve these problems, there is a method of increasing the covering depth of the concrete and an application of the epoxy paint to the steel. In this study, the hydrotalcite type corrosion inhibitor was mixed with the concrete and the compressive strength, chloride diffusion coefficient and the corrosion properties of the steel were examined.

• Journal of the Korea Concrete Institute
• /
• v.24 no.4
• /
• pp.435-444
• /
• 2012

High performance concrete mixes are selected and corresponding test specimens are made for the study of chloride diffusion coefficient at reference time. The concrete mixes were same designs as those used in construction of bridges located in a marine environment. Mix design variables included binder type, water-to-binder ratio, mineral admixtures to total binder weight substitution ratio, fine aggregate source, chemical water reducer admixture type for high strength and high flowability, and target slump or slump flow. The test results showed that the diffusion coefficients at reference time varied significantly according to the type of mineral admixtures and their substitution ratios. A model for diffusion coefficient at reference time considering the type of mineral admixture and the substitution ratio was developed. Diffusion coefficients from the developed model were compared with those from literature review, a previous model, and additional test results. All of the comparisons verified that the developed model can reasonably predict diffusion coefficients and the application of the model to the durability design against chloride penetration is appropriate.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.15 no.1
• /
• pp.25-32
• /
• 2009

The burial method has been generally used for the protection methods of submarine cable. Especially in Korea, various types of protection methods have been used according to fisheries and fishing implements. In these days, all the protection methods - burial, continuous concrete mattress, cast iron pipes, U-duct, concrete bags, rock berm, mortar bags and FCM(Flexible Concrete Mattress) are applied to the submarine cable, but these methods just focus not on the characteristics of ocean environment and the protection of environment but on the safety of submarine cable against the external damages. This research presents the protection methods of submarine cable according as the characteristics of ocean environment - external damages, depth of water, seabed condition and the protection of environment.