• Journal of Conservation Science
• /
• v.36 no.5
• /
• pp.421-429
• /
• 2020

This study examined the manufacturing process of a furnace wall excavated from the Songdu-ri Site in Jincheon, and the difference in material composition between the 11 layers of the wall using physicochemical analyses. Based on microstructure observations, these layers could be largely divided into three groups: an undercalcined first layer, calcined second to ninth layer with evidences of partial heat, and non-fired soil layers from the tenth to the eleventh layer. Particle size analyses revealed that the fired layer constituted a relatively higher content of coarse sand than the non-fired layer. This difference was further confirmed by the results of the curvature coefficient analysis. An analysis of the constituent minerals showed similar overall XRD diffraction patterns between the different layers, but variations in the intensity of the low-temperature and high-temperature minerals. This indicates that the degree of heat was different. The thermal analysis results demonstrated that the heating peak of mullite was only reached in the first and second layers of the wall, thus implying these as the layers to be finally used. Consequently, no significant difference could be observed between the materials of the various layers of the wall. Thus, it can be suggested that the furnace wall was constructed using clay, which had a composition similar to that of the soil present in the area. However, the shape and characteristics of the constituent particles between the layers displayed partial variations, and it is possible that some external materials might have been added.

• Journal of Conservation Science
• /
• v.29 no.2
• /
• pp.139-147
• /
• 2013

This study focused on iron making related information through analyzing slags and furnace wall collected from iron production site of Suryong-ri Wonmorongi, Chungju. Total Fe content of slags were from 36.98% to 44.47% and this range was general recovery rate of iron in ancient. Compounds of calcium included slags was supposed to add intentionally during smelting process as deoxidation agent in order that these helped to separate iron from impurities. Furnace wall didn't make of high alumina clay because of low $Al_2O_3$. Microstructure and main components of slags show that No. 1 to 3 slags with fayalite and wustite were products of iron ore smelting. However, No.4 slag is more likely to smelt by iron sand because of ulvospinel with $TiO_2$ in No. 4 slag. Therefore, iron ore were not only used but iron sand in smelting and furnace wall made of general clay with low $Al_2O_3$ content in this area.

• Korean Journal of Heritage: History & Science
• /
• v.50 no.1
• /
• pp.4-17
• /
• 2017

In this research, the chemical composition of the iron artifacts from the late 6th-century to early 7thcentury Baekje remains in Gwanbuk-ri, Buyeo, specifically of the nine iron artifacts including slags, furnace walls and ingot iron excavated in the District "Na", were examined by observing their chemical compounds and microstructures. As a result, GB1 and GB6 were determined to be proto-reduction lumps whereas GB2, GB3, GB4 and GB5 were determined to be tempered slags, respectively. Also, he furnace wall GB7 were containing mullite and cristobalite, which are high temperature index minerals, The extrusion temperature was found out to be about $1200{\sim}1300^{\circ}C$, and it is most likely that the smelting temperature in the furnace was in that temperature range. GB8 ingot iron was determined to be a forged ironware. This ingot iron was an intermediary product for making ironware and its nonmetallic inclusions displayed similar microstructure and contents compared to the forged iron. Because of the existence of proto-reduction lumps and forged iron, the iron making facility located in District "Na" most likely had a small-scale iron making facility that handled iron bloom smelting and refining processes.

• Journal of Conservation Science
• /
• v.33 no.4
• /
• pp.297-312
• /
• 2017

In the ancient iron-making process, a slag former was often added so that iron and other minerals in the ore could be smoothly separated. However, there are insufficient data for judging whether a slag former was added. Thus, in this study, we conducted a smelting experiment to understand the material characteristics of a steel structure that differed depending on the addition of a slag former. It was found that the steel structure produced in the first experiment had a total Fe content of 39.45-52.94 wt%, which decreased to 34.89-38.92 wt% in the second and third experiments. CaO compounds such as calcite, gehlenite, and hercynite appeared, in addition to iron oxides, after the addition of a slag former. As a result of an assessment of whether a slag former was added by comparing the ratio between the components, it was found that the ratio of $CaO/SiO_2$ was 0.42. From a comparative analysis of $Al_2O_3/SiO_2$ and $CaO/SiO_2$, it was judged that the ratio of $Al_2O_3$ and $SiO_2$ can be utilized as an index to judge similar systems of smelting process (ore, furnace wall, and fuel).