• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.1
• /
• pp.21-27
• /
• 2018

Synthesis of ferromagnetic composite materials for the $Cu-BaFe_{12}O_{19}$ system by mechanical alloying (MA) has been investigated at room temperature. A mixture of copper and barium ferrite with a weight ratio of $Cu:BaFe_{12}O_{19}=4:1$, 3 : 2, 2 : 3 and 1 : 4 was used. It is found that $Cu-BaFe_{12}O_{19}$ composite powders in which $BaFe_{12}O_{19}$ is dispersed in copper matrix are successfully produced by mechanical alloying of $BaFe_{12}O_{19}$ with Cu for 80 min. in all composition. The change in X-ray diffraction patterns and magnetic properties reflects the details for the formation of ferromagnetic metal matrix composite of pure Cu and $BaFe_{12}O_{19}$ during mechanical alloying. Magnetization of $Cu-BaFe_{12}O_{19}$ composite powders gradually increases with increasing the amounts of barium ferrite, whereas coercive force of MA powders gradually decreases due to the refinement of barium ferrite powders with ball milling. However, it can be seen that the coercivity of $Cu-BaFe_{12}O_{19}$ MA composite powders with a weight ratio of $Cu:BaFe_{12}O_{19}=4:1$ and 3 : 2 ball-milled for 80 min. is still high value of 1400 Oe and 1450 Oe, respectively suggesting that the refinement of barium ferrite powders during ball milling process tend to be suppressed due to the ductile copper.

• Advances in nano research
• /
• v.1 no.4
• /
• pp.183-192
• /
• 2013

One-dimensional multiferroic nanostructured composites have drawn increasing interest as they show tremendous potential for multifunctional devices and applications. Herein, we report the synthesis, structural and dielectric characterization of barium titanate ($BaTiO_3$)-bismuth ferrite ($BiFeO_3$) composite fibers that were obtained using a novel sol-gel based electrospinning technique. The microstructure of the fibers was investigated using scanning electron microscopy and transmission electron microscopy. The fibers had an average diameter of 120 nm and were composed of nanoparticles. X-ray diffraction (XRD) study of the composite fibers demonstrated that the fibers are composed of perovskite cubic $BaTiO_3$-$BiFeO_3$ crystallites. The magnetic hysteresis loops of the resultant fibers demonstrated that the fibers were ferromagnetic with magnetic coercivity of 1500 Oe and saturation magnetization of 1.55 emu/g at room temperature (300 K). Additionally, the dielectric response of the composite fibers was characterized as a function of frequency. Their dielectric permittivity was found to be 140 and their dielectric loss was low in the frequency range from 1000 Hz to $10^7$ Hz.

• Journal of Magnetics
• /
• v.19 no.1
• /
• pp.55-58
• /
• 2014

We have synthesized ferromagnetic ${\tau}$-phase $Mn_{54}Al_{46}/{\alpha}$-phase $Fe_{65}Co_{35}$ composite by annealing a mixture of paramagnetic ${\varepsilon}$-phase $Mn_{54}Al_{46}$ and ferromagnetic ${\alpha}$-phase $Fe_{65}Co_{35}$ particles at $650^{\circ}C$. The volume fraction ($f_h$) of hard ${\tau}$-phase $Mn_{54}Al_{46}$ of the composite was varied from 0 to 1. During the annealing, magnetic phase transformation occurred from paramagnetic ${\varepsilon}$-phase to ferromagnetic ${\tau}$-phase $Mn_{54}Al_{46}$. The magnetization and coercivity of the composite monotonically decreased and increased, respectively, as the $f_h$ increased. These results are in good agreement with our proposed composition dependent coercivity and modified magnetization equations.

• Transactions of Materials Processing
• /
• v.7 no.3
• /
• pp.215-224
• /
• 1998

A semi-solid forming has a lot of advantages compared to the die casting. squeeze casting and conventional forging. therefore, semi-solid forming process is now becoming industrial interest for the production of metal components and metal matrix composites. However the material behaviour in the semi-solid temperature range is not sufficiently known although it controls the whole process through forces and geometry evolutions because the behaviour of metal slurries is complex. The semi-solid materials(SSMs) fabricated under electric-magnetic stirring condition is necessary to be applicated in forming process. A reheating conditions were studied with the reheating time holding time and reheating temperatures. The microstructure of SSM(specimen size : d39${\times}$h85) at the condition of heating time 10min and heating temperature 590${\circ}C$ is the most globular and finest one. The microstructure of SSM(specimen size : d76${\times}$h60) reheated under the three step reheating conditions is most globular and finest.

• Journal of Magnetics
• /
• v.11 no.4
• /
• pp.164-166
• /
• 2006

We have investigated the dielectric and magnetic properties of ferroelectric-antiferromagnetic $BaTiO_{3}-LaMnO_{3}$ composite with changing relative mole percents. Due to high sintering temperature, i.e. $1150^{\circ}C$, the Ba ion in $BaTiO_{3}$ seems to diffuse into $LaMnO_{3}$; resulting in $BaTiO_{3}-(La,Ba)MnO_{3}$ ferroelectric-ferromagnetic composite. At room temperature, $0.9BaTiO_{3}-0.1LaMnO_{3}$ composite exhibits considerable magnetization (${\sim}0.7\;emu/g\;at\;2000\;Oe$) and low coercive field (${\sim}5\;Oe$). Also it exhibits high dielectric constant (${\sim}560$) and low loss (${\sim}0.08$) at 10 kHz. This result may imply that $BaTiO_{3}-LaMnO_{3}$ could be suitable for a low leakage multiferroic composite.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.1 no.1
• /
• pp.114-127
• /
• 1998

A user friendly computer code(EMCOMST; Electro-Magnetic response for COMposite STructures) was developed which provides with computations of the response characteristics such as reflectance and transmittance to the incident wave angles, frequencies, composite thicknesses, ply orientations, and types of backplate as the linearly polarized transverse electro-magnetic wave is emitted to the advanced composite structures. In this investigation were reviewed the electromagnetic characteristics of the continuous orthotropic fiber-reinforced organic matrix composites with or without ferrite fillers, which are actively applied to low-weight and high-strength aircraft structures. Also were calculated the response of the three layered compound structures which have appropriately stacked above-mentioned materials as transmitting layer, absorbing layer, reflection layer, respectively under the specific thickness constraints for mechanical strength design requirements. For the composite structures presented in this study, minimum reflectance value less than -5㏈ can be obtained in the frequency range of 4 to 12 ㎓. In addition, analysis of structures attached isotropic radar absorbing materials(RAM) is facilitated by putting the material properties in the material input card entries adequately.

• Journal of Powder Materials
• /
• v.8 no.3
• /
• pp.157-162
• /
• 2001

An optimum route to fabricate the ferrous alloy dispersed $Al_2O_3$ nanocomposites such as $Al_2O_3$/Fe-Ni and $Al_2O_3$/Fe-Co with sound microstructure and desired properties was investigated. The composites were fabricated by the sintering of powder mixtures of $Al_2O_3$ and nano-sized ferrous alloy, in which the alloy was prepared by solution-chemistry routes using metal nitrates powders and a subsequent hydorgen reduction process. Microstructural observation of reduced powder mixture revealed that the Fe-Ni or Fe-Co alloy particles of about 20 nm in size homogeneously surrounded $Al_2O_3$, forming nanocomposite powder. The sintered $Al_2O_3$/Fe-Ni composite showed the formation of Fe$Al_2O_4$ phase, while the reaction phases were not observed in $Al_2O_3$/Fe-Co composite. Hot-pressed $Al_2O_3$/Fe-Ni composite showed improved mechanical properties and magnetic response. The properties are discussed in terms of microstructural characteristics such as the distribution and size of alloy particles.

• Journal of Magnetics
• /
• v.15 no.4
• /
• pp.165-168
• /
• 2010

$Li_{0.1}Zn_{0.9}O$ and $MgFe_2O_4$ powders were synthesized using chemical methods and mixed in different proportions to prepare a mixture of $Li_{0.1}Zn_{0.9}O$ and $MgFe_2O_4$ that was thermally treated between 900 to $1100^{\circ}C$ for 1 hour. Structural characterization was done using X-ray powder diffraction measurements. Grain sizes and morphologies of $Li_{0.1}Zn_{0.9}O$, $MgFe_2O_4$, and $Li_{0.1}Zn_{0.9}O+MgFe_2O_4$ samples were observed using a scanning electron microscope. Variation of magnetic properties of the $Li_{0.1}Zn_{0.9}O+MgFe_2O_4$ samples due to the addition of $Li_{0.1}Zn_{0.9}O$ was studied in relation to the structural changes occurring due to the thermal treatment. In particular, changes in the cationic distribution between the tetrahedral and octahedral positions were studied with respect to the increase of the annealing temperature. Magnetization was found to be dependent on the cations distributed in the tetrahedral and octahedral sites of the $MgFe_2O_4$.

• Journal of Korean Society of Water Science and Technology
• /
• v.26 no.6
• /
• pp.117-124
• /
• 2018

For the effective removal of phosphorus in water, a novel type of composite was prepared by combining Poly Alumiun Chloride, widely used in sewage/wastewater treatment plants, and Humic Acid particles, which are known to have phosphorus removal ability, with CI. The surface of the ferromagnetic CI particles was oxidized and activated, and then PAC and HA were synthesized to finally produce CIPAC and CIHA. CIPAC and CIHA prepared by this study showed similar results to the phosphorus removal efficiencies of PAC and HA coagulants. The novel composite has a larger weight than the conventional coagulant, and the coagulated sludge precipitates rapidly. The sludge could be easily separated in a short time if the external magnetic field was given by the ferromagnetic force of CIPAC and CIHA prepared with CI as support. Therefore, it can be concluded that if phosphorus removal is carried out using CIPAC and CIHA prepared through this study with external magnetic field, the sedimentation rate will be much faster than that of conventional coagulant. Thus it is possible to obtain a high economic benefit in the sludge recovery part.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.18 no.11
• /
• pp.1217-1223
• /
• 2007

Advanced microwave absorbers for wide oblique incidence angles are required in many applications including wireless communication or vehicle identification in ITS(Intelligent Transport System) where 5.8 GHz DSRC(Dedicated Short Range Communication) system is applied. In this study, two-layered microwave absorber(with a laminate structure of dielectric/magnetic composites) has been designed for the achievement of low reflection coefficient over wide incidence angles at 5.8 GHz. Iron flake particles are used as the filler in the absorbing layer, and the magnetic composite sheet exhibits high magnetic loss due to ferromagnetic resonance in gigahertz frequencies. The surface layer of low dielectric constant containing small amount of carbon black is used as the impedance transformer. On the basis of transmission line theory, the reflection loss has been calculated for the two-layer structure with variation of incident angles for both TE(Transverse Electric) and TM(Transverse Magnetic) polarizations. At the optimum thickness of the composite layers, a low value of reflection loss(less than -10 dB) has been predicted for wide incidence angles up to $55^{\circ}$ which is in good agreement with the measured value determined by free-space measurement.