• Journal of the Korean Wood Science and Technology
• /
• v.12 no.2
• /
• pp.10-19
• /
• 1984

The $3{\times}3{\times}30$ ($cm^3$) sized lumbers of Populus alba-grandulosa L. were treated with four fire-retardant solutions of ammonium sulfate, monoammonium phosphate, diammonium phosphate and aluminium chloride for 1, 15, 30, and 60 minutes and 1, 3, and 7 days. Thereafter they were air-dried and burned at high temperature about $1,800^{\circ}C$ and for short time of five minutes. This study estimated the relationship between absorbed chemical amounts and rate of weight loss or residual bending strength of these burned lumbers. The results were as follows: 1) In absorption amount of fire-retardant chemicals, diammonium phosphate showed the largest, aluminium chloride the smallest, but monoammonium phosphate and ammonium sulfate showed similar level. 2) The absorption amount of chemicals was decreased with the increase of specific gravity in the same species except aluminium chloride. 3) The rate of weight loss was decreased as the absorption amount of chemicals increased, especially monoammonium phosphate was most effective. 4) The MOR value of the residual bending strength was increased as the absorption amount of chemicals increased and especially monoammonium phosphate showed the most efficient effect. 5) Aluminium chloride showed more striking increase of MOR value of residual bending strength with the increase of absorption amount than any other chemical, therefore its MOR value was similar to the maximum MOR value of the most effective monoammonium phosphate. 6) The correlation between weight loss and MOR value of the residual bending strength was negative and aluminium chloride showed the most striking negative relation, but the others showed similar trends. 7) The correlation between work to proportional limit and absorption amount of chemicals was positive and the degree of increase in work to proportional limit was most in aluminium chloride, and the next, in monoammonium phosphate and diammonium phosphate in turn. 8) The correlation between work to maximum load and absorption amount of chemicals showed positive and diammonium phosphate revealed the best result and aluminium chloride showed better results than other two chemicals.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.61-67
• /
• 1997

The bending performances of sloped finger-joints in Pinus densiflora S. et Z. were tested in order to improve the strength properties of finger-joint Sloped finger-cut pieces were jointed with four kinds of adhesives(resorcinol-phenol, oilic urethane, polyvinyl acetate, and polyvinyl-acryl acetate resin). The slope ratios of finger joints were 0, 0.5, 1.0, 2.0. The MOE, MOR and defletion to maximum load in bending of sloped finger-joints and solid wood specimen were measured. The results were: 1. The efficiencies of MOE to finger and sloped finger-joints were 82% or greater in every kind of adhesives except polyvinyl-acryl acetate resin adhesive and there were some effect of slope on the MOE in a sloped finger-joint for polyvinyl-acryl acetate and oilic urethane resin adhesives. 2. The effects of slope on the MOR to sloped finger-joints were showed in every kind of adhesive, because the efficiencies of MOR increased with increasing slope ratio in sloped finger-joints. The efficiencies of MOR to slope ratios of 0 and 2.0 ranged 43~65% and 76~82%, respectively. There was almost no effect of the kinds of adhesives on the MOR to the slope ratio of 2.0. 3. It was found impossible to estimate the bending strength of sloped finger-jointed Pinus densiflora S. et Z. by using MOE. The correlation coefficient(0.124) between MOE and MOR was very low and not significant at 5% level.

• Structural Engineering and Mechanics
• /
• v.81 no.4
• /
• pp.411-428
• /
• 2022

This paper presents the Campbell diagram analysis of the rotordynamic system using the full order model (FOM) and the reduced order model (ROM) techniques to determine the critical speeds, identify the stability and reduce the computational time. Due to the spin-speed-dependent matrices (e.g., centrifugal stiffening matrix), several model order reduction (MOR) techniques may be considered, such as the modal superposition (MS) method and the Krylov subspace-based MOR techniques (e.g., Ritz vector (RV), quasi-static Ritz vector (QSRV), multifrequency quasi-static Ritz vector (MQSRV), multifrequency/ multi-spin-speed quasi-static Ritz vector (MMQSRV) and the combined Ritz vector & modal superposition (RV+MS) methods). The proposed MMQSRV method in this study is extended from the MQSRV method by incorporating the rotational-speed-dependent stiffness matrices into the Krylov subspace during the MOR process. Thus, the objective of this note is to respond to the question of whether to use the MS method or the Krylov subspace-based MOR technique in establishing the Campbell diagram of the shaft-disc-blade assembly systems in three-dimensional (3D) finite element analysis (FEA). The Campbell diagrams produced by the FOM and various MOR methods are presented and discussed thoroughly by computing the norm of relative errors (ER). It is found that the RV and the MS methods are dominant at low and high rotating speeds, respectively. More precisely, as the spinning velocity becomes large, the calculated ER produced by the RV method is significantly increased; in contrast, the ER produced by the MS method is smaller and more consistent. From a computational point of view, the MORs have substantially reduced the time computing considerably compared to the FOM. Additionally, the verification of the 3D FE rotordynamic model is also provided and found to be in close agreement with the existing solutions.

• Korean Journal of Optics and Photonics
• /
• v.26 no.2
• /
• pp.73-82
• /
• 2015

This work demonstrates the indoor SI-traceable calibration of a transmissometer with a 75-m baseline for the measurement of visibility in MOR (Meteorological Optical Range). The calibration is performed using a set of neutral density (ND) filters (OD 0.1-2.5) and a set of high-transmission quartz glass plates (a bare quartz glass plate and antireflective-coated quartz glass plates), the collection consisting of 20 artifacts in total. The luminous transmittance values of the reference artifacts had been calibrated traceable to the KRISS spectral transmittance scale, which ranges from 0.2 % to 99.5 %. The transmissometer to be calibrated typically consists of a loosely collimated light source based on a white LED (CCT ~5000 K) and a luminous intensity detector with a CIE 1924 V(${\lambda}$) spectral response. As a result of calibration, we obtained the MOR error and its uncertainty for the transmissometer in 20 m - 40 km of MOR. Based on the results, we investigated the applicability of the calibration method and the conformity of the transmissometer to the ICAO's (International Civil Aviation Organization) accuracy requirement for meteorological visibility measurement. We expect that this work will establish the standard procedure for the SI-traceable calibration of a transmissometer.

• Membrane Journal
• /
• v.26 no.5
• /
• pp.381-390
• /
• 2016

In this study, the natural mordenite (MOR) zeolite seeds were used for the synthesis of high purity mordenite crystals. The effect of seed concentration and crystallization time on the phase purity and surface morphology of MOR crystals has also been reported. The diffraction, elemental and scanning analysis of MOR zeolite particles obtained from 100 g hydrothermal solution batch containing 3 g natural seed, hydrothermally treated at $140^{\circ}C$ for 72 h reveal the high phase-purity of as-synthesized sample having crystals of uniform size ($1-2{\mu}m$). Moreover, high seed concentration leads to the production of mesoporous MOR particles composed of needle shape primary nano crystallites. The gases adsorption performances of as-synthesized MOR particle were carried out at $25^{\circ}C$ and 0-1 bar. Surprisingly, MOR particles show good adsorption potential for $CO_2$ (97.19 mg/g) compared to other gases. Thus it confirms that high purity MOR particles can be synthesized without using any organic template which gives an advantage of separation performance at lower price.

• The Korean Journal of Pain
• /
• v.35 no.4
• /
• pp.423-432
• /
• 2022

Background: The decreased expression of mu-opioid receptors (MOR) in the amygdala may be a key molecular in chronic post-surgical pain (CPSP). It is known that miR-339-5p expression in the amygdala of a stressed rat model was increased. Analyzed by RNAhybrid, miR-339-5p could target opioid receptor mu 1 (oprm1) which codes MOR directly. So, the authors hypothesized that miR-339-5p could regulate the expression of MOR via targeting oprm1 and cause the effects to CPSP. Methods: To simulate perioperative short-term stress, a perioperative stress prolongs incision-induced pain hypersensitivity without changing basal pain perception rat model was built. A pmiR-RB-REPORT^TM dual luciferase assay was taken to verify whether miR-339-5p could act on oprm1 as a target. The serum glucocorticoid level of rats was test. Differential expressions of MOR, GFAP, and pERK1/2 in each group of the rats' amygdala were tested, and the expressions of miR-339-5p in each group of rats' amygdalas were also measured. Results: Perioperative stress prolonged the recovery time of incision pain. The expression of MOR was down-regulated in the amygdala of rats in stress + incision (S + IN) group significantly compared with other groups (P < 0.050). miR-339-5p was up-regulated in the amygdala of rats in group S + IN significantly compared with other groups (P < 0.050). miR-339-5p acts on oprm1 3'UTR and take MOR mRNA as a target. Conclusions: Perioperative stress could increase the expression of miR-339-5p, and miR-339-5p could cause the expression of MOR to decrease via targeting oprm1. This regulatory pathway maybe an important molecular mechanism of CPSP.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.5
• /
• pp.65-71
• /
• 2003

In this paper, bending capacities of glulams with different configurations of cross-section were evaluated. These configurations included horizontal(BH), vertical(BVN), vertical with vertical plywood (BVV) and vertical combination of lamination with horizontal plywood(BVH). Full-scale bending tests were performed to investigate the effect of different section configurations on bending strength(MOR) and stiffness(MOE) of glulam. Compared with type BH, MOR of glulam with type BVN configuration was improved about 23%, which was considered to be caused by defect dispersion effect, while MOE of glulams with these two types of configurations were similar. Because MOE of plywood is generally smaller than that of solid wood laminar, MOE of type BVH glulam decreased about 15%, but in the case of type BVV glulam, MOR was improved without any reduction of MOE. The reason of this result could be undersood in the view of shear-reinforcement effect, which was verified from analysis of fracture mode. From the results of this study, it was concluded that bending capacity of glulam could be improved by proper section design, such as laminar arrangement and shear reinforcement.

• Journal of the Korea Furniture Society
• /
• v.10 no.1
• /
• pp.65-71
• /
• 1999

The bending performance of sloped finger-jointed Rhus verniciflua were tested in order to improve the strength properties of finger-joint. Sloped finger-cut pieces were jointed with three kinds of adhesives (polyvinyl acetate, polyvinyl-acryl acetate and oilic resin). The slope ratios of finger joints were 0, 1.0, 1.5, and 2.0. The MOE, MOR and deflection to maximum load in bending of sloped finger-joints and solid wood specimen were measured. The results were : 1) The efficiencies of MOE to finger and sloped finger-joints to the solid wood were almost same in the three kinds of adhesives(polyvinyl acetate, polyvinyl-acryl acetate and oilic urethane resin) and there were some effect of slope on the MOE in a sloped finger-joint for three kinds of resin adhesives. 2) There was the effect of slope on the MOR in sloped finger-joints in every kind of adhesive. The efficiencies of MOR in slope ratios of 0 and 2.0 ranged 65-79%, respectively. There was also a slight effect of the kinds of adhesives on the MOR. However, the efficiencies of deflection to the urethane resin adhesive were much less than those of polyvinyl acetate, polyvinyl-acryl acetate resin adhesives except the slope ratio of 0. 3) It might be impossible to estimate the bending stregth of sloped finger-jointed Rhus verniciflua by using MOE. The correlation coefficient(0.192) between MOE was very low and not significant at 5% level.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.1
• /
• pp.22-31
• /
• 2020

In this study, rice straw and bagasse are used as raw materials to produce binderless particleboard (BPB). This study aims to evaluate the mechanical and physical properties of BPB. We identify the raw material that would be better for the production of BPB from the viewpoint of their basic properties. The BPBs are made from rice straw, bagasse, and combinations of both in ratios of 50:50 and 40:60, respectively. The modulus of elasticity (MOE), modulus of rupture (MOR), internal bonding (IB) strength, water absorption, and thickness swelling properties of the different BPBs are determined and compared. Results showed that all the properties are significantly influenced by the type of particles or particle combinations in the BPB. BPBs made from bagasse alone have the highest MOR, MOE, and IB mean values, whereas BPBs made from rice straw alone exhibit the lowest MOR, MOE, and IB values. Meanwhile, BPBs made from a combination of rice straw and bagasse at 40:60 ratio by weight have the second highest values for properties such as MOR, MOE, and IB, followed by BPBs made from a combination of rice straw and bagasse at 50:50 ratio by weight.

• Journal of the Korean Wood Science and Technology
• /
• v.50 no.4
• /
• pp.237-245
• /
• 2022

This study examined the structural performance of experimental parallel strand lumber (PSL) from a Larch veneer strand. The prototype of PSL from a Larch veneer strand was manufactured in the experimental laboratory and tested. The bending and dowel bearing strength were determined from the modulus of elasticity (MOE), modulus of rupture (MOR), and dowel bearing strength based on a 5% offset yield load. The test results indicated that the average MOR of PSL was higher than that of 2 × 4 dimension lumber, and the average MOE of PSL was lower than that of 2 × 4 dimension lumber. A linear relationship was observed between the MOR and MOE. The allowable bending stress of PSL was derived as specified in ASTM D2915 and compared with other research. The dowel bearing strength of PSL in parallel to the grain was approximately double that perpendicular to the grain of PSL. A comparison of several theoretical calculations based on each national code for the dowel bearing strength was conducted, and some theoretical equations produced results closer to the experimental results when it was parallel to the grain, but the difference was higher in the case perpendicular to the grain. The test results showed that PSL made with Japanese larch veneer strands appeared to be suitable for a raw material of structural composite lumber (SCL) appeared to be used as a raw material for SCL.