• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.1
• /
• pp.12-19
• /
• 2006

Metalorganic chemical vapor deposition (MOCYD) techniques have been applied to fabricate semiconducting ZnO thin films and nanostructures, which are promising for novel optoelectronic device applications using their unique multifunctional properties. The growth and characterization of ZnO thin films on Si and $SiO_2$ substrates by MOCYD as fundamental study to realize ZnO nanostructures was carried out. The precise control of initial nucleation processes was found to be a key issue for realizing high quality epitaxial layers on the substrates. In addition, fabrication and characterization of ZnO nanodots with low-dimensional characteristics have been investigated to establish nanostructure blocks for ZnO-based nanoscale device application. Systematic realization of self- and artificially-controlled ZnO nanodots on $SiO_2/Si$ substrates was proposed and successfully demonstrated utilizing MOCYD in addition with a focused ion beam technique.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.3
• /
• pp.139-145
• /
• 2005

[ $SnO_x$ ] films on the flexible substrate of PET film were prepared at ambient temperature under a $(CH_3)_4Sn(TMT: tetra-methyl tin)-H_2-O_2$ atmosphere in order to obtain transparent conductive polymer by using ECR-MOCVD(Electro Cyclotron Resonance Metal Organic Chemical Yfpor Deposition) system. The prepared $SnO_x$ thin films show generally over $90\%$ of optical transmittance at wavelength range of 380-780nm and about $1\times10^{-2\~3}ohm{\cdot}cm$ of electrical resistivity. In the present study, effects of $O_2/TMT\;and\;H_2/TMT$ mole ratio on the properties of $SnO_x$ films are investigated and the other process parameters such as microwave power, magnetic current power, substrate distance and working pressure are fixed. Based on our experimental results, the $SnO_x$ film composition ratio of Sn and O directly influences on the electrical and optical properties of the films prepared. The $SnO_x$ film with low electric resistivity and high transmittance could be obtained by controlling the process parameters such as $O_2/TMT\;and\;H_2/TMT$ mole ratio, which play an important role to change the composition ratio between Sn and O. An increase of $O_2/TMT$ mole ratio brought on the increases 0 content in the $SnO_x$ film. On the other hand, an increase of $H_2/TMT$ mole ratio lead to decreases the oxygen content in the film. The optimized composition ratio of oxygen : tin Is determined as 2.4: 1 at $O_2/TMT$ of 80 and $H_2/TMT$ of 40 mole ratio, respectively.