• Tribology and Lubricants
• /
• 제15권4호
• /
• pp.335-342
• /
• 1999

Corrosion of the disk has been an ongoing concern for the manufacturers of hard disk drives. With the advent of magnetoresistive (MR) head, very low levels of corrosion and contamination become more critical since the raised defects and corrosion products on the disk surface-anything that heats the MR sensor due to the contact-can distort the output signal of the head. This phenomenon is called as thermal asperity. In this paper, the effect of corrosion as a form of Co migration on the occurrence of thermal asperity in MR drives was investigated. The corrosion test at high temperature (60$^{\circ}C$) and high relative humidity (80%) was emphasized in this study and the testing results at ambient condition were compared. The corrosion on the disks was characterized as the amount of Co ion migration using an ion chromatography (IC) and a time-of-flight secondary ion mass spectroscopy (TOF-SIMS). It is proved that corrosion on the disk surface after storage testing is closely correlated to the amount of Co ions migration from the magnetic layer to disk surfaces and higher Co migration causes more thermal asperities in the drive. In order to reduce Co migration, several methods such as burnishing process and structure of the carbon overcoat were investigated. It is found that the hydrogenated carbon overcoat shows the least Co migration among different types of overcoat layer. However, the most effective way to reduce Co migration is the application of Cr layer between the overcoat and the magnetic alloy layer.

• 한국표면공학회지
• /
• 제47권5호
• /
• pp.221-226
• /
• 2014

A low temperature plasma nitrocarburizng was implemented on the duplex stainless steel to achieve the enhancement of surface hardness without degradation of its corrosion resistance. Attempts were made to investigate the influence of Pulse frequency and Duty factor of pulsed power in a high Pulse frequency regime on the surface characteristics of the hardened layer. The hardened layer (S-phase) was formed on all of the treated surfaces. Surface hardness reached up to 1300 $HV_{0.1}$ which is about 4.6 times higher than that of the untreated material (280 $HV_{0.1}$). The thickness of the hardened layer tends to increase lightly with the higher Pulse frequency and the higher Duty factor. The corrosion resistance of nitrocarburized duplex stainless steel was almost similar to that of the untreated material. Both the Pulse frequency and the Duty factor do not have a significant influence on the corrosion property of plasma treated duplex stainless steel.

• 한국분무공학회지
• /
• 제13권4호
• /
• pp.173-179
• /
• 2008

The current machinery and tools of secondary channel of the nuclear power plants were produced in the carbon-steel and low-alloy steel. What produced with the carbon-steel occurs wall thinning effect from flow accelerated corrosion by the fluid flow at high temperature, high pressure. Several nuclear power plants in Korea have experienced wall thinning damage in the area around the impingement baffle-installed. Wall thinning by flow accelerated corrosion occurs piping system, the heat exchanger, steam condenser and feedwater heaters etc,. Feedwater heaters of many nuclear power plants have recently experienced sever wall thinning damage, which will increase as operating time progress. This study describes the comparisons between the numerical results using the FLUENT code and experimental data of down scale model.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2002년도 추계학술발표회요약집
• /
• pp.225-225
• /
• 2002

• Corrosion Science and Technology
• /
• 제12권5호
• /
• pp.220-226
• /
• 2013

The uncertainty in statistical noise resistance measurement was evaluated for a type 316 stainless steel in NaCl solutions at room temperature. Sensitivity coefficients were determined for measurands or variables such as NaCl concentration, pH, solution temperature, surface roughness, inert gas flow rate and bias potential amplitude. The coefficients were larger for the variables such as NaCl concentration, pH, inert gas flow rate and solution temperature, and they were the major factors increasing the combined standard uncertainty of noise resistance. However, the contribution to the uncertainty in noise resistance measurement from the above variables was remarkably low compared to that from repeated measurements of noise resistance, and thus, it is difficult to lower the uncertainty in noise resistance measurement significantly by lowering the uncertainties related with NaCl concentration, pH, inert gas flow rate and solution temperature. In addition, the uncertainty in noise resistance measurement was high amounting to 17.3 % of the mean, indicating that the reliability in measurement of noise resistance is low.

• Corrosion Science and Technology
• /
• 제13권1호
• /
• pp.28-35
• /
• 2014

Recently, the fuel oil of diesel engines of marine ships has been increasingly changed to heavy oil of low quality as the oil price is getting higher and higher. Therefore, the spiral gear attached at the motor of the oil purifier which plays an important role to purify the heavy oil is also easy to expose at severe environmental condition due to the purification of the heavy oil in higher temperature. Thus, the material of the spiral gear requires a better mechanical strength, wear and corrosion resistance. In this study, the heat treatment(tempering) with various holding time at temperature of $500^{\circ}C$ was carried out to the alloy of Cu-7Al-2.5Si as centrifugal casting, and the properties of both hardness and corrosion resistance with and without heat treatment were investigated with observation of the microstructure and with electrochemical methods, such as measurement of corrosion potential, cathodic and anodic polarization curves, cyclic voltammogram, and a.c. impedance. in natural seawater solution. The ${\alpha}$, ${\beta}^{\prime}$ and ${\gamma}_2$ phases were observed in the material in spite of no heat treatment due to quenching effect of a spin mold. However, their phases, that is, ${\beta}^{\prime}$ and ${\gamma}_2$ phases decreased gradually with increasing the holding time at a constant temperature of $500^{\circ}C$. The hardness more or less decreased with heat treatment, however its corrosion resistance was improved with the heat treatment. Furthermore, the longer holding time, the better corrosion resistance. In addition, when the holding time was 48hrs, its corrosion current density showed the lowest value. The pattern of corroded surface was nearly similar to that of the pitting corrosion, and this morphology was greatly observed in the case of no heat treatment. It is considered that ${\gamma}_2$ phase at the grain boundary was corroded preferentially as an anode. However, the pattern of general corrosion exhibited increasingly due to decreasing the ${\gamma}_2$ phase with heat treatment. Consequently, it is suggested that the corrosion resistance of Cu-7Al-2.5Si alloy can be improved with the heat treatment as a holding time for 48 hrs at $500^{\circ}C$.

• Corrosion Science and Technology
• /
• 제2권4호
• /
• pp.178-182
• /
• 2003

Slow Strain Rate Tests (SSRT) were carried out to investigate the effect of environmental factors on the Stress Corrosion Cracking (SCC) susceptibility of 3.5NiCrMoV steels used in discs for Low-Pressure (LP) steam turbines in electric power generating plants. The influences of dissolved oxygen on the stress corrosion cracking of turbine steel were studied, For this purpose, specimens were strained at variously oxygenated conditions at $150^{\circ}C$ in pure water. When the specimen was strained with $1{\times}10^{-7}s^{-1}$ at $150^{\circ}C$ in pure water, increasing concentration of dissolved oxygen decreased the elongation and the UTS. The corrosion potential and the corrosion rare increased as the amounts of dissolved oxygen increased. The increase of the SCC susceptibility of the turbine steel in a highly dissolved oxygen environment is due to the non protectiveness of the oxide layer on the turbine steel surface and the increase of the corrosion current. These results clearly indicate that oxygen concentration increases Stress Corrosion Cracking susceptibility in turbine steel at $150^{\circ}C$.

• Corrosion Science and Technology
• /
• 제2권6호
• /
• pp.253-259
• /
• 2003

Zirconium based alloys have been extensively used as a cladding material for fuel rods in nuclear reactors, due to their low thermal neutron absorption cross-section, excellent corrosion resistance and good mechanical properties at high temperatures. However, a cladding material for fuel rods in nuclear reactors was contact water during long time at high-temperature, so it is necessary to improve the wear and corrosion resistance of the fuel cladding, At ambient environment, there are few data or paper on the characteristic of corrosion in chloride solution and acidic solution. The specimens used in this work are pure Zr and Zircaloy-4. Zircaloy-4 is a specific zirconium-based alloy containing, on a weight percent basis, 1.4% Sn, 0.2% Fe, 0.1% Cr. Pitting corrosion resistance of two alloys by ASTM G48 is higher than that of electrochemical method. Passive film formed on Zircaloy-4 is mainly composed of $ZrO_2$, metallic Sn, and iron species regardless of formation environments. Also, passive film formed on Zr alloys shows n-type semiconductic property on the base of Mott-Schottky plot.

• 한국재료학회지
• /
• 제12권1호
• /
• pp.3-9
• /
• 2002

The corrosion behavior of alloys in a molten salt was investigated along with the oxidation characteristics in the air. The basic composition of alloys in the study was Fe-25Ni-7Cr with Si and RE(rare-earth metal) as additives. The corrosion rate of the alloys was low in a molten salt of LiCl while the rate was high in the mixed molten salt of LiCl and $Li_2O$. When Si is added to the base alloy of Fe-25Ni-7Cr, corrosion resistance was improved as the Si content is increased up to 3%, however, it was observed that the corrosion resistance was getting worse as the Si content is increased. The base alloy with 2.43% of Si and 0.9% of RE(KSA-65), showed higher corrosion rate compared to that of KSA-63 alloy with an equivalent amount of only Si. The corrosion resistance of KSA-65 was similar to that of the base alloy(KSA-60). The oxidation resistance of KSA-65 alloy was greatly increased even at $850^{\circ}C$ for a long term exposure.

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.502-514
• /
• 1998

The purpose of this study is to observe the corrosion characteristcs of four dental amalgams(CAULK FINE CUT, CAULK SPHERICAL, DISPERSALLOY, TYTIN) and to determine a function of chloride concentration through the anodic polarization curve obtained by using a potentiostat. After each amalgam alloy and Hg being triturated, the triturated mass was inserted into the cylinderical metal mold, and condensed by hydrolic pressure. Each specimen was removed from the metal mold. 24 hours after condensation, specimens were polished with the emery paper and stored at room temperature for 6 months. The anodic polarization curves were employed to compare the corrosion behaviours of the amalgam m KCl and KCl-NaCl solution, which had chlonde concentration of 0.4 g/l, 0.8 g/l, 1.2 gil, and 1.6 gil at $37^{\circ}C$ with 3-electrode potentiostat. After the immersion of specimen in electrolyte for 1 hour, the potential scan was begun. The potential scan range was - 1500mV ~+800mV(vs. S.C.E.) in the working electrode and the scan rate was 50mV/sec. The results were as follows, 1. The corrosion potential. the potential of anodic current peak, and transpassive potential in the solution of high chloride concentration shifted to more cathodic direction than those in the solution of low concentration, and the current density in the solution of high chloride concentration was higher than that in the solution of low concentration. 2. The corrosion potential, the potential of anodic current peak, and transpassive potential for CAULK FINE CUT amalgam were the most cathodic among the others, and the current density were the highest among the others. 3. In the solution of low chloride concentration, the corrosion potential, the potential of anodic current peak, and transpassive potential for DISPERSALLOY were the most anodic among the others, however in the solution of high chloride concentration, those for TYTIN were the most anodic among the others. 4. The anodic polarization curve for CAULK SPHERICAL was similar to that for high copper amalgams.