• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.6
• /
• pp.166-175
• /
• 2002

Low cycle fatigue tests are performed on the HSLA steel that be developed for a submarine material. The relation between strain energy density and numbers of cycles to failure is examined in order to predict the low cycle fatigue life of HSLA steel. The cyclic properties are determined by a least square fit techniques. The life predicted by the strain energy method is found to coincide with experimental data and results obtained from the Coffin-Manson method. Also the cyclic behavior of HSLA steel is characterized by cyclic softening with increasing number of cycle at room temperature. Especially, low cycle fatigue characteristics and microstructural changes of HSLA steel are investigated according to changing tempering temperatures. In the case of HSLA steel, the $\varepsilon$-Cu is farmed in $550^{\circ}C$ of tempering temperature and enhances the low cycle fatigue properties.

• Journal of Industrial Technology
• /
• v.20 no.B
• /
• pp.3-8
• /
• 2000

Low cycle fatigue life of spheroidal graphite cast iron is determined by the morphological parameters of internal graphite. The aim of this study is to clarify the effect of the number of nodular grain of spheroidal graphite cast iron on low cycle fatigue life. Two specimens that have identical average nodular grain size by changing nodular grain volume fraction and different number of nodular grain count was tested. In this paper, the parameter governing fatigue life through fatigue test, the number of nodular grain seriously affect fatigue life and nodular grain size is no longer governing parameter of it.

• Steel and Composite Structures
• /
• v.17 no.2
• /
• pp.185-198
• /
• 2014

Carbon-manganese steel A42 (French standards) is used in steam generator pipes of nuclear center and subject to low cycle fatigue (LCF) loads. In order to obtain the material LCF behavior, the tests are implemented in a hydraulic fatigue machine. The LCF plastic deformation and cyclic stress in macroscope have been influenced by the accumulated low cycle fatigue damage. The constitutive kinematic and isotropic hardening modeling is modified with coupling fatigue damage to describe the fatigue behavior. The improved model seems to be good agreement with the test results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.2
• /
• pp.199-208
• /
• 1997

A local strain approach was applied to an external single and double grooved C-shaped specimen in order to evaluate and predict the fatigue crack initiation life by using low cycle fatigue properties. The low cycle fatigue properties were determined from the strain-controlled fatigue tests using smooth cylindrical axial specimens. Fatigue crack initiation life was evaluated by a life prediction software, FALIPS, based on the local strain approach. The fatigue life was significantly influenced by the mean stress, and SWT parameter represented the fatigue life effectively. The predicted fatigue crack initiation life was then compared to the experimental fatigue life evaluated from the C-shaped fatigue test specimens. A good correlation was found between the experimental and predicted fatigue lives within factors of 2 and 4 for the single and double grooved C-shaped specimens respectively. Also, experimental fatigue life of the double grooved specimen was 10-12 times longer than that of the single grooved specimen.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.5 no.1
• /
• pp.129-135
• /
• 1997

Previous studies has shown that the curve of low-cycle fatigue life was not expressed with the single line subjected to Manson-Coffin's law type and bent to short life in low ${\Delta}{\varepsilon}_p$ region. The main cause of this phenomenon has been considered that the localization of plastic strain in the crack initiation process fosters the crack initiation. In this study, the low-cycle fatigue life was investigated for each specimens omitted crack initiation process and it was found that fatigue life curve in log(${\Delta}{\varepsilon}_p$)-log($N_f$)was bent in low ${\Delta}{\varepsilon}_p$ region as ever. Therefore, the main cause of appearance of knee point in fatigue life curve is not found in the crack initiation process but in the crack propagation process. In the crack propagation process, the localization of the plastic strain in the vicinity of crack tip and the influence of test environment on the crack propagation rate were observed and these inclinations were more remarkable in low ${\Delta}{\varepsilon}_p$ region. Hence, it was concluded that these two phenomena in the crack propagation process were proved to the main cause which accelerates the crack propagation in low ${\Delta}{\varepsilon}_p$ region and bent the fatigue life curve in result.

• International Journal of Naval Architecture and Ocean Engineering
• /
• v.11 no.2
• /
• pp.671-678
• /
• 2019

In this paper, the low cycle fatigue failure and ratcheting behavior, as well as their interaction of AH32 steel were experimentally investigated under uniaxial cyclic loading. The effects of mean stress, stress amplitude and stress ratio on the low cycle fatigue life and ratcheting strain were discussed. It was found that the ratcheting strain increased while the fatigue life decreased with the increase of mean stress and stress amplitude, and the increasing stress ratio would result in smaller ratcheting and larger fatigue life. Two kinds of failure modes, i.e. low cycle fatigue failure due to crack propagates and ratcheting failure due to large plastic strain will take place respectively. Based on the experimental results, considered the effect of ratcheting on fatigue life, a model with the maximum stress and ratcheting strain rate was proposed. Comparison with the experimental result showed that the new model provided a good prediction for AH32 steel.

• Korean Journal of Materials Research
• /
• v.24 no.9
• /
• pp.481-487
• /
• 2014

The effect of alpha phase on the fatigue properties of Fe-29%Ni-17%Co low thermal expansion alloy was investigated. Two kinds of alloys (Base alloy and Alpha alloy) were prepared by controlling the minimal alloy composition. Microstructure observation, tensile, high-cycle fatigue, and low-cycle fatigue results were measured in this study. The Base alloy microstructure showed typical austenite ${\gamma}$ phase. Alpha alloy represented the dispersed phase in the austenite ${\gamma}$ matrix. As a result of tensile testing, Alpha alloy was found to have higher strengths (Y.S. & T.S.) and lower elongation compared to those of the Base alloy. High cycle fatigue results showed that Alpha alloy had a higher fatigue limit (360MPa) than that (330MPa) of the Base alloy. The Alpha alloy exhibited the superior high cycle fatigue property in all of the fatigue stress conditions. SEM fractography results showed that the alpha phase could act to effectively retard both fatigue crack initiation and crack propagation. In the case of low-cycle fatigue, the Base alloy had longer fatigue life in the high plastic strain amplitude region and the Alpha alloy showed better fatigue property only in the low plastic strain amplitude region. The fatigue deformation behavior of the Fe-29%Ni-17%Co alloy was also discussed as related with its microstructure.

• Journal of Power System Engineering
• /
• v.21 no.1
• /
• pp.43-49
• /
• 2017

This work aims to investigate on the low cycle fatigue life assessment, which is adopted on the strain-life relationship, or better known as the Coffin-Manson relationship, and also the strain energy density-based model. The low cycle fatigue test results of Alloy 617 weldments under $900^{\circ}C$ have been statistically estimated through the Coffin-Manson relationship according to the provided strain profile. In addition, the strain energy density-based model is proposed to represent the energy dissipated per cycle as fatigue damage parameter. Based on the results, Alloy 617 weldments followed the Coffin-Manson relationship and strain energy density-based model well, and they were compatible with the experimental data. The predicted lives based on these two proposed models were examined with the experimental data to select a proper life prediction parameter.

• Journal of Welding and Joining
• /
• v.8 no.4
• /
• pp.46-57
• /
• 1990

TMCP steel manufactured by controlled rolling followed by accelerated cooling process is known to have extra-ordinary mechanical properties such as tensile strength and toughness. However, there is much uncertainty about the fatigue fracture characteristics, especially, in the welded state of this steel. In case of this steel, the softening zone by welding is generated in heat affected zone in contrast with the case of conventional normalized high strength steel. This softening zone is considered to play significant roles in low cycle fatigue fracture of the welded part of this steel. In this paper, the low cycle fatigue behaviors of TMCP steel were inspected in as-received and welded state using the smooth specimen. The fatigue life-time was seperately investigated on the basis of failure of the specimen and crack initiation which is detected by differential strain method. Moreover, the low cycle fatigue characteristics of TMCP steel were quantitatively compared with those of the conventional normalized steel of same strength level.

• Journal of Welding and Joining
• /
• v.14 no.1
• /
• pp.38-46
• /
• 1996

High temperature low cycle fatigue crack growth behavior is investigated over a range of two temperatures and various frequencies in SUS 304 stainless steel. It is found that low frequency and temperature can enhance time-dependent crack growth. With high temperature, low frequency and long crack length, ${\Delta}J_c/{\Delta}J_ f$, the ratio of creep J integral range to fatigue J integral range is increased and time-dependent crack growth is accelerated. Interaction between ${\Delta}J_f$ and ${\Delta}J_c$ is occured at high frequency and low temparature and ${\Delta}J_c$, creep J integral range is fracture mechanical parameter on transition from cycle-dependent to time dependent crack growth in creep temperature region.