• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.7
• /
• pp.623-626
• /
• 2014

The LBB (Leak Before Break) concept is based on evaluating the fracture toughness. NUREG 1061, Vol.3 announced that the specimen for evaluating fracture resistance needs to have same thickness or thicker than pipe. Therefore, it is difficult to collect specimen from pipe which has same thickness as a pipe. So, ASTM standard suggested the use of standard specimen with 1 inch thickness. However, it has been known that an application of LBB by test results of standard specimen is conservative compare with that by real pipe. In this study, to supplement such conservatism, the evaluation of fracture resistance characteristics was performed with curved CT specimen, which has same thickness and curvature as a pipe. In addition, fracture resistance characteristics of curved CT specimen were compared with those of CT specimen. For this, shape factor F, hpl and g were obtained from FEM analysis using the limit load method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.10 s.181
• /
• pp.2405-2412
• /
• 2000

A cast stainless steel may experience an embrittlement when it is exposed to approximately 30$0^{\circ}C$ for long period. In the present investigation, The three classes of the thermally aged CF8M specimie n are prepared using an artificially accelerated aging method. Namely, after the specimen are held for 300, 1800 and 3600hrs. at 43$0^{\circ}C$ respectively, the specimens are quenched in water to room temperature. Load versus load line displacement curves and J-R curves are obtained using the unloading compliance method. $J_{IC}$ values are obtained following ASTM E 813-87 and ASTM E 813-81 methods. In addition to these methods, JIC values are obtained using SZW(stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are $J_Q$=485.7 kJ/m$^2$ for virgin material, $J_{IC}$ of the degraded materials associated with 300, 1800 and 3600hrs are obtained 369.25 kJ/m$^2$, 311.02 kJ/m$^2$, 276.7 kJ/m$^2$, respectively. The results of SZW method are similar to those of the unloading compliance method. Through the elastic-plastic fracture toughness test, it is found that the value of $J_{IC}$ is decreased with increasing of the aging time. The results obtained through the investigation can provide reference data for a leak before break(LBB) of reactor coolant system of nuclear power plants.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.138-146
• /
• 2013

The present paper provides the elastic stress intensity factors(SIFs) of thick-walled cylinder with non-idealized circumferential through-wall cracks. For estimating these elastic SIFs, the systematic three-dimensional(3D) elastic finite element(FE) analyses were performed. In order to consider practical shape of thick-walled cylinder and non-idealized circumferential through-wall crack, the values of thickness of cylinder, reference crack length and crack length ratio were systematically varied. As for loading conditions, axial tension, global bending and internal pressure were considered. In particular, in order to calculate the SIFs of thick-walled cylinder with non-idealized circumferential through-wall crack from those of thick-walled cylinder with idealized circumferential through-wall crack, the correction factor representing the effect of non-idealized crack on the SIFs were proposed in this paper. The present results can be applied to accurately evaluate the rupture probabilities of nuclear piping considering actual crack growth behaviors.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.7
• /
• pp.729-736
• /
• 2015

In this study, the effects of specimen size and side-groove on the results of the J-R test for leak-before-break (LBB) evaluation were investigated. A series of J-R tests were conducted at both RT and $316^{\circ}C$, using three different sizes of compact tension (CT) specimens machined from SA508 Gr.1a piping material: 12.7 mm-thick 1T-CT, 25.4 mm-thick 1T-CT, and 25.4 mm-thick 2T-CT with and without side-groove. The results showed that side-grooving reduced the J-R curve for all specimens and the effect of side-grooving was more significant at $316^{\circ}C$ than at RT. As the thickness of the specimens decreased and the width of the specimens increased, the J-R curve slightly decreased at RT but it increased at $316^{\circ}C$. However, the variation in the J-R curve of SA508 Gr.1a with the thickness and width of CT specimen was insignificant.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.305-311
• /
• 1998

최근들어 고려된 LBB(Leak Before Break) 적용요건중 동적파괴시힘 절차에는 울진 3&4호기 이후 파단전누설개념이 적용되는 배관이 탄소강으로 제작될 경우. 이 배관이 Dynamic Strain Aging (DSA)에 의해 파괴저항치가 감소되지 않는다는 것이 정량적으로 입증되지 않는 한, 동 배관의 파괴 물성치 결정시 DSA의 영향이 고려되어야 하며, DSA 영향을 평가하기 위해서는 동적과괴시험이 수행되어야 함을 요건화 하고 있다. 본 연구에서는 DSA 효과에 의한 파괴저항(J-R) 특성의 저하가차세대원전 원자로냉각재배관 파단전누설개넘(LBB) 적용시 설계 안전여유도에 영향을 미치지 않는 정도임을 평가하는데 있다. 따라서 ASME Section III에서 탄소강으로 분류하고 있는 강종별 파괴인성 변화를 고찰하고, 차세대원전 주냉각재배관 재료인 SA508 Class la의 최대 파괴인성 감소치를 예측하여, 울진 3&4호기에서 측정된 엘보우용 SA516-Gr.70 강의 DSA 영향 평가 결과와 비교 분석하여 차세대원전 주냉각재배관의 DSA영향을 평가하였다. 도출된 결론으로는 DSA 영향을 고려한 SA508 Class la의 J 및 dJ/dA 값은 극히 보수적으로 추정할 때 50% 이상 감소하는 것으로 예측된다. 이러한 DSA 영향을 고려하였을 경우 배관재 모재의 파괴인성치는 Weld-SAW의 J/T 값 수준으로 감소하였다. 그러나 현 LRB 해석이 가장 낮은 J/T값을 갖는 Weld-SAW Auto의 균열길이 2a인 J/T선도에 의거하여 수행되고 있다는 점을 고려한다면 비록 DSA가 배관재에 영향을 주는 가장 보수적인 값(J 및 dJ/dA값을 50% 이상)을 사용한다고 하더라도 차세대원전 LBB 적용에 문제가 되지 않음을 알 수 있다. 즉 차세대원자로 주냉각재배관에 LBB를 적용하는데는 DSA 영향은 상대적으로 중요하지 않다는 결론을 얻었다. 표면에 수소화물이 농축되어 있는 hydride layer가 형성됨을 관찰하였으며 ～5,000ppm 이상의 경우에는 수소화물의 방향성이 random하였으며 특히, ZIRLO$^{TM}$ 시편의 경우에서는 원주방향으로 길게 이어진 수소화물과 기계적 성질에 치명적인 반경방향의 수소화물이 평행하게 배열된 것을 관찰하였다.하였을 때는 Li$_2$O의 첨가에 의해 치밀화가 주로 일어났고, 반면에 $N_2$-7vol.%H$_2$ 분위기에서 소결하면 Li$_2$O의 첨가에 의해 작은 기공은 소멸되고 큰 기공이 생성되었다.지나치게 모국어의 영향만 강조하고 다른 요인들에 대해서는 다분히 추상적인 언급으로 끝났지만 이 분석을 통 해서 배경어, 목표어, 특히 중간규칙의 역할이 괄목할 만한 것임을 가시적으로 관찰할 수 있 다. 이와 같은 오류분석 방법은 학습자의 모국어 및 관련 외국어의 음운규칙만 알면 어느 학습대상 외국어에라도 적용할 수 있는 보편성을 지니는 것으로 사료된다.없다. 그렇다면 겹의문사를 [-wh]의리를 지 닌 의문사의 병렬로 분석할 수 없다. 예를 들어 누구누구를 [주구-이-ν가] [누구누구-이- ν가]로부터 생성되었다고 볼 수 없다. 그러므로 [-wh] 겹의문사는 복수 의미를 지닐 수 없 다. 그러면 단수 의미는 어떻게 생성되는가\ulcorner 본 논문에서는 표면적 형태에도 불구하고 [-wh]의미의 겹의문사는 병렬적 관계의 합성어가 아니라 내부구조를 지니지 않은 단순한 단어(minimal $X^{0}$ elements)로 가정한다. 즉, [+wh] 의미의 겹의문사는 동일한 구성요 소를 지닌 병렬적 합성어([$[W1]_{XO-}$ $[W1]_{XO}$ ]$_{XO}$)로