• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.640-646
• /
• 1998

PbO-TiO2-B2O3-BaO계 유리에서 PbTiO3의 핵생성 및 결정화를 위한 최적조건의 확입을 위해 핵생성 속도 곡선을 도출하고자 열시차 분석법(DTA)을 응용하였다. PbTiO3의 함량비가 60mol%인 4성분계 유리 샘플은 용융액으로부터 자연 냉각시켜 제조되었으며, 핵생성을 위해 유리 샘플은 40$0^{\circ}C$와 50$0^{\circ}C$ 사이에서 열처리하였다. 이때 46$0^{\circ}C$에서 핵생성 속도가 최대값을 나타내었다. DTA의 결정화 피크 온도는 핵생성을 위한 열처리시간이 증가함에 따라 감소하였으며, DTA의 승온속도에 비례하여 증가하였다. 이러한 결과는 계에 생성된 핵의 밀도가 핵생성 처리온도와 시간의 증가에 따라 증가함을 보여주고 있다.

• 한국세라믹학회지
• /
• 제35권7호
• /
• pp.665-670
• /
• 1998

Ferroelectric anomaly in PbO-{{{{ { {B }_{2 }O }_{3 } }}-{{{{ {TiO }_{3 } }}-BaO glasses which is observed in DAT measurements was in-vestigated together with the effect of BaO content on the shift of Cuire temperature. The temperature where the ferroelectric anomaly apperars on cooling in DTA decreased in proportion with increasing BaO content,. For as-crystallized samples the ferroelectric anomaly was not observed on heating but on cooling whilist for powder samples leached chemically from the crystallized samples both endothermic and ex-otehrmic peaks were observed. This fact suggests that the appearance of the ferroelectric anomaly in DAT largely depends on glassy phases surrounding individual {{{{ {PbTiO }_{3 } }} crystals rather than effects of grain size and crystallinity.

• The Korean Journal of Ceramics
• /
• 제1권4호
• /
• pp.191-196
• /
• 1995

Using sol-gel processing method, thin films of lathanum modified lead titanate(PLT) on Corning 7059 glass were prepared. A differential thermal analysis (DTA/TG) curve of gel powder and infrared spectra (FT-IR) of the films were measured to estimate residual organices in them. The heat-treated films were characterized by X-ray diffraction(XRD). Microstructures of the films were observed by a scanning electron microscope (SEM). Optical properties of the films were determined by a UV-VIS spectrophotometer. The waveguiding properties and optical attenuation were measured with the end coupling method and the cut back method. Effects of the drying conditions on the transmittance and the propagation loss of the films were investigated. Experimemtal results showed that the content of residual organics in the film decreased as the drying temperature of the film increased. As the La content of the film increased, the grain size decreased and the transmittance increased. The transmittances of the films increased with the increasing of the drying temperature. The propagation losses in the film decreased as the drying temperature increased.