• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.640-646
• /
• 1998

Nucleation and crystallzation of a quaternary glass system for lead titanate glass-ceramics were in-vestigated using DTA(differential thermal analysis ) with variation of nucleation temperature and crystal growth time. Glass samples containing 60mol% of PbO-{{{{ { TiO}_{2 } }} were prepared from melts by the conventional normal cooling method in a cylindrical brass mould. The glass sample was nucleated between 40$0^{\circ}C$ and 50$0^{\circ}C$ for a given time and showed the maximum nucleation rate at 46$0^{\circ}C$ The DTA crystallization peak temperature decreased with increasing nucleating time and decreasing heating rate during DTA runs which indicated an increase of the number of nuclei produced in the system.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.665-670
• /
• 1998

Ferroelectric anomaly in PbO-{{{{ { {B }_{2 }O }_{3 } }}-{{{{ {TiO }_{3 } }}-BaO glasses which is observed in DAT measurements was in-vestigated together with the effect of BaO content on the shift of Cuire temperature. The temperature where the ferroelectric anomaly apperars on cooling in DTA decreased in proportion with increasing BaO content,. For as-crystallized samples the ferroelectric anomaly was not observed on heating but on cooling whilist for powder samples leached chemically from the crystallized samples both endothermic and ex-otehrmic peaks were observed. This fact suggests that the appearance of the ferroelectric anomaly in DAT largely depends on glassy phases surrounding individual {{{{ {PbTiO }_{3 } }} crystals rather than effects of grain size and crystallinity.

• The Korean Journal of Ceramics
• /
• v.1 no.4
• /
• pp.191-196
• /
• 1995

Using sol-gel processing method, thin films of lathanum modified lead titanate(PLT) on Corning 7059 glass were prepared. A differential thermal analysis (DTA/TG) curve of gel powder and infrared spectra (FT-IR) of the films were measured to estimate residual organices in them. The heat-treated films were characterized by X-ray diffraction(XRD). Microstructures of the films were observed by a scanning electron microscope (SEM). Optical properties of the films were determined by a UV-VIS spectrophotometer. The waveguiding properties and optical attenuation were measured with the end coupling method and the cut back method. Effects of the drying conditions on the transmittance and the propagation loss of the films were investigated. Experimemtal results showed that the content of residual organics in the film decreased as the drying temperature of the film increased. As the La content of the film increased, the grain size decreased and the transmittance increased. The transmittances of the films increased with the increasing of the drying temperature. The propagation losses in the film decreased as the drying temperature increased.