• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.24-27
• /
• 2000

Ferroelectric P $b_{0.99}$〔(Z $r_{0.6}$S $n_{0.4}$)$_{0.9}$ $Ti_{0.1}$〕$_{0.98}$N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on (L $a_{0.5}$S $r_{0.5}$)Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole％. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ were crystallized to a perovskite phase after rapid thermal annealing(RTA) The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures and ferroelectric properties. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 ％.0 ％.％.0 ％.0 ％.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.162-162
• /
• 2003

최근에 산화물 인공격자의 우수한 특성으로 인하여 활발한 연구가 진행되고 있다. 본 연구에서는 펄스레이저 증착방법을 이용하여 산소분압 100mTorr, $650^{\circ}C$에서 LSCO/MgO 기판위에 La-50mol% 첨가된 SrTiO$_3$ (SLTO)와 SrTiO$_3$ 를 적층시켜 산화물 인공격자를 만들어 결정구조에 대하여 연구하였다. SrTiO$_3$ (STO)는 상온에서 3.904$\AA$인 cubic perovskite 구조를 가지고 있다. 일반적으로 La$^{3+}$ (1.14$\AA$)은 Sr$^{2+}$(1.12$\AA$)과 이온반경이 거의 유사하기 때문에 ABO 페로브스카이트 구조의 A자리에 치환될 것으로 기대되며 또한 Sr$^{2+}$ 자리에 La$^{3+}$ 가 치환되므로써 발생하는 charge compensation은 Sr 자리에 Vacancy 생성으로 판단된다. 인공격자의 성장확인을 위하여 SLTO와 STO를 10층씩 증착하여 XRD분석을 통하여 평가하여 보았다. 확인된 결과를 바탕으로 산화물 인공격자의 적층 주기를 SLTO layer를 한층으로 고정시키고 STO를 한 층에서 다섯 층까지 다양하게 변화시켰다. 본 연구의 목적은 산화물 인공격자에서 결정결함을 제어하여 소자에 응용할 수 있는 전기적 물성을 평가하기 위함이다. X-ray diffraction 결과 SLTO/STO 인공격자는 (001) 방향으로 우선배향하였으며 적층주기에 따라 격자상수의 변화를 보였다. AES의 depth profile 분석을 통하여 La의 분포를 확인하였으며, HRTEM 분석을 통하여 미세구조분석을 실시하였다.

• Korean Journal of Materials Research
• /
• v.7 no.12
• /
• pp.1058-1062
• /
• 1997

강유전체 전계효과를 관찰하기 위해 LaCoO$_{3}$/Pb(Zr, Ti)O$_{3}$(La, Sr)CoO$_{3}$ 다층구조를 LcOo$_{3}$가 기판 위에 pulsed laser deposition(PLD)법으로 에피택셜하게 성장시켰다. 이러한 다층구조에서는 전도성 채널층으로 Si대신 반도성 LaCoO$_{3}$가 사용 되었다. LaCoO$_{3}$(LCO)의 비저항은 산소 분위기에 의하여 변화되었는데 특히 증착시 산소 분위기에 의존함을 보였다. LCO의 비저항은 0.1-100Ωcm범위에서 변화되었다. LCO층에 유도되는 강유전체 전계효과는 Pb(Zr, Ti)O$_{3}$(PZT)의 분극 상태에 따른 LCO의 저항 변화를 측정함으로써 관찰되었는데 1020$\AA$ 두께를 가진 LCO층에서는 4%의 저항 변화를 얻었으며 680$\AA$의 LCO에서는 9%의 증가된 저항 변화를 얻었다. DC 바이어스(-5V)를 가한 후에는 저항 변화가 45%까지 증가하였다. 이러한 결과는 적당한 비저항을 갖는 LCO를 사용한 LCO/PZT/LSCO다층구조가 강유전체 전계효과 트랜지스터로 사용될 수 있다는 가능성을 제시하고 있다.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.30 no.12 s.255
• /
• pp.1211-1217
• /
• 2006

This study is focused on oxidation prevention of STS430, which is generally used as solid oxide fuel cell(SOFC) interconnect at intermediate operating temperatures with oxidation-proof coatings. Inconel, $La_{0.6}Sr_{0.4}CoO_3(LSCo)$ and $La_{0.6}Sr_{0.4}CoO_3(LSCr)$ were chosen as coating materials. Using a radio frequency magnetron sputtering method, each target material was deposited as thin film on STS430 and was analyzed to find out favorable conditions. In this study, LSCr-coated STS430 can reduce electrical resistance to 1/3 level, compared with uncoated STS430. Also, long-term durability test at $700^{\circ}C$ for 1000 hours tells that LSCr thin layer performs an important role to prohibit serious degradations. Superior oxidation-resistant characteristic of LSCr-coated STS430 is attributed to the inhibition of spinel structure formation such as $MnCr_2O_4$.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.4
• /
• pp.283-287
• /
• 2007

KIER has been developing the anode-supported flat tubular solid oxide fuel cell unit bundle for the intermediate temperature($700{\sim}800^{\circ}C$) operation. Anode-supported flat tubular cells have Ni/YSZ cermet anode support, 8 moi.% $Y_2O_3$ stabilized $ZrO_2(YSZ)$ thin electrolyte, and cathode multi-layer composed of Sr-doped $LaSrMnO_3(LSM)$, LSM-YSZ composite, and $LaSrCoFeO_3(LSCF)$. The prepared anode-supported flat tubular cell was joined with ferritic stainless steel cap by induction brazing process. Current collection for the cathode was achieved by winding Ag wire and $La_{0.6}Sr_{0.4}CoO_3(LSCo)$ paste, while current collection for the anode was achieved by using Ni wire and felt. For making stack, the prepared anode-supported flat tubular cells with effective electrode area of $90\;cm^2$ connected in series with 12 unit bundles, in which unit bundle consists of two cells connected in parallel. The performance of unit bundle in 3% humidified $H_2$ and air at $800^{\circ}C$ shows maximum power density of $0.39\;W/cm^2$ (@ 0.7V). Through these experiments, we obtained basic technology of the anode-supported flat tubular cell and established the proprietary concept of the anode-supported flat tubular cell unit bundle.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.54-54
• /
• 2003

최근 새로운 개념에 물성 구현을 위한 강유전체 산화물 인공격자의 연구가 활발히 진행되고 있다. 본 연구에서는 펄스레이져 증착법을 이용하여 산소분압 100 mTorr와 증착온도 50$0^{\circ}C$에서 LSCO/MgO 기판 위에 PbTiO$_3$(PTO) 와 PbZrO$_3$(PZO)을 주기적으로 적층하여 강유전체 산화물 인공격자를 형성하였다. 인공격자의 주기는 1~100 unitcell 까지 변화시켰다. 적층주기와 두께 변화에 따른 PZO/PTO 인공격자의 성장과 전기적 특성에 대하여 관찰하였다. X선 회절분석을 통하여 PZO/PTO 인공격자는 주기가 25 unit cell 이하의 적층구조에서 초격자의 형성으로 인한 위성피크가 관찰되었으며, 그 이하의 낮은 주기(1~10 unitcell)에서는 위성피크와 강한 (100)과 (200) 성장거동을 보였다. 높은 주기에서는 c축 성장된 PTO와 a축 성장된 PZO 각각의 성장거동을 보였다. 적층 주기가 감소함에 따라 a축 성장된 PTO와 c축 성장된 PZO가 초격자를 형성하였다. 적층주기가 감소함에 따라 유전상수와 잔류분극값이 향상되었다. 유전상수는 1 unitcell 주기에서 800정도의 값을 보였고, 잔류분극값은 2 unitcell 주기에서 2Pr=38.7 $\mu$C/$\textrm{cm}^2$ 정도의 가장 큰 값을 나타냈다. 적층주기가 2 unitcell에서 두께가 감소함에 따라 유전상수가 감소하였고, 20 nm 까지 분극반전에 의한 capacitance-voltage 특성곡선의 이력 현상(강유전성)을 관찰하였다. 이러한 산화물 인공초격자에서의 유전상수와 잔류분극값의 향상에 대하여 논의 할 것이며, 임계크기효과 관점에서 나노사이즈(50 nm~5 nm)에서 인공초격자의 전기적 분극의 안정성에 대하여 또한 논의 할 것이다.소수성 가스의 경우70% 이상 향상되었음을 알 수 있었으며, 본 연구를 통해 광분해를 이용한 스크러버가 기존설비의 장.단점을 충분히 보완 가능한 환경 설비임을 확인할 수 있었다. duty로 구동하였으며, duty비 증가에 따라 pulse의 on-time을 고정하고 frequency를 변화시켰다. dc까지 duty비가 증가됨에 따라 방출전류의 양이 선형적으로 증가하였다. 전압을 일정하게 고정시키고 각 duty비에서 시간에 따라 방출전류를 측정한 결과 duty비가 높을수록 방출전류가 시간에 따라 급격히 감소하였다. 각 duty비에서 방출전류의 양이 1/2로 감소하는 시점을 에미터의 수명으로 볼 때 duty비 대 에미터 수명관계를 구해 높은 duty비에서 전계방출을 시킴으로써 실제의 구동조건인 낮은 duty비에서의 수명을 단시간에 예측할 수 있었다. 단속적으로 일어난 것으로 생각된다.리 폐 관류는 정맥주입 방법에 비해 고농도의 cisplatin 투여로 인한 다른 장기에서의 농도 증가 없이 폐 조직에 약 50배 정도의 고농도 cisplatin을 투여할 수 있었으며, 또한 분리 폐 관류 시 cisplatin에 의한 직접적 폐 독성은 발견되지 않았다이 낮았으나 통계학적 의의는 없었다[10.0%(4/40) : 8.2%(20/244), p>0.05]. 결론: 비디오흉강경술에서 재발을 낮추기 위해 수술시 폐야 전체를 관찰하여 존재하는 폐기포를 놓치지 않는 것이 중요하며, 폐기포를 확인하지 못한 경우와 이차성 자연기흉에 대해서는 흉막유착술에 더 세심한 주의가 필요하다는 것을 확인하였다. 비디오흉강경수술은 통증이 적고, 입원기간이 짧고, 사회로의 복귀가 빠르며, 고위험군에 적용할 수 있고, 무엇보다도 미용상의 이점이 크다는 면에서 자연기흉에 대해 유용한 치료방법임에는 틀림이 없으나 개흉술에 비해 재발율이 높고 비용이 비싸다는 문제가 제기되고 있는 만큼 더 세심한 주의와 장기 추적관찰이 필요하리라 사료된