• Journal of the Korean institute of surface engineering
• /
• v.57 no.1
• /
• pp.22-30
• /
• 2024

This study reports a direct growth of carbon nanotubes (CNTs) on the surface of LiCoO₂ (LCO) powders to apply as highly efficient cathode materials in lithium-ion batteries (LIB). The CNT synthesis was performed using a thermal chemical vapor deposition apparatus with temperatures from 575 to 625 ℃. Ferritin molecules as growth catalyst of CNTs were mixed in deionized (DI) water with various concentrations from 0.05 to 1.0 mg/mL. Then, the LCO powders was dissolved in the ferritin solution at a ratio of 1g/mL. To obtain catalytic iron nanoparticles on the LCO surface, the LCO-ferritin suspension was dropped in silicon dioxide substrates and calcined under air at 550℃. Subsequently, the direct growth of CNTs on LCO powders was performed using a mixture of acetylene (10 sccm) and hydrogen (100 sccm) for 10 min. The growth behavior was characterized by scanning and transmission electron microscopy, Raman scattering spectroscopy, X-ray diffraction, and thermogravimetric analysis. The optimized condition yielding high structural quality and amount of CNTs was 600 ℃ and 0.5 mg/mL. The obtained materials will be developed as cathode materials in LIB.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.2
• /
• pp.111-118
• /
• 2014

The electrochemical properties using the cells assembled with the synthesized $LiCoO_2$(LCO) were evaluated in this study. The LCO was synthesized from high-purity cobalt sulfate($CoSO_4$) which is recovered from the cathode scrap in the wastes lithium ion secondary battery(LIB). The leaching process for dissolving the metallic elements from the LCO scrap was controlled by the quantities of the sulfuric acid and hydrogen peroxide. The metal precipitation to remove the impurities was controlled by the pH value using the caustic soda. And also, D2EHPA and $CYANEX^{(R)}272$ were used in the solvent extraction process in order to remove the impurities again. The high-purity $CoSO_4$ solution was recovered by the processes mentioned above. We made the 6 wt.% $CoSO_4$ solution mixed with distilled water. And the 6 wt.% $CoSO_4$ solution was mixed with oxalic acid by the stirring method and dried in oven. $LiCoO_2$ as a cathode material for LIB was formed by the calcination after the drying and synthesis with the $Li_2CO_3$ powder. We assembled the cells using the $LiCoO_2$ powders and evaluated the electrochemical properties. And then, we confirmed possibility of the recyclability about the cathode materials for LIBs.