• Journal of Korean Society of Forest Science
• /
• v.26 no.1
• /
• pp.57-65
• /
• 1975

This study was carried out to examine the effect of manufacturing factors on physical properties of hardboard (S.I.S) made from the juvenile wood of sycamore (Platanus orientalis L.) The results obtained may be summarized as follows: 1. The difference among the yields of pulp treated with preheat time (defibrate condition) was significant in those of treatments. There was no difference in the yield of pulp treated with defibrate time. The yields of pulp on the tree age classes were shown the difference by 2<4<6<8 years. 2. The specific gravities of hardboard that were treated with hot pressing conditions showed us significantly in those of treatments. There was no difference on the specific gravities among hardboards, treated with resin and wax contents. But in all cases of the specific gravities satisfied the standard which specified the KS F 3203 (Hardboard) 3. The moisture contents of hardboard satisfied the standard which calls for 13-percent below. There were difference in moisture contents between hardboard, treated with preheating time, resin and wax contents and hot pressing conditions. And the moisture contents of hardboard on the tree age classes showed the difference by 2<4<6<8 years. 4. The water absorption and thickness swelling of hardboard treated with defibrations, resin and wax contents, and hot pressing conditions were significant in those of treatments. And the water absorption and thickness swelling of hardboard on the tree age classes showed us the significant difference by 8<6<4<2 years. 5. The difference among the flexural strength in using tested three conditions showed us the difference by defibration$200kg/cm^2$) of hardboard, it is likely to be recommened that the juvenile wood of sycamore is valuable for the raw materials of hardboards.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.3
• /
• pp.36-44
• /
• 2007

The purpose of this study was to investigate thermal stability, reactivity, and bonding strength of existing epoxy resin mixed with the epoxidized soybean oil (ESBO) in order to use soybean oil economically. In the dry shear test, the marked strengths showed $30.5kgf/cm^2$ at the ratio of ESBO to epoxy resin 9 : 1 and $6.2kgf/cm^2$ at the ratio 8 : 2. The bonding strengths of the others, except mixing ratios 2 : 8 and 1 : 9, exceeded the requirement of Korean plywood standard of $7.0kgf/cm^2$. In the wet shear test, the result was $5.8kgf/cm^2$ at the ratio 9 : 1. There were no thickness swelling and moisture absorption in the water resistance of the film. The value of activation energy, Tg (${\Delta}E$), by DSC analysis showed between $110^{\circ}C$ and $120^{\circ}C$ through all ratios. Epoxy in the epoxy resin fully reacted with the hardener (TETA), but it is difficult to decide that epoxys in the ESBO were reacted directly with the hardener from FT-IR analysis. As the mixing ratio of ESBO increased, the thermal stabilities dropped from TGA analysis. From the comprehensive view on the results of above experiments, it could be confirmed through experiments that the ESBO in the mixed adhesive of epoxy resin/ESBO played a role as an extending agent level of epoxy adhesive, and we were able to know that in order to utilize ESBO as an adhesive, a study should be performed on the condition of hardening, inducible of the hardening reaction.

• Korean Journal of Agricultural Science
• /
• v.6 no.1
• /
• pp.45-55
• /
• 1979

This study made to find the variation of strengths of briquette ash which were hardened into cement. The briquette ash were mixed with the cement, ((cement (90%)+slaked lime (10%)) and ((cement (80%)+fly ash (20%)) in the ratio of 1:2, 1:3, 1:4, 1:5, 1:7 and 1:9, respectively, and these were compared with the one made of cement plus standard sand in the strengths of compression, tension and bending at the ages of 7 days and 28 days. The results from the study conducted preliminary without studying the economical aspects or duration of the products are summarized as follows: 1. The compressive strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash and (cement+fly ash) to briquette ash were 84%, 90% and 75% at the age of 7 days and 84.9%, 73.5% and 69.8%, respectively of those of Korean Standard values. 2. The compressive strength s of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash and (cement+fly ash) to briquette ash were 69.3%, 75.1% and 41.3% at the age of 7 days and 56.4%, 49%, and 46.5% at the age of 28 days, respectively of the mortar made of standard sand. 3. The tension strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash, and (cement+fly ash) to briquette ash were 64.4%, 47.1% and 35.4% at the age of 7days and 69.6%, 64.8%, and 57.3%, respectively of that of the mort ar produced with standard sand. 4. The bending strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash, and (cement+fly ash) to briquette ash were 46.3%, 65.9% and 39.1% at the age of 7 days and 89.9%, 96.7%, and 85.1%, respectively of that of mortar produced with standard sand. 5. The bending strength of the mortar was lower than that of cement mortar, when the briquette ash were harqened into cement. However, the mortar produced by such method seemed to be used as the secondary products of cement or concrete. The additional usefullness of the hardened biquette ash can be found in contributing toward the solving the various pollution problems, the saving the labor costs needed to clean-up waste materials, and the saving the construction materials.

• Journal of Korean Society of Forest Science
• /
• v.30 no.1
• /
• pp.19-29
• /
• 1976

The fiberboard and paper mills in this country are much affected by the price hikes and shortage of phenolic resins, since phenolic acid as a raw material depends on imported good. It is prerequisite to fiberboard industry to help replace with other sized and stabilize the prices and supply of them, improving the quality of boards. Thus, the present study was carried out to examine the effect of strength increasing sized such as urea formaldehyde resin (anion and cation type) and urea melamine copolymer resin, on the quality of the wet forming hardboard, and comparing them with two types of proprietary modified melamine resins, and ordinary size, phenol resin. The Asplund pulp was prepared from wood wastes mixed with 20 percent of lauan and 80 percent of pines as a fibrous material. After sizing agents were added at a pH of 4.5 for 10 minutes with alum in the beater, the stock was made in the form of wet sheet, prepared, and then performed by hot pressing cycle: $180^{\circ}C$, $50-6-5kg/cm^2$, 1-2-7 minutes. The properties of hardboard were examined after air conditioning. The results obtained are summarized as follows: 1. There is a significant difference in specific gravity among hardboards that were treated with strength increasing resins, but no difference is effected by the increase in the resin content. In the case of modified melamine resin, its specific gravity is highest. The middle group comprises cation type of urea resin, anion type of urea resin, and acid colloid of urea-melamine copolymer resin. The lowest is phenolic resin. 2. The difference of the moisture content of hardboard both by the resins and by the amount of each resin applied is significant. The moisture content of hardboard becomes lower along with the increase of each resin content, but there is no difference between 2 and 3 percent. 3. For water absorption, there is a significant difference both in the adhesives used and in the amount of paraffin wax emulsion. The water resistance becomes higher inn proportion to the content of the paraffin wax emulsion. To satisfy KS F standards of the water resistance, a proprietary modified melamine resin (p-6100) and modified cation type of urea resin (p-1500) do not require any paraffin wax emulsion, but in the case of anion type of urea resin, cation type of urea resin, and urea-melamine copolymer resin, 1 percent of paraffin wax emulsion is needed, and 2 percent of paraffin wax emulsion in the case of phenolic resin. 4. The difference of flexural strength of hardboard both by the resins and by the amount of each resin is significant. Modified melamine resin shows the highest degree of flexural strength. Among the middle group are urea-melamine copolymer resin, p-1500, anion type of urea resin, and cation type of urea resin. Phenolic resin is the lowest. The cause may be attributable to factors combined with the pressing temperature, sizing effect, and thermal efficiency of press platens heated electrically. 5. Considering the economic advantages and properties of hardboard, it is proposed that urea-melamine copolymer resin and cation type of urea resin be used for the development of the fiberboard industry. It is desirable to further develop the modified urea-melamine copolymer resin and cation type of urea resin through continuous study.

• Korean Journal of Soil Science and Fertilizer
• /
• v.40 no.5
• /
• pp.418-428
• /
• 2007

Physical and chemical properties of the aggregate by-products including sludge and crushed dust samples collected from the 21 private companies throughout the country were analyzed to evaluate possible usage of the by-products as artificial soil materials for plantation. The pH of the materials ranged from 8.0 to 11.0. The organic matter content was $2.85g\;kg^{-1}$, and the total nitrogen content and available phosphate content were low as 0.7 percents and $12.98mg\;kg^{-1}$, respectively. Exchangeable $Ca^{2+}$, $Mg^{2+}$, $K^+$, and $Na^+$ were 2.29, 0.47, 0.02 and $0.05cmol\;kg^{-1}$, respectively. Heavy metal contents were lower than the limits regulated by environmental law of Korea. Textural analysis showed that most of the materials were silt loam with low water holding capacity ranged from 0.67 to 7.41 percents, and with low hydraulic conductivity ranged from 0.4 to $2.8m\;s^{-1}$. Mineralogical analysis showed that the aggregate by product materials were mostly composed of silicate, alumina and ferric oxides except calcium oxide dominant materials derived from limestones. The primary minerals were quartz, feldspars and dolomites derived from granite and granitic gneiss materials. Some samples derived from limestone material showed calcite and graphite together with the above minerals. According to the result, it can be concluded that the materials could be used as the artificial soil material for plantation after proper improvement of the physico-chemical properties and fertility.