• Computers and Concrete
• /
• v.11 no.6
• /
• pp.531-539
• /
• 2013

An experimental investigation of mechanical properties of jute fiber-reinforced concrete (JFRC) has been reported for making a suitable construction material in terms of fiber reinforcement. Two jute fiber reinforced concretes, called jute fiber reinforced normal strength concrete (JFRNSC) and jute fiber-reinforced high-fluidity concrete (JFRHFC), were tested in compression, flexure and splitting tension. Compressive, flexural and splitting tensile strengths of specimens were investigated to four levels of jute fiber contents by volume fraction. From the test results, Jute fiber can be successfully used for normal strength concrete (NSC) and high-fluidity concrete (HFC). Particularly, HFC with jute fibers shows relatively higher improvement of strength property than that of normal strength concrete.

• Journal of Adhesion and Interface
• /
• v.8 no.3
• /
• pp.9-15
• /
• 2007

The interfacial evaluation of surface modified Jute fiber/polypropylene (PP) composites before and after hydration was investigated using micromechanical test and dynamic contact angle measurement. The IFSS of alkaline and silane-treated Jute fiber/PP composites increased, whereas after hydration, the IFSS of the untreated, alkaline- and silane-treated Jute fibers/PP composites decreased due to swelled fibrils by water infiltration. The interfacial adhesion of silane treated fiber/PP composites was higher than alkaline-treated or the untreated cases. The surface energies of Jute fiber treated under various conditions were obtained using dynamic contact angle measurement. Especially after hydration, the thermodynamic work of adhesion was calculated by considering water interlayer, which indicated the stability of IFSS between silane treated Jute fiber and PP matrix showing better than others.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.3A
• /
• pp.251-260
• /
• 2011

In this study, the effect of natural jute fiber volume fraction on the bond characteristics of polyolefin based macro fiber in natural jute fiber reinforced cement composites, including bond strength, interface toughness, and microstructure analysis are presented. The experimental results on polyolefin based macro fiber pullout test of different conditions are reported. Natural jute fiber volume fractions ranging from 0.1% to 0.2% are used in the mix proportions. Pullout tests are conducted to measure the bond characteristics of polyolefin based macro fiber from natural jute fiber reinforced cement composites. Test results are found that the incorporation of natural jute fiber can effectively enhance the polyolefin based macro fiber-cement matrix interfacial properties. The bond strength and interface toughness between polyolefin based macro fiber and natural jute fiber reinforced cement composites increases with the volume fraction of natural jute fiber. The microstructural observation confirms the findings on the interface bond mechanism drawn from the fiber pullout test results.

• Advanced Composite Materials
• /
• v.18 no.3
• /
• pp.197-208
• /
• 2009

Changes occurring in jute and coir fiber composites with 2-8% concentration of a NaOH treatment for 24 h were investigated, respectively, for void content, microscopy images, mechanical properties and water absorption. The jute and coir fibers were vacuum dried before molding composite specimens. Mechanical properties indicated good adhesion between natural fibers and PP. Jute fibers, when alkali-treated with 2% concentration for 24 h, showed best improvement in tensile strength by 40% and modulus by 9%, respectively, while coir fibers, when alkali-treated with 6% concentration for 24 h, showed best improvement in tensile strengths by 62% and modulus by 17%, respectively. With 2% concentration of alkali-treatments, the elongation of jute and coir composites reached 8% and 13.5%, respectively. Moisture absorption for jute and coir composites are 50% and 60% lower than untreated fiber composites, respectively.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.11a
• /
• pp.34-35
• /
• 2014

In this study, the effects of high temperatures on the compressive strength and elastic modulus of HPC with pp and jute fiber (jute fiber addition ratio: 0.075 vol%; length: 12 mm; PP fiber addition ratio: 0.075 vol%; length: 12 mm) were experimentally investigated. The work was intended to clarify the influence of elevated temperatures ranging from 20 to 500℃ on the material mechanical properties of HPC at 80 MPa.

• Structural Engineering and Mechanics
• /
• v.56 no.6
• /
• pp.1095-1113
• /
• 2015

Jute rope is one of the most popular materials used for composites in various industries and in civil engineering. This experimental study investigated two types of jute rope with different diameters for jute rope composite plates to determine the best combination of jute rope and carbon fiber in terms of ratio and physical and mechanical properties. Eight combinations of carbon fiber and jute rope with different percentages of carbon fiber were analyzed. Tensile tests for the jute rope composite plate and hybrid jute rope composite were conducted, and the mechanical and physical properties of the specimens were compared. Thereafter, the ideal combinations of jute rope with an optimum percentage of carbon fiber were identified and recommended. These particular combinations had tensile strengths that were 2.23 times and 1.76 times higher than other varieties in each type.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.111-115
• /
• 2005

Recently, natural fibers draw much interests in composite industry due to low cost, light weight, and environment-friendly characteristics compared with glass fibers. In this study, mechanical properties were evaluated for two extreme cases of jute fiber orientations, i.e. the unidirectional yarn composites and the felt fabric composites. Samples of jute fiber composites were fabricated by RTM process using epoxy resin, and tensile, compression, and shear tests were conducted. As can be expected, unidirectional fiber specimens in longitudinal direction showed the highest strength and modulus. Compared with glass/epoxy composites of the similar fabric architecture and fiber volume fraction, the tensile strength and modulus of jute felt/epoxy composites reached only 40% and 50% levels. However, the specific tensile strength and modulus increased to 80% and 90% of the glass/epoxy composites. The main reason for the poor mechanical properties of jute composites is associated with the weak interfacial bonding between fiber and matrix. The effect of surface treatment of jute fibers on the interfacial bonding will be examined in the future work.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.55 no.4
• /
• pp.29-35
• /
• 2013

The objective of the current study is to evaluate the effects depending on the types of reinforcing fibers being influential in view of mechanical properties and impact resistance of hybrid fiber reinforced concrete (HFRC) for applications to precast concrete structure. Hybrid fibers applied therefor were three types such as PP/MSF (polypropylene fiber+macro synthetic fiber), PVA/MAF (polyvinyl alcohol fiber+MSF) and JUTE/MSF (natural jute fiber+MSF), where the volume fraction of PP, PVA and natural jute was applied with 0.2 %, respectively, while based on 0.05 % volume fraction of MSF. The HFRC was tested for slump, compressive strength, flexural strength and impact resistance. The test result demonstrated that mixture of such hybrid fibers improve compressive strength, flexural strength and impact resistance of concrete. Moreover, it was found that HFRCs to which hydrophilic fibers, i.e. PVA/MSF and JUTE/MSF, were mixed show more improved features that HFRC to which non-hydrophilic fiber, i.e. PP/MSF was mixed. Meanwhile, the finding that PVA/MSF HFRC exhibited better performance than JUTE/MSF HFRC was attributed from the former having higher aspect ratio than that of the latter.

• Composites Research
• /
• v.20 no.3
• /
• pp.55-62
• /
• 2007

Interfacial evaluation and durability of Jute and Hemp fibers/polypropylene (PP) composites were investigated. Moisture content of various treated conditions were measured by thermogravimetic analyzer (TGA). After boiling water test, mechanical properties and IFSS between Jute, Hemp fibers and PP matrix decreased. On the other hand, work of adhesion increased due to swelled fibril by water. Surface energies of Jute and Hemp fibers before and after boiling water test were obtained using dynamic contact angle measurement. IFSS was not always consistent with thermodynamic work of adhesion. In boiling water case, since Jute and Hemp fibers could be swelled by water, surface area and moisture infiltration space increased. Environmental effect on microfailure modes of Jute or Hemp fibers and Jute or Hemp fibers/PP composites were obtained by observing via optical microscope and by monitoring acoustic emission (AE) events and their AE parameters. After boiling water test, unlike Hemp fiber, microfailure process of Jute fiber could occur due to low tensile strength by swelled fibril. In addition, AE events occurred more and AE amplitude and energy became lower than those of before boiling water test.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.57 no.2
• /
• pp.67-73
• /
• 2015

This study evaluated the effects of fibers on the void ratio, compressive strength and repeated freezing and thawing resistance of porous vegetation concrete with binder type (non-sintering inorganic binder and blast furnace slag cement) and natural jute fiber volume fraction (0.0 %, 0.1 % and 0.2 %). The natural jute fiber volume fraction affected the void ratio, compressive strength and repeated freezing and thawing resistance. Added of natural jute fiber resulted in improved properties of the void ratio, compressive strength and freezing and thawing resistance. Also, the both compressive strength and freezing and thawing resistance increased with natural jute fiber volume fraction up to 0.1 % and then decreased with fiber volume fraction at 0.2 %.