• Journal of Welding and Joining
• /
• 제20권5호
• /
• pp.127-133
• /
• 2002

In this study, metal transfer characteristics in pulsed current metal inert gas (MIG) welding of aluminum was investigated. Based on the metal transfer characteristics from direct current electrode negative MIG welding, the one drop per one pulse(ODOP) condition was predicted and compared with experimental data. The results indicated that experimental pulse range for the ODOP condition is wider than that predicted from the DCEP MIG welding data. In addition, more stable metal trnasfer behavior was obtained at the higher end of the ODOP condition.

• Journal of Welding and Joining
• /
• 제26권1호
• /
• pp.76-82
• /
• 2008

The effect of Nb addition on the precipitation and precipitate coarsening behavior was investigated in Ti and Ti + Nb steel weld HAZ. A dilatometer equipped with a He-quenching system was used to simulate the weld thermal cycle. Compared to $TiC_yN_{1-y}$ precipitate in a Ti containing steel, $Ti_xNb_{1-x}C_yN_{1-y}$ complex particle with addition of Nb is precipitated in a Ti + Nb containing steel. Meanwhile, precipitate coarsening occurred more easily in Ti + Nb steel, which may be because the high temperature stability of $Ti_xNb_{1-x}C_yN_{1-y}$ complex particle is deteriorated by the Nb addition.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.53-59
• /
• 1987

The effect of applied stress, current density and heat-treatment after welding on the time to fracture, fracture behavior was investigated by the method of constant load tensile testing under catholic charging with hydrogen in E.B. welded 250,300 Grade 18% Ni Maraging steel sheet. The main results obtained are as follows: 1. All specimen showed the characteristic delayed failure and the time to fracture showed decreasing tendency with the increase in current density and applied stress. 2. Hydrogen embitterment susceptibility of notched specimen after solution-treatment and aging after welding was more increased than that of aged smooth specimen and as welded specimen. 3. Fracture surface showed a typical intergranular fracture on the border, a dimple pattern in the center of specimen and some quasi-cleavage fracture between the intergranular and the dimple.

• Journal of Welding and Joining
• /
• 제6권4호
• /
• pp.35-43
• /
• 1988

Welding residual stresses were calculated by two dimensional thermal elasto-plastic analysis using element method. Complicated plastic behavior during heat transfer was simulated with time. Fist, temperature distributions. To consider time varying behavior of material properties and loading and unloading processes, iterative calculation based on initial stiffness method was carried out. The method proposed by Yamata was used in time increment control which determined the accuracy of claculation. comparison with other caculated and experimental results shows fairly good agreement.

• Journal of Welding and Joining
• /
• 제16권6호
• /
• pp.77-85
• /
• 1998

Effects of non-cleaning and cleaning fluxes on the wetting properties and defects at flow soldered joints were investigated. Non-cleaning flux (R-type of 3.3% solid content) and cleaning flux (RMA-type of 15% solid content) were used. Wetting test was accomplished by wetting balance method with changing surface state of wetting specimen, CU. Sn-37%Pb solder was used for wetting test and flow soldering. As experimental results, the wetting time for vertical force from the surface tension being zero was mainly affected by surface state of the wetting specimen. Non-cleaning flux had a good wettability compared with cleaning flux. In case of non-cleaning flux, conveyor speed had a great affection to defects of bridge, icicle, and poor solder.

• Journal of Welding and Joining
• /
• 제19권5호
• /
• pp.540-547
• /
• 2001

This study has evaluated the wear behavior of PTA (Plasma Transferred Arc) Inconel 625 and Stellite 6 overlays on Nimonic 80A substrate. Nimonic 80A alloy was also included for comparison. In order to evaluate the wear performance, three-body abrasive wear test and pin-on-disk dry sliding wear test were performed. Microstructural development during the solidification of deposits is also discussed. Wear test results show that the wear rate of Stellite 6 deposit is lower than that of Inconel 625 deposit and Nimonic 80A. The sliding wear resistance of overlay deposits follows a similar trend to the abrasive wear resistance, but for Nimonic 80A. The main wear mechanisms were abrasive wear for Inconel 625 deposit, adhesive wear and delamination for Stellite 6 deposit in pin-on-disk dry sliding wear test and ploughing in three-body abrasive wear test. Cross sectional examinations of the worn surface of pin specimens after pin-on-disk dry sliding wear test implies that the plastic deformation near worn surface has occurred during the wear testing.

• Journal of Welding and Joining
• /
• 제10권4호
• /
• pp.250-258
• /
• 1992

In order to clarify the mechanical behavior of welding crack and to evaluate the mechanical characteristics of welded parts in thick plate, it is very important to accurately predict the welding deformation and residual stress including transient state before welding. In this paper, the theory of a three-dimensional elasto-plastic problem for the analysis of mechanical phenomenon of welding joint on the plate is developed into an efficient and accurate method based on the finite element method, and then several examples are considered by using the proposed model. The results of numerical analyses are discussed in the viewpoint of the mechanical characteristics of the distribution of three-dimensional welding residual stresses, plastic strains and their production mechanism on the thick plate.

• Journal of Welding and Joining
• /
• 제33권6호
• /
• pp.42-48
• /
• 2015

Reduced activation ferritic/martensitic steels are recognized as the primary candidate structural materials for fusion blanket systems. Welding is an inevitable for breeding blanket for pressure tightness and radioisotope confinement. Especially, TIG welding was chosen for sealing because it has the largest gap allowance compared to the other welding methods, and its properties are controllable by feed wire and welding conditions. In this study, the low cycle fatigue test using two-type gage such as extensometer and strain gage was applied to the TIG welded joint of F82H steel, for evaluating fatigue damage accumulation behavior of the HAZs. As the result, the over-tempered HAZ have shown a higher fatigue damage accumulation compared with other materials at all the testing conditions.

• Journal of Welding and Joining
• /
• 제20권4호
• /
• pp.534-537
• /
• 2002

In the various industry such as shipbuilding and automobile, etc., Al-alloys are used to reduce weight and improve economical efficiency, and they are mainly utilized in the process of Friction Stir Welding (FSW). A number of studies have been carried out on the metallurgical characteristics of friction stir welding In Al-alloys. However, research on the thermal behavior of FSW by using numerical analysis is not sufficient in the domestic and abroad. In this paper, therefore, numerical simulation was used to find out thermal behaviour of FSW by finite element method. We considered heat source that occurred by friction between tool shoulder including pin and base metal. To confirm the result of simulation, macrostructure is examined and compared after welding. The result of numerical simulation shows that Al-alloy is welded under a melting point of Al around pin by FSW.

• Journal of Welding and Joining
• /
• 제20권4호
• /
• pp.491-497
• /
• 2002

Dynamic behavior of the molten drop during the peak period in the pulsed-GMAW is simulated in this work using the VOF(volume of the fluid) algerian. The dynamic characteristics of molten drop such as minimum radius, average velocity and displacement of mass center were computed as well as the internal pressure and velocity. The minimum and maximum peak durations for detaching a drop were calculated.. The result of Analysis reveals that peak current and volume of pendant drop are important factors which affecting drop detachment. A simplified model of constant acceleration is proposed to describe the behavior of molten drop during peak current, and its results agree with the experimental results.