• Journal of Conservation Science
• /
• v.36 no.6
• /
• pp.549-561
• /
• 2020

This study aimed to assess the performance and life of nine natural mineral dancheong pigments: Seokganju, Jinsa, Hwangto, Jahwang, Wunghwang, Seokrok, Noerok, Seokcheong, and Baekto. The design of the accelerated weathering test considered the domestic climate characteristics and the location of Dancheong. Outdoor weathering tests were conducted at the Research Institute in Daejeon and the Sungnyemun Gate in Seoul to confirm the field reproducibility of the accelerated weathering test. Monitoring of the physical changes in pigments through accelerated and outdoor weathering tests are based on ultraviolet exposure dose. Despite small cracks at the beginning of the tests, the monitoring showed that Seokganju and Baekto had no marked physical changes, but the surface cracks of Jinsa and Seorok continue to expand. Hwangto and Noerok were marked with water or were resin stained, and the particles of Jahwang, Wunghwang, and Seokcheong had lost their luster. Despite the absolute difference in color change in each test, the final chromaticity change patterns of pigments were similar in that the color difference between Baekto and Noerok was below five, and Jina was above 28. The physical and surface color pigment changes were more concentrated in outdoor weathering tests than in accelerated tests, and the Seoul site was more intense than the Daejeon site. This is because outdoor weathering tests are exposed to severe variations of temperature and moisture or deposition of dust particles and, in the case of Seoul, the site is more exposed to the external environment than the Daejeon site.

• Journal of the Mineralogical Society of Korea
• /
• v.32 no.4
• /
• pp.259-271
• /
• 2019

We evaluated mineralogical, physical property and accelerated weather resistance of cinnabar, realgar and orpiment used as cultural heritages and traditional paintings. JB and JS are sample names of cinnabar and JH and UH are sample names of orpiment and Realgar, respectively. As a result of mineralogical property evaluation, Jinsa was identified cinnabar (HgS) and there was no difference in chemical composition according to the grade. UH and JH were confirmed realgar (AsS) and orpiment (As₂S₃), respectively. The polarization characteristics such as shape and color indicate that pigments using our test were natural mineral pigment observed by polarization microscope. Especially, in the case of cinnabar, it is not easy to distinguish between natural mineral pigment and synthetic pigment. But the results of polarization microscope said that cinnabar is natural occurring mineral which have authentic mineral particle and unevenly fracture. As a result of thermal analysis, JH has a higher glass transition temperature and heat stability than UH. After accelerated weather test, cinnabar, realgar and orpiment were striking result in color change because of light degradation. Red color of cinnabar turn into black and the color of realgar and orpiment became brighter than before. JB (meta-cinnabar) is more photosensitivity and faster becoming dark than JB (cinnabar). Finally light transforms realgar (red, As₄S₄) in arsenolite (As₂O₃).