• 대한기계학회논문집
• /
• 제13권4호
• /
• pp.653-659
• /
• 1989

본 연구에서는 실험방법과 해석방법 등의 차이가 Ｊ$_{IC}$ 값에 미치는 영향을 고찰하여 보았으며, E 813-81법으로 해석된 Ｊ$_{IC}$ 값으로 환산하는 방법을 제안하고 몇 가지 재료와 환경에서 그 오차를 검토하였다.하였다.

• Journal of Mechanical Science and Technology
• /
• 제16권7호
• /
• pp.902-910
• /
• 2002

Cast stainless steel may experience embrittlement when it is exposed approximately to 300$\^{C}$ for a long period. In the present investigation, the three classes of the thermally-aged CF8M specimen were prepared using an artificially-accelerated aging method. After the specimens were held for 300, 1800 and 3600hrs. at 430$\^{C}$, respectively, the specimens were quenched in water which is at room temperature. Load versus load line displacement curves and J-R curves were obtained using the unloading compliance method. talc values were obtained using the ASTM E813-87 and ASTM E 813-81 methods. In addition to these methods, talc values were obtained using the SZW (stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are J$\_$Q/=543.9kJ/㎡ for virgin materials. The values of J$\_$IC/ for the degraded materials at 300, 1800 and 3600hrs. are obtained 369.25kJ/㎡, 311.02kJ/㎡, 276.7kJ/㎡, respectively. The results obtained by the SZW method are compared with those obtained by the unloading compliance method. Both results are quite similar. Through the elastic-plastic fracture toughness test, it is found that the value of loc is decreased with an increase of the aging time.

• 대한기계학회논문집A
• /
• 제24권10호
• /
• pp.2405-2412
• /
• 2000

A cast stainless steel may experience an embrittlement when it is exposed to approximately 30$0^{\circ}C$ for long period. In the present investigation, The three classes of the thermally aged CF8M specimie n are prepared using an artificially accelerated aging method. Namely, after the specimen are held for 300, 1800 and 3600hrs. at 43$0^{\circ}C$ respectively, the specimens are quenched in water to room temperature. Load versus load line displacement curves and J-R curves are obtained using the unloading compliance method. $J_{IC}$ values are obtained following ASTM E 813-87 and ASTM E 813-81 methods. In addition to these methods, JIC values are obtained using SZW(stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are $J_Q$=485.7 kJ/m$^2$ for virgin material, $J_{IC}$ of the degraded materials associated with 300, 1800 and 3600hrs are obtained 369.25 kJ/m$^2$, 311.02 kJ/m$^2$, 276.7 kJ/m$^2$, respectively. The results of SZW method are similar to those of the unloading compliance method. Through the elastic-plastic fracture toughness test, it is found that the value of $J_{IC}$ is decreased with increasing of the aging time. The results obtained through the investigation can provide reference data for a leak before break(LBB) of reactor coolant system of nuclear power plants.