• Clean Technology
• /
• v.13 no.3
• /
• pp.180-187
• /
• 2007

The indium tin oxide(ITO) film on PET was prepared by a wet coating method to obtain the transparent film with a high conductance. ITO nano-particles was synthesized by a SAS method at 15 MPa and $50^{\circ}C$, where optimized rate of In/Sn was 65. Average diameter and resistivity of ITO obtained from SAS are $15{\pm}2\;nm$ and $4{\times}10^4\;{\Omega}{\cdot}cm$. Coating solution was prepared at pH 10. The ITO film was obtained by solution including 0.1 0.5, 1, and 2 ITO wt% on PET. Roughness(Ra) of ITO film with 0.1, 0.5, 1. and 2 ITO wt% is 4, 10, 12, and 16 nm. Resistivity with an increasing ITO concentration is $3.7{\times}10^6,\;2.4{\times}10^6,\;8{\times}10^5,\;and\;2{\times}10^5\;{\Omega}{\cdot}cm$. Transmissivity of ITO film decreased as 89, 88, 86, and 82% with an increasing ITO concentration as 0.1, 0.5, 1, and 2 wt%.