• 한국분말재료학회지
• /
• 제21권6호
• /
• pp.422-428
• /
• 2014

In this study, the reduction kinetics and behaviors of oxides in the water-atomized iron powder have been evaluated as a function of temperature ranging $850-1000^{\circ}C$ in hydrogen environment, and compared to the reduction behaviors of individual iron oxides including $Fe_2O_3$, $Fe_3O_4$ and FeO. The water-atomized iron powder contained a significant amount of iron oxides, mainly $Fe_3O_4$ and FeO, which were formed as a partially-continuous surface layer and an inner inclusion. During hydrogen reduction, a significant weight loss in the iron powder occurred in the initial stage of 10 min by the reduction of surface oxides, and then further reduction underwent slowly with increasing time. A higher temperature in the hydrogen reduction promoted a high purity of iron powder, but no significant change in the reduction occurred above $950^{\circ}C$. Sequence reduction process by an alternating environment of hydrogen and inert gases effectively removed the oxide scale in the iron powder, which lowered reduction temperature and/or shortened reduction time.

• 한국분말재료학회지
• /
• 제28권6호
• /
• pp.518-526
• /
• 2021

This review summarizes the recent progress in iron-oxide-based heat generators. Cancer treatment using magnetic nanoparticles as a heat generator, termed magnetic fluid hyperthermia, is a promising noninvasive approach that has gained significant interest. Most previous studies on improving the hyperthermia effect have focused on the construction of dopant-containing iron oxides. However, their applications in a clinical application can be limited due to extra dopants, and pure iron oxide is the only inorganic material approved by the Food and Drug Administration (FDA). Several factors that influence the heat generation capability of iron-oxide-based nanoparticles are summarized by reviewing recent studies on hyperthermia agents. Thus, our paper will provide the guideline for developing pure iron oxide-based heat generators with high heat dissipation capabilities.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.446-447
• /
• 2006

Magnetic oxide-coated iron nanoparticles with the mean size ranging from 6 to 75 nm were synthesized by aerosol method using iron carbonyl as a precursor under the flowing inert gas atmosphere. Oxide shells were formed by passivation of asprepared iron particles. The influence of experimental parameters on the nanoparticles' microstructure, phase composition and growth behavior as well as magnetic properties were investigated and discussed in this study.

• 한국분말재료학회지
• /
• 제12권3호
• /
• pp.225-230
• /
• 2005

In order to prevent the oxide formation on the surface of nano-size iron particles and thereby to improve the oxidation resistance, iron nanoparticles synthesized by a chemical vapor condensation method were directly soaked in hexadecanethiol solution to coat them with a polymer layer. Oxygen content in the polymer-coated iron nanoparticles was significantly lower than that in air-passivated particles possessing iron-core/oxide-shell structure. Accordingly, oxidation resistance of the polymer-coated particles at an elevated temperature below $130^{\circ}C$ in air was $10\~40$ times higher than that of the air- passivated particles.

• 한국분말재료학회지
• /
• 제20권3호
• /
• pp.180-185
• /
• 2013

The iron oxides nanoparticles and iron oxide with other compounds are of importance in fields including biomedicine, clinical and bio-sensing applications, corrosion resistance, and magnetic properties of materials, catalyst, and geochemical processes etc. In this work we describe the preparation and investigation of the properties of coated magnetic nanoparticles consisting of the iron oxide core and organic modification of the residue. These fine iron oxide nanoparticles were prepared in air environment by the co-precipitation method using of $Fe^{2+}$: $Fe^{3+}$ where chemical precipitation was achieved by adding ammonia aqueous solution with vigorous stirring. During the synthesis of nanoparticles with a narrow size distribution, the techniques of separation and powdering of nanoparticles into rather monodisperse fractions are observed. This is done using controlled precipitation of particles from surfactant stabilized solutions in the form organic components. It is desirable to maintain the particle size within pH range, temperature, solution ratio wherein the particle growth is held at a minimum. The iron oxide nanoparticles can be well dispersed in an aqueous solution were prepared by the mentioned co-precipitation method. Besides the iron oxide nanowires were prepared by using similar method. These iron oxide nanoparticles and nanowires have controlled average size and the obtained products were investigated by X-ray diffraction, FESEM and other methods.

• 한국세라믹학회지
• /
• 제48권2호
• /
• pp.117-120
• /
• 2011

In this study, the redox state of iron in sodium silicate glasses was varied by changing the melting conditions, such as the melting temperature and particle size of iron oxide. The oxidation states of the iron ion were determined by wet chemical analysis and UV-Vis spectroscopy methods. Iron commonly exists as an equilibrium mixture of ferrous ions, $Fe^{2+}$, and ferric ions $Fe^{3+}$. In this study, sodium silicate glasses containing nanoparticles of iron oxide (0.5% mol) were prepared at various temperatures. Increase of temperature led to the transformation of ferric ions to ferrous ions, and the intensity of the ferrous peak in 1050 nm increased. Nanoparticle iron oxide caused fewer ferrous ions to be formed and the $\frac{Fe^{2+}}{Fe^{3+}}$ equilibrium ratio compared to that with micro-oxide iron powder was lower.

• 자원리싸이클링
• /
• 제11권5호
• /
• pp.24-29
• /
• 2002

철강압연공장에서 산세공정중 발생하는 산화철의 색상을 개선하기 위하여 배소로 조업과 색상혼합공정을 연구하였다. 배소로 조업에서는 조업온도, 폐산장입량, 폐산분사 노즐수에 대하여 검토하였으며, 색상혼합공정에서는 산화티탄, 실리카, 괴타이트를 색상혼합재로 검토하였다. 배소로 조업에서는 조업온도를 낮게 할수록 산화철의 명도가 개선되었으며, 색상혼합공정에서는 괴타이트 첨가 경우에 제일 많이 산화철의 적색 및 명도가 개선되었다.

• 한국주조공학회지
• /
• 제10권2호
• /
• pp.154-161
• /
• 1990

The microstructures of sintered products of $Fe_2O_3$or $Fe_3O_4$-Oxide added cast iron powder was investigated. And the effects of particle size distribution was investigated too. As the result, the structures of sintered products did not related to the species of Fe-Oxide. Th porosity of sintered products was decreased in size and spherodized with increasing sintering temperature, decreasing Fe-Oxide quantity. Fe-Oxide itself did not hinder sintering of cast iron powder particularly, therefore sintering could be occurred without termination of reduction of it. And the sintered products of finer particle size distribution had finer and more spherodized porosity, and had minimized the deviation of size and shape of porosity.

• 자원리싸이클링
• /
• 제21권1호
• /
• pp.75-81
• /
• 2012

선탄경석을 환경개선물질로 순환자원화하기 위해 철산화물과 혼합하여 중금속 불용화제를 제조하고 이의 적정제조 조건과 중금속에 대한 불용화 성능을 평가하였다 선탄경석을 분쇄한 후 철산화물의 분말을 혼합하여 구형의 펠릿을 제조하고 이를 가열하여 중금속 불용화제를 제조하였다. 온도별로 가열한 결과, $1100^{\circ}C$부터 선탄경석에 함유된 탄질분에 의해 영가철이 생성되었다. 제조된 불용화제는 구형의 다공체로서 공극률은 34.63%, 겉보기 밀도는 1.31 g/mL, 공극의 평균크기는 9.82 ${\mu}m$로 측정되었다. 불용화제를 비소(V), 구리(II), 크롬(VI), 카드뮴(II)이 함유된 각각의 중금속 용액과 반응시킨 결과, 영가철이 생성된 $1100^{\circ}C$에서 제조된 펠릿이 중금속 불용화도가 높고 pH를 더 높이는 것으로 나타났다. 중금속농도 10 ppm의 용액을 99.9%이상 불용화하기까지 비소의 경우 1시간, 크롬의 경우 2시간, 구리의 경우 4시간이 필요하였다. 그러나 카드뮴의 경우 불용화도가 낮게 나타났고 중금속농도가 높을수록 불용화도가 더 낮아지는 것으로 나타났다.

• 한국결정성장학회지
• /
• 제11권4호
• /
• pp.176-179
• /
• 2001

Iron oxide powders were prepared under high temperature (up to $175^{\circ}C$) and pressure conditions( up to 129 pasi) by precipitation from metal nitrates with aqueous potassium hydroxide. Various types of iron oxide powders were obtained at different conditions. The size and the shape of the particles can be controlled as afunction of starting solution pH. The average particles size of the synthesized iron oxide powders increased, the particle shapes of the powders became fibrous, and the crystalline phase of the powder changes from iron oxide to iron hydroxide with increasing solution pH. The effects of synthesis parameters are discussed.