• 한국재료학회지
• /
• 제10권2호
• /
• pp.111-116
• /
• 2000

니켈기 주조용 합금 738LC를 816$^{\circ}C$와 982$^{\circ}C$에서 크리프 파단 시험과 열간 노출시험을 통해 온도와 응력 변화에 따른 파단양상, 탄화물과 $\sigma$상의 석출 거동에 대해 조사하였다. 816$^{\circ}C$/440MPa에서는 크리프 파단양상이 전단변형에 의한 입내파괴를 나타내었으나, 982$^{\circ}C$/152MPa에서는 표면과 접하는 결정입계에서 입계산화에 의해 표면에너지의 감소로 균열이 나타나 진행되는 입계파괴가 나타났다. M(sub)23C(sub)6 탄화물이 816$^{\circ}C$에서는 주로 결정입계에서와 전단변형에 의한 입내균열을 따라 석출하였으나, 982$^{\circ}C$에서는 결정입계 뿐만 아니라 입내에서는 석출하였으며 석출양은 증가하였다. $\sigma$상은 Cr(sub)23C(sub)6 탄화물에서 핵생성 후 기지로 성장하며, 온도가 높고 응력이 주어지면 Cr(sub)23C(sub)6 탄화물의 양이 증가하여 $\sigma$상의 석출도 많아졌다.

• Corrosion Science and Technology
• /
• 제11권4호
• /
• pp.141-150
• /
• 2012

Stress corrosion cracks in Alloy 600 compact tension specimens tested at $325^{\circ}C$ in a simulated primary water environment of pressurized water reactor were analyzed by analytical transmission electron microscopy and secondary ion mass spectroscopy (SIMS). From a fine-probe chemical analysis, oxygen was found on the grain boundary just ahead of the crack tip, and chromium oxides were precipitated on the crack tip and the grain boundary attacked by the oxygen diffusion, leaving a Cr/Fe depletion (or Ni enrichment) zone. The oxide layer inside the crack was revealed to consist of a double (inner and outer) layer. Chromium oxides existed in the inner layer, with NiO and (Ni,Cr) spinels in the outer layer. From the nano-SIMS analysis, oxygen was detected at the locations of intergranular chromium carbides ahead of the crack tip, which means that oxygen diffused into the grain boundary and oxidized the surfaces of the chromium carbides. The intergranular chromium carbide blunted the crack tip, thereby suppressing the crack propagation.

• Corrosion Science and Technology
• /
• 제2권2호
• /
• pp.59-67
• /
• 2003

Electrochemical potentiokinetic reactivation (EPR) tests are used to evaluate the degree of sensitization (DOS) of stainless steels and nickel base alloys. The validity of EPR test to detect DOS of these alloys, however, depends all the electrolyte composition employed. The existence of precipitates such as NbC, and TiC, etc. in the alloys also affects the reactivation behaviors of these alloys. In this investigation, the reactions involved during EPR processes are analyzed. In 0.5 M $H_2SO_4$+ 0.01 M KSCN electrolyte, a reactivation peak associated with the localized attack around NbC, different from that of intergranular corrosion, is observed for the solution annealed 347 SS. For solution annealed Alloy 600, matrix corrosion and localized attack around TiC with distinct anodic peaks appeared in the EPR curves are seen in the $H_2SO_4$+ KSCN electrolyte. With proper adjustment of elect rolyte composition, the contribution from intergranular corrosion, as a result of chromium carbide precipitation along the grain boundaries, can be distingui shed from the matrix and localized corrosion for the sensitized Alloy 600.

• 한국주조공학회지
• /
• 제40권2호
• /
• pp.16-24
• /
• 2020

The effect of a heat treatment on the microstructure and mechanical properties of Inconel 713C alloy vacuum investment castings were investigated. The microstructure of the as-cast state was observed, showing well-developed dendrite structures and distributed carbide particles and solidified massive precipitates in the grain or grain boundary during solidification, in this case the γ′ phase and MC particles. During a heat treatment, the γ phase matrix was reinforced by solid solution elements, carbide particles from the film morphology precipitated along the grain boundary, and many micro-precipitates of second γ′ phases 0.2 ㎛~2 ㎛ in size were newly formed in the γ phase matrix according to SEM-EDS analysis results. The tensile strength at a high temperature (850℃) decreased slightly becoming comparable with the room-temperature result, while the hardness value of the specimen after the vacuum heat treatment increased by approximately 19%, becoming similar to that of the as-cast condition. However, the impact values at room temperature and low temperature (-196℃) were approximated; this alloy was mostly not affected by an impact at a low temperature. In the observations of the fracture surface morphologies of the specimens after the tensile tests, the fractures at room temperature were a mix of brittle and ductile fractures, and an intergranular fracture in the inter-dendrite structure and some dimples in the matrix were observed, whereas the fractures at high temperatures were ductile fractures, with many dimples arising due to precipitation. It was found that a reinforced matrix and precipitates of carbide and the γ′ phase due to the heat treatment had significant effects, contributing greatly to the excellent mechanical properties.

• Corrosion Science and Technology
• /
• 제2권3호
• /
• pp.117-126
• /
• 2003

Due to excellent corrosion resistance and mechanical properties, austenitic stainless steel is widely used as the material for chemical plants. nuclear power plants, and food processing facilities. But, the zone affected by heat in the range of 400 to $800^{\circ}C$ during welding loses corrosion resistance and tensile strength since Cr-carbide precipitation like $Cr_{23}C_6$ forms at the grain boundary and thereby takes place the intergranular corrosion. In this study, AISI 304 stainless steel with the added Nb of 0.3 to 0.7 wt% was solutionized at $1050^{\circ}C$ and sensitized at $650^{\circ}C$. Specimen was welded by MIG. The phase and the microstructure of the specimens were examined by an optical microscope, a scanning electron microscope, and a x-ray diffractometer. The corrosion characteristics of specimens were tested by electrolytic etching and by double loop electrochemical potentiokinetic reactivation method(EPR) in the mixed solution of 0.5M $H_2SO_4$ + 0.01M KSCN. The melting zone had dendritic structure constituted of austenitic phase and $\delta$-ferrite phase. Cr carbide at the matrix did not appear, as Nb content increased. At the grain boundaries of the heat affected zone, the precipitates decreased and the twins appeared. The hardness increased, as Nb content increased. The hardness was highest in the order of the heat affected zone>melted zone>matrix. According to EPR curve, as the Nb content decreased, the reactivation current density(Ir) and the activation current density(la) were highest in the order of the melted zone

• 한국분말재료학회지
• /
• 제6권2호
• /
• pp.152-162
• /
• 1999

The present study is concerned with the effect of PM process variables on the microstructure by using atomized superalloy powders. It is suggested that the inhomogeneity of composition is strongly dependent on the process variables. The contents of segregation elements of plasma rotating electrode process (PREP) powders are larger than those of Ar atomization (AA) powders. As HIP treatment temperature in-increases, the secondary phases on the prior particle boundaries (PPB) have continuous,uniform distribution and high density, but the amount of PPB decreases suddenly at 1150$^{\circ}$C. Segregated phases on the PPB are identified to be MC type carbide. Brittle MC type carbides on the PPB provide fracture initiation sites and preferred fracture path, thereby leading to intergranular type brittle fracture.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.228-234
• /
• 1989

Pressureless-sintering of SiC with additions of yttria and alumina was studied. SiC could be densified to about 97% of its theoretical density at 185$0^{\circ}C$ which is about 20$0^{\circ}C$ below the normal sintering temperature of SiC with boron and carbon. Yttria and alumina formed intergranular liquid phases at the sintering temperature and promoted densification by the liquid phase sintering mechanism. The microstructure of sintered specimens was equiaxed and the liquid phase appeared to wet and dissolve SiC grains. The fracture toughness was measured by indentation method and found to be 5.3MPa.m1/2. Processing flaws near the surface of specimens appeared to be the major fracture origin during 3-point bending tests.

• 한국표면공학회지
• /
• 제30권2호
• /
• pp.144-154
• /
• 1997

Effects of plasma nitriding on the surface charcteristice of stainless steel(SS) were investjgated by utilizing wear tester, micro-hardness tester and potentiostat. The surface and corrosion morphology of plasma nitrided SS were analyzed by utilizing optical microscopy, SEM, XRD and WDX. It was found that plasma nitriding at $550^{\circ}C$, compared with $380^{\circ}C$, prodiced a good wear resistance and hardness as nitriding time increased, whereas Mo addition showd that were resistance and hardness decreased. Intergranular corrosion(IGC) resistance improved significantly in the case of plasma nirtrided SS containing 4.05wt% Mo at $380^{\circ}C$ because that nitrogen and Mo ast syner gidically to form a protective layer on surface which is responsible for the aggresive SCN-ion. Plasma nitrided at $550^{\circ}C$ decreased IGC as Mo content increased. Pitting improved in the plasma nitirided SS at Mo content incresased owing to retard a nucleation and growth of chromium carbide or nitirde in grain boundary.

• 분석과학
• /
• 제6권2호
• /
• pp.157-165
• /
• 1993

강 중 석출물을 추출분리한 후 이를 정량분석하는 것을 목적으로 개발된 정전위 전해법을 304 스테인레스 판재 및 선재 제조시에 발생한 결함 원인 분석에 활용하여 시료의 조직을 관찰하였으며, 결함 원인을 조사하였다. 스테인레스 선재 및 판재의 균열 전파 양상은 정전위 전해법을 이용하여 에칭한 후 주사전자현미경으로 관찰하였고, 입계를 따라서 존재하는 조대한 석출물은 EDS 및 EPMA를 이용하여 성분분석을 행하였다. 이들 조대한 석출물의 구조분석은 X-선 회절 패턴을 이용하여 행하였다. 판재 및 선재 두 경우 모두 균열은 입계를 따라서 전파하고 있었으며, 입계에는 $M_{23}(C,\;B)_6$ 이외에 조대한 $M_2C$ 석출물이 존재하는 것으로 확인되었다. 이들 석출물들의 분석에 정전위 전해에칭법을 이용함으로써 양호한 시료를 얻을 수 있었다.

• 열처리공학회지
• /
• 제23권6호
• /
• pp.338-343
• /
• 2010

Mechanical properties and microstructures of medium carbon high manganese steels were investigated in terms of alloying elements such as Mn, C contents, and heat treatment condition. Austenite volume fraction was increased with increasing Mn content, leading to hardness decrease in the range of Mn content of above 10% after quenching and tempering. Such results are also supported by microstructural analysis and X-ray diffraction in that the increase in mangaese content results in the increase in austenite fraction. Studies on tempering condition indicated that not only hardness and tensile strength but also charpy impact values were reduced as tempering temperature were raised in the range of $250^{\circ}C$ to $600^{\circ}C$. It was also observed that fracture mode was changed from dimple to intergranular fracture. Such results are thought to be due to very fine carbide precipitation or impurity segreagation at grain boundaries as tempering temperature goes up. Heat treatment of Fe-5Mn-2Si-1Al-0.4C can be optimized by austenitizing at $850^{\circ}C$, air cooling and tempering at $250^{\circ}C$, resulting in 1950 MPa in Tensile strength, 17% in elongation and 23.3 $J/cm^2$ in charpy impact energy with high work hardening characteristics.