• Korean Journal of Metals and Materials
• /
• v.48 no.10
• /
• pp.914-921
• /
• 2010

Studies were carried out to assess the microstructural and mechanical properties of ferriticmartensitic steel under a flowing sodium environment. HT9 (12Cr-MoVW) and Gr.92 (9Cr-MoVNbW) steel were exposed to liquid sodium at $650^{\circ}C$ containing dissolved oxygen of 20 ppm for 2333 hours and evaluations of the microstructure as well as the mechanical properties of the microhardness and nanoindentation were carried out. The result showed that both HT9 and Gr.92 exhibited macroscopic weight loss caused by general corrosion as well as localized types such as intergranular corrosion and pitting. Decarburization at the steel surface took place as the test proceeded. As the Cr content increased, dissolution and decarburization were suppressed. Assessment of the actual cladding geometry revealed that an aging process rather than decarburization governed the mechanical properties, which resulted in a decrease of the microhardness and yield stress.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.17 no.4
• /
• pp.16-24
• /
• 2013

The analysis of performance and internal flow according to various numerical models for interior ballistics has been conducted. The initial flow has been mainly affected by the drag model of propellants and their drag degradation reduces oscillations of differential pressure between the breech and the shot base. Models of Nusselt number haven't influenced the major performance of interior ballistics. The negative differential pressure isn't generated in the case without the heat transfer of propellants.

• Journal of Energy Engineering
• /
• v.23 no.2
• /
• pp.149-157
• /
• 2014

The steam generator tubes of nuclear power plants have various types of corrosion failures during the plant operation. The stress corrosion cracking which occurs on the outer surface of tube is called the secondary side stress corrosion cracking and mainly occurs in the expansion-transition area of tube. The causes are the concentration of impurities by the sludge pile-up related to the geometry of its region and the residual stress by tube expansion in the process of steam generator manufacturing. Especially the directionality and sizes of residual stresses are differed according to the tube expansion methods and the direction and the frequency of tube cracks depend on their characteristics. In bases on the plant experiences, it is notified that circumferential cracks of tubes expanded with explosive expansion method are dominantly occurred compared to those of tubes done with hydraulic expansion one. Therefore in this study, according to tube expansion methods frequencies and sizes of tube cracks with specific direction are compared by means of accelerated immersion test and also the crack morphology and the specific chemicals from water-chemistry environment are observed through the fracture surface examination.

• Journal of the Korean Society of Safety
• /
• v.14 no.1
• /
• pp.208-215
• /
• 1999

The creep behavior of a rapidly solidified and consolidated Al-9.45wt%Fe-4.45wt%Cr alloy were investigated in the stress range 40 to 115 MPa and temperature range 300(0.53Tm) to 441$^{\circ}C$(0.66Tm). It is of use to available aerospace and automobile industries for the improved performance of materials used at high temperature. Because Al alloys with improved creep resistance offer the potential for lower weight and reduced costs in aerospace and automobile components (e.g., structural members and engine parts) through the replacement of heavier and more costly materials, the safety in use at high temperature is good. The alloy is characterized by high stress exponents and activation energies for creep, which are greatly dependent on the stress and temperature. Because the creep stress is seen to cause a strongly significant enhancement of coarsening, the coarsening rate of the dispersed particles in all crept specimens is faster than that in isothermally annealed specimens. Dislocations connecting dispersoids are observed more cofrequently in crept specimens with higher stress and lower temperature. The creep strain rates in the power law creep regime were found to be predicted much better by the Shorty and Rosler/Arzt equation with the inclusion of a threshold stress and dislocation detachment mechanism. The dispersoids in this alloy were acting a source of void nucleation that finally leaded to ductile fracture within the grain so called intergranular. Each void was initiated, grown and failed at the dispersoids in the aluminium matrix. Grain boundary accommodation of the slip produced, which result in initiation of the void and then final transgranular fracture. Therefore, it was confirmed that these dispersoids played an important role in the fracture mechanism by the formation of $Al_{13}Fe_4$, $Al_{13}Cr_2$ and $Al_2O_3$.

• Journal of Korea Foundry Society
• /
• v.38 no.2
• /
• pp.48-54
• /
• 2018

To improve the durability of the turbocharger, it is important to suppress cracking of the turbine housing; therefore, we investigated the initiation and growth of these cracks. First, we initiated a crack in the turbine housing using endurance experiments. After the endurance test, cracks mainly occurred in the valve seat, the nozzle area, and the scroll part of the turbine housing. The results of a fracture analysis of the cracks showed that cracks in the valve seat were initiated by fatigue fracture. This seems to be caused by the accumulation of mechanical and thermal stresses due to vibration of the turbine wheel and high-temperature exhaust gas. Also, cracks in nozzle and scroll area were initiated by intergranular corrosion due to the exhaust gas. Thus, although there are differences in the cause of initiation according to the site, a concentric waveform was observed in all fracture planes. This phenomenon indicates that cracks gradually grow due to repeated stress changes, and the main causes are the temperature difference of the exhaust gas and the vibration caused by the turbine shaft.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.4
• /
• pp.423-428
• /
• 2016

The last stage blades of a low pressure (LP) turbine get frequently fractured because of stress corrosion cracking. This is because they operate in a severe corrosive environment that is caused by the impurities dissolved in condensed steam and high stress due to high speed rotation. To improve the reliability of the blades under severe conditions, 12% Cr martensitic stainless steel, having excellent corrosion resistance and higher strength, is widely used as the blade material. This paper shows the result of root cause analysis on a blade which got fractured suddenly during normal operation. Testing of mechanical properties and microstructure examination were performed on the fractured blade and on a blade in sound condition. The results of testing of mechanical properties of the fractured blade showed that the hardness were higher but impact energy were lower, and were not meeting the criteria as per the material certificate specification. This result showed that the fractured blade became embrittled. The branch-type crack was found to have propagated through the grain boundary and components of chloride and sulfur were detected on the fractured surface. Based on these results, the root cause of fracture was confirmed to be stress corrosion cracking.

• Korean Journal of Materials Research
• /
• v.2 no.4
• /
• pp.270-278
• /
• 1992

The effect of Ni-rich phase on the stress-rupture properties of Ni mlcroalloyed W were studied using direct load creep tester at 100$0^{\circ}C$, 110$0^{\circ}C$, and 120$0^{\circ}C$ in $H_2.$ The stress rupture strength of 100hrs. of W-0.4wt% Ni was 43% higher at 100$0^{\circ}C$ and 35% higher at 110 $0^{\circ}C$than that of W-0.2wt% Ni due to the larger initial grain size, the higher relative density and the higher grain growth during test. That of W-0.8wt% Ni was 90% higher at 100$0^{\circ}C$ and 60% higher at 110$0^{\circ}C$ than that of W-0.2wt% Ni. The activation energy of W-0.4wt% Ni for creep was 81.3 Kcal/mole. It was considered that creep deformation was controlled by the diffusion of W in the Ni rich phase between the grains and the deformation of grains. All of the specimens showed intergranular fracture by grain boundary cavitation and growth of cavity throughout the entire spcimen cross-section.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.16 no.3
• /
• pp.174-183
• /
• 1996

Acoustic emission(AE) response during stress corrosion cracking(SCC) of Inconel 600 alloy has been monitored to study the AE detectability of crack generation and growth by comparing the crack behavior with AE parameters processed, and to evaluate the applicability as a nondestructive evaluation(AE) by measuring the minimum crack size detectable with AE. Variously heat-treated specimens were tensioned by constant extension rate test(CERT) in various extension rate to give rise to the different SCC behavior of specimens. The AE amplitude level generated from intergranular stress-corrosion cracking(IGSCC) is higher than those from ductile fracture and mechanical deformation, which means the AE amplitude can be a significant parameter for distinguishing the An source. AE can also provide the effective means to identify the transition from the small crack initiation and formation of dominant cracks to the dominant crack growth. Minimum crack size detectable with AE is supposed to be approximately 200 to $400{\mu}m$ in length and below $100{\mu}m$ in depth. The test results show that AE technique has a capability for detecting the early stage of IGSCC growth and the potential for practical application as a NDE.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.6.2-6.2
• /
• 2010

Stainless steel is widely known to have superior corrosion properties. However, in some harsh conditions it still suffers various kinds of corrosions such as galvanic corrosion, pitting corrosion, intergranular corrosion, chloride stress corrosion cracking, and etc. For the corrosion protection of stainless steel, the ceramic coatings such as protective silica film can be used. The sol-gel coating technique for the silica film has been extensively studied especially because of the cost effectiveness. It has been proved that silica can improve the oxidation and the acidic corrosion resistance of metal surface in a wide range of temperatures due to its high heat and chemical resistance. However, in the sol-gel coating process there used to engage a heat treatment at an elevated temperature like $500^{\circ}C{\sim}600^{\circ}C$ where cracks in the silica film would be formed because of the thermal expansion mismatch with the metal. The cracks and pores of the film would deteriorate the corrosion resistance. When the heat treatment temperature is reduced while keeping the adhesion and the density of the film, it could possibly give the enhanced corrosion resistance. In this respect, inorganic protective silica film was tried on the surface of stainless steel using a sol-gel chemical route where silica nanoparticles, tetraethoxysilane (TEOS) and methyltriethoxysilane (MTES) were used. Silica nanoparticles with different sizes were mixed and then the film was deposited on the stainless steel substrate. It was intended by mixing the small and the large particles at the same time a sufficient consolidation of the film is possible because of the high surface activity of the small nanoparticles and a modest silica film is obtained with a low temperature heat treatment at as low as $200^{\circ}C$. The prepared film showed enhanced adhesion when compared with a silica film without nanoparticle addition. The films also showed improved protect ability against corrosion.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.139-139
• /
• 2017

최근 환경오염 문제로 인한 연비 규제 강화 속도가 빨라지고 있으며 이에 따른 연비 향상 기술이 크게 대두 되고 있다. 연비 향상 기술 중 경량화 방안소재로 알루미늄(Al), 마그네슘(Mg) 등의 비철금속을 주로 사용하고 있으며, 이중 알루미늄은 다른 경량화 금속소재보다 우수한 경쟁력을 가지고 있다. 하지만 경제적인 측면에서 철 대비 비용적인 어려움을 가지고 있고 용접성이 떨어지기 때문에, 자동차 부품의 일부만 알루미늄 소재를 선택하여 사용하고 있는 실정이며 알루미늄의 높은 이온화 경향으로 인해 기존 자동차 철강 소재와 접촉 시 쉽게 부식되는 단점을 가지고 있다. 이러한 문제점을 해결하기 위해서는 알루미늄의 금속원소를 첨가하는 연구가 지속적으로 개발 되고 있다. 알루미늄 합금에서 마그네슘의 첨가는 좋은 용접성과 내식성, 강도를 향상시킨다. 하지만 3%이상의 마그네슘 첨가는 입계에 ${\beta}(Al_xMg_y)$석출상이 석출되게 되며, 입계에 연속적으로 형성된 ${\beta}(Al_xMg_y)$석출상은 응력 부식 균열 (Stress corrsion cracking)과 입계 부식(Intergranular corrosion)을 야기하는 결과를 가져온다고 알려져 있다. 이 문제를 해결하기 위해 Al 5000계열 합금의 Zn의 첨가를 통해 ${\tau}(Al_xMg_yZn_z)$을 입계에 석출시켜서 입계에 ${\beta}(Al_xMg_y)$상의 석출을 방지함으로써 내식성을 향상시키거나 Al 5000계열 합금의 열처리를 통해 ${\beta}(Al_xMg_y)$석출상을 고용시킴으로써 응력부식균열의 발생을 억제하는 연구도 있다. 하지만 열처리 후 Polarization test를 이용한 내식성 연구는 잘 안 알려져 있다. 따라서 이번 연구에서는 Al5000계열의 주조한 합금을 DSC분석을 통하여 ${\beta}(Al_xMg_y)$석출상의 고용 온도가 약 $470^{\circ}C$라는 것을 확인한 후, 실온에서 $100^{\circ}C/hr$으로 가열하고 조건에 따라 $450^{\circ}C$에서 3시간, 6시간, 12시간, 24시간, 30시간 항온 유지시킨 후 공냉을 진행하였다. 열처리를 마친 시편은 에폭시를 이용하여 마운팅 하였으며, 시편표면을 2000#까지 연마 후 증류수로 세척한 다음 질소를 이용하여 건조 후 분극 시험을 진행하였다. 3.5wt% NaCl 용액에서 분극 곡선을 통해 부식거동을 확인한 결과 24시간까지 시간이 증가 할수록 내식성이 우수해지는 것을 확인하였으며, 추가적으로 조직사진, SEM & EDS 분석과 XRD, TEM 분석을 통해 내식성은 입계에 존재하는 Mg의 조성이 감소하게 되면 내식성이 향상되는 것을 관찰하였다.