• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.617-622
• /
• 1992

In order to study on the effect of SiC whisker in flexural strength characterization of macro defect-free (MDF) cement composites, which composed of high alumina cement and polyvinyl alcohol, microstructural characterization of the composite specimens fabricated by the addition of SiC whiskers was investigated. Microproes are created around the SiC whisker, MDF cement didn't react with the SiC whisker. However, flexural strength of the composites have been improved. Fracture morphology of the composites, presents mainly intergranular type fracture passing around the unhydrated particles and siC whiskers, and partially transgranular type fracture. The main strengthening mechanisms of the MDF cement composites reinforced with SiC whiskers are characterized by crack deflection, microcracking, and bridging of cracks.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.1
• /
• pp.61-67
• /
• 2000

Gears are the most commonly used parts in automotive and industrial applications. One of most common modes of gear failures is tooth breakage, which is usually produced by the bending fatigue failure. It is important to manufacture the gears which can withstand the applied stresses in view of safety and economic requirement. This paper deals with bending fatigue strength for cold forged bevel gear. Especially, to compare fatigue characteristics for manufacturing processes difference, bending fatigue tests of bevel gears made by three different processes respectively. Results indicate that the fatigue strength of bevel gear is improved by cold forging process. Intergranular fracture is found on fatigue fracture surface, and dimples are observed on final fracture surface. The fatigue failure cannot be considered as a deterministic quantity, but must be characterized statistically. This study proposes a method to estimate bending fatigue lift of the bevel gear using the probability-load-life and Weibull analysis.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.719-727
• /
• 1989

By using commercial zirconia powder CeO2-ZrO2 ceramics containing 8~16mol% CeO2 was made by heat treatment at 1350~155$0^{\circ}C$ for 1~10hr. The minimum amount of CeO2 for obtaining complete tetragonal phase was 12mol%, and in the tetragonal phase region fracture toughness of Ce-TZP was decreased with increasing CeO2 content and the maximum value was obtained when 12mol% CeO2 was added. The bending strength goes through maximum at 14mol% CeO2. Fracture mode of Ce-TZP transformed from intergranular to transgranular fracture with increasing CeO2 content, so the morphology of fracture surface of 16mol% Ce-TZP was wholly transgranular and this tendency was independent on grain size. The crystal structure of the 12mol% Ce-TZP was monoclinic with fringes along the grain boundaries which are lying in the particular plane from the TEM observation. The chemical composition of the sintered body was homogeneous as a whole and some amorphism or air pocket was observed at the triple junction.

• Journal of Korea Foundry Society
• /
• v.9 no.1
• /
• pp.58-66
• /
• 1989

The effect of heat treating temperature and ${\alpha}$ phase In the ${\beta}$ phase matrix were investigated for ${\beta}-CuZnAl$ shape memory alloys by tension test, fatigue test, and shape memory effect test. After heat treatment at $677^{\circ}C$, $750^{\circ}C$, $800^{\circ}C$ and $850^{\circ}C$ for 10 min. respectively, static fracture stress(${\sigma}_f$), fatigue fracture stress(${\tau}_{max}$) at $10^6$ cycle, and elongation(${\epsilon}_f$) was $24.2kg/mm^2$, $17.21kg/mm^2$ and 11.8%, respectively. As heat treating temperature decreased, fracture surfaces of the specimens were changed from the intergranular to the transgranular fracture mode. Especially, the a phase precipitated in the ${\beta}$ phase matrix had an effect on crack propagation and the fracture surface was characterized by dimple-like pattern when crack propagated in transgranular cracking mode. Precipitation of the ${\alpha}$ phase in the ${\beta}$ phase matrix lowered the transformation temperature by $10^{\circ}C$, and about 2.5 vol.% ${\alpha}$ phase did not affect the shape memory effect examined by the bending test.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.11a
• /
• pp.705-706
• /
• 2008

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1062-1067
• /
• 2003

In this study, corrosion fatigue characteristics of CF8M and CF8A steel were investigated on the simulated PWR condition(Temp.:$316^{\circ}C$, Pres.: 15:MPa). To make the simulated PWR condition. the special test machine consisted of INSTRON, Autoclave, LOOP and Measurement system was developed. As ${\Delta}K$ is ranged from 11 to $20MPa{\sqrt{m}}$, Crack growth rate of PWR condition is faster than air condition. Above $20MPa{\sqrt{m}}$, the crack growth rate of PWR and air condition is similar. Corrosion fatigue characteristics regardless of the ferrite contents($10{\sim}25wt.%$) is not different. After the test, the fracture surface of specimens was examined. It was difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, the more particles covered fracture surface were peeled.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.195-200
• /
• 2003

Ni coated $Al_2O_3$ composite was successfully Prepared by the electroless deposition Process. The average size of Ni particles coated on the $Al_2O_3$ matrix powder was about 20 nm. It was hard to find any reaction compound as an impurity at interface between $Al_2O_3$ and Ni particles after sintering. The characterization of microstructure crystal structure and fracture behavior of the sintered body were investigated using XRD, TEM and Victors hardness tester, and compared with those of the sintered $Al_2O_3$ monolithic body. Many dislocations were observed in the Ni phase due to the difference of thermal expansion coefficient between $Al_2O_3$ and Ni phase, and no observed microcracks at their $Al_2O_3$ and Ni interface. In the $Al_2O_3$/Ni composite, the main fracture mode showed a mixed fracture with intergranular and transgranuluar type having some ,surface roughness. The fracture toughness was slightly increased due to the plastic deformation mechanism of Ni phase in the $Al_2O_3$/Ni composite.

• Korean Journal of Materials Research
• /
• v.2 no.4
• /
• pp.306-310
• /
• 1992

Effects of hafnium, boron and zirconium on the ductility of Ni$_3$(Al, Fe) intermetallic compounds were studied using tensile test and SIMS analysis. Ni$_3$(Al, Fe) alloy with 0.1 at.% Hf, 0.05 at.% B and 0.1 at.% Zr additions showed maximum elongations of about 30% at 300K, 10% at 300K and 14% at 473K, respectively. The fracture mode of the alloy without the additive was the mixture of intergranular and transgranular fractures, but the addition of Hf, Zr or B changed the fracture mode to transgranular only. SIMS analysis showed that the beneficial effects of Hf, Zr or B segregation on the grain boundary strength are consistent with the grain boundary cohesion theory.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.198-207
• /
• 1994

In order to find an optimal friction-welding condition for Ni-base ODS alloy (MA 754) produced by mechanical alloying, joint experiments were performed with various conditions of friction pressures (50~500 MPa), friction times (1~5 sec) and upset pressures (50~600 MPa). The optimal friction pressure and upset pressure must be above 400 MPa and 500 MPa, respectively, which are determined by tensile strengths and fracture features of as-welded joints. A maximum stress설h of 975 MPa could be obtained under these pressure conditions at friction time of 2 sec. Microstructural features of bonded interface by optical microscope and SEM revealed that the interface regions of all specimens are consisted with three distinct regions and defects such as voids, cracks and wavy interfaces exist in the joints produced under not-optimized conditions. EDS results showed that these defects include oxides composed with elements of Al, Y and Ti. The hardness on the bonded interface was higher than in the base metal region. Specimens fractured in bonded interface region had lower strength values compared to those fractured in base metal region. Surfaces of the former showed a typical intergranular fracture.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.228-234
• /
• 1989

Pressureless-sintering of SiC with additions of yttria and alumina was studied. SiC could be densified to about 97% of its theoretical density at 185$0^{\circ}C$ which is about 20$0^{\circ}C$ below the normal sintering temperature of SiC with boron and carbon. Yttria and alumina formed intergranular liquid phases at the sintering temperature and promoted densification by the liquid phase sintering mechanism. The microstructure of sintered specimens was equiaxed and the liquid phase appeared to wet and dissolve SiC grains. The fracture toughness was measured by indentation method and found to be 5.3MPa.m1/2. Processing flaws near the surface of specimens appeared to be the major fracture origin during 3-point bending tests.