• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.3
• /
• pp.139-144
• /
• 2004

Dynamic crack initiation in ductile steel is investigated by means of impact loaded 3 point bend(PB) specimens. Results from non-viscoplastic and viscoplastic materials are compared. Their materials are applied with various impact velocities and static strain rates. The specimen has the size 320${\times}$750 mm with a thickness of 10 mm. A modified 3PB specimen design with reduced width at the ends has been developed in order to avoid the initial compressive load of the crack tip and also to avoid the uncertain boundary conditions at the impact heads. Numerical simulations are made by using the FEM code ABAQUS. Therefore, their results are plotted by shapes of the von Mises plastic stress and equivalent plastic strain of the specimens applied by various impact velocities.

• Computers and Concrete
• /
• v.9 no.1
• /
• pp.51-61
• /
• 2012

According to the results of three-point bending tests of rubberized concrete and plain concrete, the parameters such as total fracture energy ($G_F$), initial fracture energy ($G_f$), and tensile strength ($f_t$) are obtained for concrete material. Using ABAQUS software and a bilinear softening fictitious crack model, the crack propagation process was simulated and compared to the experimental results. It is found that the increase of AE hit count has a similar trend with the increase of energy dissipation in FEM simulation. For two types of concretes, both experimental results and numerical simulation indicate that the rubberized concrete has a better fracture resistance.

• Proceedings of the KWS Conference
• /
• 1995.10a
• /
• pp.214-217
• /
• 1995

In order to investigate characteristics of surface fatigue crack propagation from a pit shaped surface defect which frequently exists near weld joints, SS400 steel with thickness of 12mm, which generally used for structure members, was submerged-arc welded with butt type and machined for both surface. The weld joints were devided into 5 regions, weld metal, boundary between heat affected zone (HAZ), HAZ, boundary between HAZ and base metal, and base metal. Specimens from each region were machined for a pit shaped initial surface defect with aspect ratio of 2. characteristics of surface fatigue crack por pagation from the defect under the same loading condition were compared and discussed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.311-314
• /
• 2005

This research aims to analyze of prestressed composite hollow-core slab and box type steel beam. The smeared crack model used in abaqus for the modeling of hollow core reinforced concrete, including cracking of the concrete, rebar and concrete interaction using the tension stiffening concept, and rebar yield. The structure modeled is a simply supported hollow core spancrete slab subjected spa-h beams and prestressed in one direction. The hollow core spancrete slab is subjected to four-point bending. The concrete-rebar interaction that occur as the concrete begins to crack are of major importance in determining the spancrete slab's response between its initial, deformation and its collapse. This smeared crack model used in analysis involved non-liner concrete analysis concept.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.205-210
• /
• 1998

The strength and dimension of recent constructed subway box structures are increased considerably. These increases are resulting in much initial cracks by hydration heat and thermal stress. According to previous studies, decrease of cement amount by using superplasticizer and L/H value is the best way to eliminate hydration heat and stress. The analyses using finite element model were performed. By the result of analysis, the use of superplasticizer and the decrease of the change of longitudinal placing length are proved to be more effective for elimination thermal cracks. By ACI Code, for longitudinal placing length 25 m, the amount of wall temperature reinforcement is always lack despite of concrete mix proportion. With analytical result and the inducing crack joint, the in-site test were performed and the analytical results proved to be effective. However, the inducing crack joint is not effective if it is a small size.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.155-160
• /
• 2001

This paper describes a probabilistic fracture mechanics (PFM) analysis based on Monte Carlo (MC) simulation. In the analysis of CANDU pressure tube, it is necessary to perform the PFM analyses based on statistical consideration of flaw generation time. A depth and an aspect ratio of initial semi-elliptical surface crack, a fracture toughness value, delayed hydride cracking (DHC) velocity, and flaw generation time are assumed to be probabilistic variables. In all the analyses, degradation of fracture toughness due to neutron irradiation is considered. Also, the failure criteria considered are plastic collapse, unstable fracture and crack penetration. For the crack growth by DHC, the failure probability was evaluated in due consideration of flaw generation time.

• Journal of Mechanical Science and Technology
• /
• v.17 no.2
• /
• pp.215-220
• /
• 2003

Trepan prevents the wear of the inside part of a bearing when the initial shaft rotates. It continuously contacts with the eccentric part of the shaft in rotation and is loaded repeatedly. Therefore, even if an early crack of a trepan part is small, the crack may progress by the repeated load. If the crack progresses, very small chips come out. This Is put in the rotor and prevents the rotation of the compressor, There can be leaks in a microgroove and extreme wear can occur due to lack of oil on the surface contact part. Therefore, this study was carried out to compare and investigate the trepan strength and deflection characteristics between trepan locations and dimension changes using the finite element method and search a motor bearing for a model with bigger stiffness of a trepan part and the same deflection.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.2
• /
• pp.129-135
• /
• 2003

The fatigue life of a structure can be enhanced by improving the mechanical and metallurgical aspects to strengthen the material around regions of high stress. Coldworking of holes in structures is one of the mechanical methods of strengthening material. The material for this research is A12024-T351 which is used for the primary member or aircraft. Specimens were tested under constant amplitude loading and residual stresses measured by X-ray diffraction technique. Fatigue crack initiation life was evaluated by a strain-life equation which was considered initial residual stress and residual stress relaxation exponent as a function of the strain amplitude. The predictions on fatigue crack initiation life were compared with experimental results. A wide range of discrepancies between them was found.

• Journal of the Korean Society for Precision Engineering
• /
• v.25 no.4
• /
• pp.86-92
• /
• 2008

This paper is to investigate the behavior of linear static structure stress, the fatigue and experimental shock fracture far engine base in the Auxiliary Power Unit to resolve its restricted electrical power problem. The shock fracture test was experimentally made under MIL standard criteria. The numerical results by finite element method had a good agreement with those from the shock test. The design data of predicting the fracture at the initial crack and the damage behavior of structure with shock and vibration load in the battle field can be obtained from shock test. In the functional shock test, the crack at the side parts of the engine base was found at peak acceleration of 40g.

• Journal of the Korean Society of Safety
• /
• v.25 no.6
• /
• pp.161-168
• /
• 2010

A series of fatigue tests have been performed on the non-load carrying fillet welded joints in order to quantitatively assess the fatigue characteristics due to the grindings and TIG(Tungsten Inert Gas) welding treatments. From the results of fatigue tests, it has been shown that the fatigue strengths at $2{\times}106$ load cycles were improved in the case of the grinding sand TIG welding treatments, and we could know that it is satisfying fatigue strength prescribed in fatigue design standard in general. Besides, from the results of fracture mechanics approaches, the geometric shape correction factors were the most dominant factors in the initial fatigue crack growth, but as the fatigue crack develops, the finite plate correction factor were became the most dominant factor, and the fatigue life on non-load carrying fillet welded joints could be relatively exactly estimated by using the relations between fatigue crack growth rate and stress intensity factor obtained from finite element analysis and existing proposed formulae.