• 한국표면공학회지
• /
• 제49권2호
• /
• pp.172-177
• /
• 2016

In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.217-219
• /
• 2005

In the conventional GMAW of 9% Ni steel, Inconel wire has been employed. The major problem of the Inconel GMAW is that arc stability and fluidity of weld pool is poor. Lack of fusion and convex weld bead is liable to occur in case of 9% Ni steel because of low melting point of Inconel wire. In this study the effect of shielding gases on the Inconel 625 GMA weldability was investigated.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1421-1425
• /
• 1996

Sintered Si3N4 and Inconel composed of Ni(58-63%) Cr(21-25%) Al(1-17%) Mn(<1%) fe(balance) were pressurelessly joined by using Ag-Cu-Ti brazing filler metal at 950℃ and 1200℃ under N2 gas atmosphere of 1atm and their interfacial structures were investigated. In case that the reaction temperature was low as 950℃ its interfacial structure was "Inconel metal/Ti-rich phase layer/brazing filler metal layer/Si3N4 " Ti used as reactive metal existed in between inconel steel and brazing metal and moved to the interface of between brazing filler metal nd Si3N4 according as reaction temperature increased up to 1200℃. The interfacial structure of inconel steel-Si3N4 reacted at 1200℃ was ' inconel metal/Ni-rich phase layer containing of Fe. Cr and Si/Cu-rich phase layer containing of Mn and Si/Si3N4 " Cr Mn, Ni and Fe diffused to the interface of between brazing filler metal and Si3N4 and reacted with Si3N4 The most reactive components of ingredients of inconel metal were Cr and Mn. On the other hand Ti added as reactive components to Ag-Cu eutectic segregated into Ni-rich phase layer,.

• 방사성폐기물학회지
• /
• 제18권4호
• /
• pp.481-496
• /
• 2020

After nuclear power plants are permanently shut down and decommissioned, the remaining irradiated metal components such as stainless steel, carbon steel, and Inconel can be used as neutron absorber. This study investigates the possibility of reusing these metal components as neutron absorber materials, that is burnable poison. The absorption cross section of the irradiated metals did not lose their chemical properties and performance even if they were irradiated over 40-50 years in the NPPs. To examine the absorption capability of the waste metals, the lattice calculations of WH 17×17 fuel assembly were analyzed. From the results, Inconel-718 significantly hold-down fuel assembly excess reactivity compared to stainless steel 304 and carbon steel because Inconel-718 contains a small amount of boron nuclide. From the results, a 20wt% impurity of boron in irradiated Inconel-718 enhances the excess reactivity suppression. The application of irradiated Inconel-718 as a burnable absorber for SMR core was investigated. The irradiated Inconel-718 impurity with 20wt% of boron content can maintain and suppress the whole core reactivity. We emphasize that the irradiated metal components can be used as burnable absorber materials to control the reactivity of commercial reactor power and small modular reactors.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.349-353
• /
• 2015

In this paper, arc thermal spray coating was conducted onto the SS400 steel using Inconel 625 wires in order to improve the durability of marine steel structures, and then investigated cavitation damage behavior of Inconel 625 coating layer in sea water. For the Inconel 625 coating layer, surface hardness appeared similar to that of existing high velocity oxy-fuel coating technology with 380~480 HV, but the porosity of about 6 % was larger relatively. During the cavitation experiment, pit damages were originated and grown at the rough surface and pore defect area of Inconel 625 coating layer. And, after the 72 hours of experimental time, weight loss of Inconel 625 coating layer exhibited gradually increasing tendency due to surface damage effect of the undercut.

• Journal of Welding and Joining
• /
• 제20권2호
• /
• pp.82-89
• /
• 2002

In order to clarify hot cracking phenomena occurred in Inconel 690 welds and it's prevention, in this study, the cracking behavior and the influence of welding variables on cracking in Inconel 690 overlay welds on Mn-Ni-Cr-Mo steel(SA 508 cl.3) for pressure vessel were investigated by using mock-up test. The main results are as follows: The cracks in Inconel 690 overlay welds were mainly generated near the start and the end part of welding beads adjacent to STS 309L welded outside of Inconel 690 welds. Most of the cracks showed typical solidification crack, and also it was assumed that there was possibility of liquation cracking in HAZ. The existence of Nb constituents or concentration of Nb was recognized on the fracture facets of the solidification cracks in the welds by SMAW. Therefore Nb was considered to be the main factor of the solidification cracking. As the weld heat input was more increased and the weld bead length was longer, the extent of cracking was more increased. Moreover the extent of cracking was considerably decreased by changing of welding sequence to the start and the end part of welds. Hot cracking in welds by GTAW was considerably decreased as compared with that of SMAW. And cracks were well generated in the Inconel 690 overlay welds adjacent to 575 309L welds. This means that the hot cracking susceptibility of Inconel 690 welds was largely varied by chemical components and/or compositions of filter metals, base metals and neighboring welds.

• Corrosion Science and Technology
• /
• 제20권5호
• /
• pp.281-288
• /
• 2021

Due to advancement of the industry, operation of a device in a harsh environment is increasing. Especially, the marine environment contains Cl^- ions which causes localized corrosion such as pitting and crevice corrosion of stainless steel and various metals. In this study, electrochemical corrosion behaviors of austenitic stainless steel (STS 316L) and nickel alloy (Inconel 600) with different seawater concentrations (fresh water, seawater, mixed water) were investigated. The STS 316L and Inconel 600 were etched in 10% oxalic acid and composed of an austenitic phase. Results of Tafel analysis in seawater showed that STS 316L and Inconel 600 presented the highest corrosion current densities of 7.75 × 10^-4 mA/cm² and 1.11 × 10^-4 mA/cm² and the most negative pitting potentials of 0.94 V and 1.06 V, respectively. The maximum damage depths and surface damage ratio by pitting corrosion increased with chloride concentration. The STS 316L had higher PREN than Inconel 600. However, the surface damage and weight loss of Inconel 600 were superior to STS 316L. It was difficult to compare the pitting resistance of STS 316L based on Fe and Inconel 600 based on Ni with PREN simply.

• 한국표면공학회지
• /
• 제28권3호
• /
• pp.133-141
• /
• 1995

The deposition characteristics of diamond films were investigated for three different substrates : Si, Inconel 600 and steel. Diamond films were prepared by microwave plasma CVD method using $CH_4$, $H_2$ and $O_2$ as reaction gases. The deposited films were analyzed with SEM, Raman spectroscopy and ellipsometer. For Si substrate, diamond films were successfully obtained for most of the deposition conditions used in this study. As the $CH_4$ flow rate decreased and the $O_2$ flow rate increased, the quality of the film was improved due to the reduced non-diamond phase in the film. For Inconel 600 substrate, the surface pretreatment with diamond powders was required to deposit a continuous diamond film. The films deposited at temperatures of $600^{\circ}C$ and $700^{\circ}C$ had mainly diamond phase, but they were peeled off locally due to the difference in the thermal expansion coefficient between the substrate and the deposited films. The films deposited at $500^{\circ}C$ and $850^{\circ}C$ had only the graphitic carbon phase. For steel substrate, all of the films deposited had only the graphitie carbon phase. We speculated that the formation of diamond nuclei on the steel substrate was inhibited due to the diffusion of carbon atoms into the steel substrate which has a large amount of carbon solubility.

• Nuclear Engineering and Technology
• /
• 제54권10호
• /
• pp.3778-3787
• /
• 2022

The stress-assisted oxidation behaviour of Inconel 52 M/316 austenitic stainless-steel (SS) dissimilar weld joints (DMWJ) in a simulated pressurised water reactor environment was investigated. A corrosion galvanic couple formed between the Inconel 52 M and 316 SS due to differences in their nonferrous metal content. The electric field from the corrosion couple attracted metal cations (e.g. Fe²⁺, Cr³⁺) to the Inconel 52 M that were deposited as FeCr₂O₄. An additional corrosion galvanic couple was generated due to variations in the plastic deformation of the DMWJ. The superposition of electric fields from the different couples resulted in ridge-like oxide depositions in the fusion zone.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.244-249
• /
• 2007

In several locations of the pressurized water reactors, dissimilar metal welds using inconel welding wires are used to join the low alloy steel nozzles to stainless steel pipes. To evaluate the integrity and design the dissimilar welds, tensile and fracture properties variations are needed. In this study, dissimilar metal welds composed of SA508 Gr.3 LAS, inconel 82/182 weld, and TP316 stainless steel were prepared by gas tungsten arc welding and shielded metal arc welding technique. Microstructures were observed using optical and electron microscopes. Different tensile and fracture properties were observed depending on the specimen sampling position at room temperature and $320^{\circ}C,$ and that was discussed based on the microstructure characteristics. It was found that the strength at the bottom of weld was greater than at the top of the weld. Also, from the test data using small punch specimen, more detailed tensile property variations were evaluated.