A Study on the Recycling Process of Nickel Recovery from Inconel 713C Scrap based on Hydrometallurgy (인코넬 713C 스크랩으로부터 니켈 자원 회수를 위한 습식제련 기반 재활용공정 연구)

  • Min-seuk Kim;Rina Kim;Kyeong-woo Chung;Jong-Gwan Ahn
    • Resources Recycling
    • /
    • v.33 no.4
    • /
    • pp.36-46
    • /
    • 2024
  • We investigated a hydrometallurgical process of nickel recovery from Inconel 713C scrap. The process proceeded with a series of i) comminution of pyrometallurgical treated scrap, ii) sulfuric acid leaching, iii) solvent extraction of unreacted acid, molybdenum, aluminum, and precipitation of chromium, iv) crystallization of nickel sulfate by vacuum evaporation, and v) nickel electrowinning. The nickel-aluminum intermetallic compound, Ni2Al3, was formed by the pyrometallurgical pretreatment readily grounded under 75 ㎛. Sulfuric acid leaching was done for 2 hours in 2 mol/L, 20 g/L solid/liquid ratio, and 80 ℃. It revealed that over 98 % of nickel and aluminum was dissolved, whereas 28 % of molybdenum was. A nickel sulfate solution with 2.34 g/L for the crystallization of nickel sulfate hydrate was prepared via solvent extraction and precipitation. Over 99 % of molybdenum and aluminum and 93 % of chromium was removed. Nickel metal with 99.9 % purity was obtained by electrowinning with the nickel sulfate monohydrate in the cell equipped with anion exchange membranes for catholyte pH control. The membrane did not work well, resulting in a low current efficiency of 73.3 %.

Effect of Oxygen Injection on Microstructure and Mechanical Properties of Ni-based Superalloy Recycled by AOD Process (AOD공정으로 재활용된 니켈합금의 산소주입량에 따른 조직과 기계적 성질 변화)

  • Lee, Duk-Hee;Woo, Kee-Do;Kang, Whang-Jin;Yoon, Jin-Ho
    • Resources Recycling
    • /
    • v.25 no.2
    • /
    • pp.10-16
    • /
    • 2016
  • In this study, the Ni base superalloy was recycled by Argon oxygen decarburization(AOD) process using an inconel 713C scrap. During AOD process, argon gas was continuously injected 1,000 sccm and oxygen gas was injected into 10, 20 and 30 minutes of 100, 250 and 500 sccm.. In early stage of oxygen injection, the oxygen dose increased with increasing Al, Cr, and Mo content and decreasing C content. And Al content was decreased by carburization with added elements in late stage Because of oxidation was occurred with Al, Cr etc. after the reaction of carbon has been finished. From the results, the ratio of ${\gamma}^{\prime}$ phase reduced due to decreasing of Al content for that reason Al is the main element to form the ${\gamma}^{\prime}$ phase. Also carbide reduced owing to decreasing of C content so the mechanical properties of the specimens excessively injected by excess $O_2$ gas were decreased.