• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.14 no.1
• /
• pp.5-14
• /
• 1977

"Electrical Properties of Barium Titanates with Addition Sb2O3." PTC BaTiO3 in low resistance at room temperature was prepatred. Al2O3, SiO2 and TiO2 were doped with a view to improving reproduction. Sb2O3 was doped as impurity in order to control of resistivity of the specimens. The relations between the amount of Sb3O3 and electrical properties wereinvestigated. Of the compositions studied, additions of 3.75mole% Al2O3, 1.25mole% SiO2, 2.25mole% TiO2 and 0.16~0.25wt% Sb2O3 to BaTiC3 was low resistivity in 14-300 ohm-cm.00 ohm-cm.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.57-62
• /
• 2013

We investigated the thermal and electrical properties of the $B_2O_3-ZnO-Bi_2O_3$ glass system as a sealing material in sheath heater modules. A composition with over 90 wt% $Bi_2O_3$ in the $B_2O_3-ZnO-Bi_2O_3$ system was glassified by controlling the cooling rate. The glass transition temperature and thermal expansion coefficient in bismate glass could be controlled by the minor ingredients of ZnO, $SiO_2$, $BaO_2$, and $K_2O$. The $B_2O_3-ZnO-Bi_2O_3$ glass system bonded well to metal, and bismate glass insulating properties were comparable to those of bismate glass $B_2O_3-ZnO-PbO$ glass system in a sheath heater module.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.550-553
• /
• 2001

Li$_2$O-P$_2$O$_{5}$-Bi$_2$O$_3$-V$_2$O$_{5}$ glass containing glass former, P$_2$O$_{5}$ and Bi$_2$O$_3$ was prepard by melting the glass batch in pt. erucible followed by quenching on the copper plate. We found that Li$_2$O-P$_2$O$_{5}$-Bi$_2$O$_3$-V$_2$O$_{5}$ g1ass-ceramics obtained from the crystallization of glass showed significantly higher capacity and longer cycle life tham LiV$_3$O$_{8}$ made from powder synthesis. In this paper, we described crystallization process and LiV$_3$O$_{8}$ crystal growth in glass matrix by increasing temperature. The electrochemical properties were strongly affected by LiV$_3$O$_{8}$ crystal growth in matrix.rowth in matrix.

• Journal of the Korean Ceramic Society
• /
• v.15 no.2
• /
• pp.66-71
• /
• 1978

The cobalt blue spinel stains (main composition; CoO:$Al_2O_3$=1 : 1) in CoO-NiO-$Al_2O_$3 and $CoO-Al_2O_3-Cr_2O_3$ system were prepared by the calcination of each component oxides to be adequate for the factory. The color development, the change of the lattice constnat of the spinel and its application to colored glazes were studied. The results were summarized as follows. 1) In CoO-Al_2O_3$ spinel, the excess addition of each component hardly made any variation in lattice constantand alumina-rich spinel specimens caused the brilliant blue color fade. 2) An increase of $Ni^{2+}$ in $CoO-NiO-Al_2O_3$ system, made the lattice constnat of the $CoO-Al_2O_3$ spinel smaller, and an increase of $Cr^{3+}$ in $CoO-Al_2O_3-Cr_2O_3$, larger. 3) Glazed stains under lead glaze were colored nearly same dark blue color fade.

• Journal of Environmental Science International
• /
• v.15 no.3
• /
• pp.193-201
• /
• 2006

Advanced oxidation processes involving $O_3/H_2O_2$ and $O_3/catalyst$ were used to compare the degradability and the effect of pH on the oxidation of 1,4-dioxane, Oxidation processes were carried out in a bubble column reactor under different pH. Initial hydrogen peroxide concentration was 3.52 mM in $O_3/H_2O_2$ process and 115 g/L (0.65 wt.%) of activated carbon impregnated with palladium was packed in $O_3/catalyst$ column. 1,4-dioxane concentration was reduced steadily with reaction time in $O_3/H_2O_2$ oxidation process, however, in case of $O_3/catalyst$ process, about $50{\sim}75%$ of 1,4-dioxane was degraded only in 5 minutes after reaction. Overall reaction efficiency of $O_3/catalyst$ was also higher than that of $O_3/H_2O_2$ process. TOC and $COD_{cr}$ were analyzed in order to examine the oxidation characteristics with $O_3/H_2O_2\;and\;O_3/catalyst$ process. The results of $COD_{cr}$ removal efficiency and ${\Delta}TOC/{\Delta}ThOC$ ratio in $O_3/catalyst$ process gave that this process could more proceed the oxidation reaction than $O_3/H_2O_2$ oxidation process. Therefore, it was considered that $O_3/catalyst$ advanced oxidation process could be used as a effective oxidation process for removing non-degradable toxic organic materials.

• Journal of the Korean Ceramic Society
• /
• v.31 no.2
• /
• pp.213-219
• /
• 1994

The formations of spinel and colors of ZnO-Fe2O3-TiO2-SnO2 system have been researched on the basis of ZnO-Fe2O3 system. Specimens were prepared by substituting Fe3+, with Ti4+ or Sn4+ when mole ratios between Fe3+ and Ti4+ or between Fe3+ and Sn4+ were 0.2 mole. The reflectance measurement and X-ray diffraction analysis of the formation of spinel and the colors of there specimens were carried out. ZnO-Fe2O3 system in which Fe2O3 was substituted with SnO2 and TiO2 was formed the spinel structure of 2ZnO.TiO2, 2ZnO.SnO2, ZnO.Fe2O3. The stable stains which were colored with yellow and brown could be manufactured.

• Korean Journal of Materials Research
• /
• v.26 no.2
• /
• pp.90-94
• /
• 2016

In this study, to increase the strength and enhance the sintering property of $Al_2O_3$, $Y_2O_3$ and $La_2O_3$ were added; the effects of these additions on the sintering characteristics of $Al_2O_3$ were observed. Adding 1% of $Y_2O_3$ to $Al_2O_3$ repressed the development of abnormal particles and reduced the grain boundary migration of $Al_2O_3$, curbing pores to capture particles; as such, the material showed a fine microstructure. But, when over 2% of $Y_2O_3$ was added, the sintering property was reduced because of abnormal particle grain growth and pore formation in particles. Adding 1% of $Y_2O_3$ and $La_2O_3$ to $Al_2O_3$ led to the development of abnormal particles and formed pores in the particles; when over 3% of $La_2O_3$ was added, the sintering property was reduced because the shape of the $Al_2O_3$ particles changed to angled plates.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.775-782
• /
• 1998

This experiment is third study concerning BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} (Ln=Sm, Nd, Pr, La..) system which is known to show a high dielectric constant and Q value in microwave dielectric materials. The process of cry-stallization and the microwave dielectric properties of the specimens sintered at 1220-140$0^{\circ}C$ for 2 hr was investigated in the BaO-(Na,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} as well as BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system. The single phase BaPr2Ti5O14 and Ba(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}Ti5O14 was finally formed from the Pr2Ti2O7 (Nd, Pr)2Ti2O7 as a secondary phase in the BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} and BaO-(Nd, {{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system respectively The dielectric constant of the specimens sint-ered at 1280~131$0^{\circ}C$ showed the maximum value as 105(BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system) and 88 (BaO-(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system) and the Q values of them showed higher value than 1800 which are due to the maximum den-sity. However the dielectric properties of the specimens sintered at higher temperature than 131$0^{\circ}C$ were reduced due to the increases of pore which were resulted from the sudden grain growth.

• Journal of the Korean Ceramic Society
• /
• v.21 no.3
• /
• pp.221-230
• /
• 1984

In this study an investigation was made to determine optimum ratio between $SO_3$, MgO and $K_2O$ that maximizes $C_2S$ formation in Clinkering reaction Using response surface analysis method. It was proved that 1) Residual $K_2O$ int he clinker should be converted to $K_2SO_4$ because $K_2SO_4$ has less effect on the burnability than $K_2O$, 2) Optimum ratio if $SO_3$/K2O is 1.5, 3) Optimun balance between $CaSO_4$ and MgO is to be adjusted to such a level that w/o SO3=0.7(w/o MgO-2).4) In case of lack of $K_2O$ free CaO was minimized when $K_2SO_4$=2.3w/o and MgO=1.5w/o but if remaining $K_2O$ was 2w/o free CaI was minimized in the level that $K_2SO_4$=2.3w/o and MgO =1.5 w/o but if remaining $K_2O$ was 2 w/o free CaO was minimized in the level that $K_2SO_4$=4.5w/o and MgO =3.0 w/o.