이온보조반응법으로 처리한 알루미나 코아의 인장결합강도에 관한 연구 (TENSILE BOND STRENGTH OF ALUNMINA CORE TREATED BY ION ASSISTED REACTION)

  • 김형섭;우이형;권긍록;최부병;최원국
    • 대한치과보철학회지
    • /
    • 제38권5호
    • /
    • pp.704-723
    • /
    • 2000
  • This study was undertaken to evaluate the tensile bond strength of In-Ceram alumina core treat-ed by ion assisted reaction(IAR). Ion assisted reaction is a prospective surface modification technique without damage by a keV low energy ion beam irradiation in reactive gas environments or reactive ion itself. 120 In-Ceram specimens were fabricated according to manufacturer's directions and divided into six groups by surface treatment methods of In-Ceram alumina core. SD group(control group): sandblasting SL group: sandblasting + silane treatment SC group: sandblasting + Siloc treatment IAR I group: sandblasting + Ion assisted reaction with argon ion and oxygen gas IAR II group: sandblasting + Ion assisted reaction with oxygen ion and oxygen gas IAR III group: sandblasting + Ion assisted reaction with oxygen ion only For measuring of tensile bond strength, pairs of specimens within a group were bonded with Panavia 21 resin cement using special device secured that the film thickness was $80{\mu}m$. The results of tensile strength were statistically analyzed with the SPSS release version 8.0 programs. Physical change like surface roughness of In-Ceram alumina core treated by ion assistad reaction was evaluated by Contact Angle Measurement, Scanning Electron Microscopy, Atomic Force Microscopy; chemical surface change was evaluated by X-ray Photoelectron Spectroscopy. The results as follows: 1. In tensile bond strength, there were no statistically significant differences with SC group, IAR groups and SL group except control group(P<0.05). 2. Contact angle measurement showed that wettability of In-Ceram alumina core was enhanced after IAR treatment. 3. SEM and AFM showed that surface roughness of In-Ceram alumina core was not changed after IAR treatment. 4. XPS showed that IAR treatment of In-Ceram alumina core was enabled to create a new functional layer. A keV IAR treatment of In-Ceram alumina core could enhanced tensile bond strength with resin cement. In the future, this ion assisted reaction may be used effectively in various dental materials as well as in In-Ceram to promote the bond strength to natural tooth structure.

  • PDF

압자압입법에 의한 치과용 도재의 파괴인성 평가 (AN EVALUATION OF FRACTURE TOUGHNESS OF DENTAL CERAMICS BY INDENTATION FRACTURE METHOD)

  • 안승근;이주형;배태성
    • 대한치과보철학회지
    • /
    • 제34권2호
    • /
    • pp.309-319
    • /
    • 1996
  • This study was performed to evaluate the fracture toughness of seven commercially available dental ceramics by indentation fracture method. All specimens were fabricated to the final dimensions of approximately 12mm in diameter 2mm in thickness. The characte-ristic indentation dimensions of Vickers or Knoop indentation were measured to calculate the fracture toughness values and Young’s moduli. The results obtained were summarized as follows; 1. Young’s modulus and Vickers hardness of Vita In-Ceram showed the maximum values of $154.4{\pm}49.2$ Gpa and $12.60{\pm}0.71$Gpa, respectively. Results of Scheff test exhibited the significant difference between Vita In-Ceram group and others(p<0.01). 2. Maximum fracture toughness of $2.562{\pm}0.37 MPam^{1/2}$ for Vita In-Ceram and the maxi-mum one of $0.908{\pm}0.132MPam^{1/2}$ for Vitadur-N were calculated. Results of Scheff test showed the significant difference between Vita In-Ceram group and Vita Hi-Ceram(p<0.05) : also between Vita In-Ceram or Vita Hi-Ceram and others(p<0.01). 3. The alumina-based core ceramics showed the aspect of Palmqvist crack for the indentation load of 49.0N, but others showed the median/lateral crack for the indentation load of 9.8N.

  • PDF

In-Ceram 코아의 표면처리 방법에 따른 레진시멘트와의 전단결합강도에 관한 연구 (THE INFLUENCE OF SURFACE TREATMENTS ON THE SHEAR BOND STRENGTH OF RESIN CEMENTS TO IN-CERAM CORE)

  • 윤정태;이선형;양재호
    • 대한치과보철학회지
    • /
    • 제38권2호
    • /
    • pp.129-146
    • /
    • 2000
  • An increasing demand for esthetic restorations has led to the development of new ceramic systems. In-Ceram, a glass-infiltrated alumina ceramic has three to few times greater flexural strength than other ceramic glass material. Because of its high strength, In-Ceram has been suggested as inlay, crown, laminate veneer and core material for resin bonded fixed partial dentures. This clinical application requires a stable resin bond to In-Ceram core. The purpose of this study was to evaluate the shear bond strength between In-Ceram core and resin cements according to various surface treatments and storage conditions. The surface of each In-Ceram core sample was subjected to one of the following treatments and then bonded to Panavia 21 or Variolink II resin cement. ; (1) sandblasting with $110{\mu}m$ aluminum oxide powder, (2) sandblasting and silanization, (3) sandblasting and Siloc treatment, (4) sandblasting and Targis link application. Each of eight bonding groups was tested in shear bond strengths after the following storage times and thermocycling. ; A) 24 hours storage in distilled water at $37^{\circ}C$, B) 5 weeks storage in distilled water at $37^{\circ}C$ C) 5 weeks storage in distilled water at $37^{\circ}C$ and thermocycled 2,000 thormocycling for every 10 days(totally 10,000 thermocycting) in $5^{\circ}C-55^{\circ}C$ bath. The bond failure modes were observed with scanning electron microscope(SEM). The results were as fellows : 1 The shear bond strengths of sandblasting group were significantly lesser than the other groups after 24 hours water storage. No significant difference of bonding strengths was found between storage time conditions(24 hours and 5 weeks). The shear bond strengths showed a tendency to decrease in Variolink II bonding groups and to increase in Panavia 21 bonding groups. 3. After thermocycling, the shear bond strengths of all groups were significantly decreased(p<0.01) and Targis link group exhibited significantly greater strengths than the other groups(p<0.05). 4. Panavia 21 bonding groups exhibited significantly greater bonding strengths in sandblasting group(p<0.01) and silane group(p<0.05) than Variolink II bonding groups. 5. In observation of bond failure modes, Targis link group showed cohesive failure in resin part and silane group and Siloc group showed complex failure and sandblasting group showed adhesive failure between In-Ceram and resin.

  • PDF

Zirconia ceramic의 표면처리 방법이 레진시멘트의 결합강도에 미치는 영향 (EFFECT OF SURFACE TREATMENTS OF ZIRCONIA CERAMIC ON THE BOND STRENGTH OF RESIN CEMENTS)

  • 김창훈;전영찬;정창모;임장섭
    • 대한치과보철학회지
    • /
    • 제42권4호
    • /
    • pp.386-396
    • /
    • 2004
  • Statement of problem: It is not clear how to make a stable bonding between zirconia ceramic and resin cement. And the study about surface treatment of zirconia ceramic or bonding resin cement are not enough. Purpose: To measure and compare the shear bond strength of some resin cements on zirconia ceramic after different surface treatments. Material and method: 48 ceramic discs were made of 3 ceramic materials, zirconia ceramics (Zi-Ceram), heat-pressed ceramics (IPS Empress 2) and slip cast alumina ceramics (In-Ceram). According to the surface treatments of ceramic specimens and resin cements, specimens were classified into 6 groups and each group was composed of 8 specimens. For the surface treatment of Zi-Ceram group (test group), sandblasting and diamond bur preparation were applied and Superbond C&B and Panavia F were bonded respectively. For IPS Empress 2 group (control group), Variolink II was bonded after sandblasting, acid etching, silanization and for In-Ceram ALUMINA group (control group), Panavia F was bonded after sandblasting. After storing specimens in distilled water for 24 hours, the shear bond strength was measured by the universal testing machine. Results and conclusion: 1. Zi-Ceram group with Superbond C&B cement showed higher bond strength than with Panavia F cement regardless to the surface treatments (p<0.05). 2. In Zi-Ceram group with Superbond C&B cement, sandblasting treatment group (12.1MPa) showed higher bond strength than diamond bur treatment group (7.7MPa) (p<0.05). In Zi-Ceram group with Panavia F cement, there were no significant differences in the bond strength according to the surface treatments (p>0.05). 3. Zi-Ceram group with sandblasting and Superbond C&B cement (12.1MPa) showed the highest bond strength. The bond strength of this group was not significantly different from In-Ceram ALUMINA group (10.4MPa) (p>0.05) and lower than IPS Empress 2 group (15.9MPa) (p<0.05).

Celay System을 이용한 In-Ceram Alumina 3 Unit Bridge제작법 (THE CONSTRUCTION METHOD OF IN-CERAM ALUMINA 3 UNIT BRIDGE USING CELAY SYSTEM)

  • 조병완
    • 대한심미치과학회지
    • /
    • 제5권1호
    • /
    • pp.34-43
    • /
    • 1996
  • In nowdays many dental CAD/CAM system were developed. Among those only Cerec and Celay were used globally as clinical application. Celay is a machinable ceramic system that is capable of milling inlays, onlays, and veneers from prefabricated industrial ceramic blocks(Vita Celay Blanks). The advatages of Celay are to simplify the manufactures and to save the processing time. For esthetics In-Ceram Alumina bridges were introduced into maxillary anterior restoration. They have a high strength, a high translucency and an excellent marginal adapation. But the laboratory processes are very difficult and complicated. So the construction of In-Ceram Alumina bridge combined with celay system was desgined. The patient is a 28 year old age male. The chief complain is missing of maxillary left central incisor. He wants to restore anterior bridge for esthetically. The Alumina bridge framework was constructed easily by celay system. Glass ilfiltration was occurred. After that, vitadura-${\alpha}$porcelain build up was occurred by conventional method. The translucency of In-Ceram Alumina 3 unit bridge revealed to be superior to that of porcelain fused to metal bridge. So we report it with clincal case and literature reviews.

  • PDF

CCD카메라를 이용한 수종 전부도재관의 변연적합도에 관한 연구 (A STUDY ON THE MARGINAL FIT OF ALL-CERAMIC CROWNS USING CCD CAMERA)

  • 문병화;양재호;이선형;정헌영
    • 대한치과보철학회지
    • /
    • 제36권2호
    • /
    • pp.273-292
    • /
    • 1998
  • The purpose of this study was to evaluate marginal fit of four all-ceramic crown systems 1) conventional In-Ceram, 2) copy-milled In-Ceram using Celay system, 3) IPS Empress, 4) OPC(Optimal Pressable Ceramic). All ceramic crowns were made on epoxy dies. The fabricated crowns were sandblasted, cleaned with ultrasonic cleansing, silanated, and cemented with Bistite composite resin cement. the selected marginal areas of the crowns were the labial, lingual, mesial, and distal surface. Each selected area of surface was $0.6{\times}1.6mm$ in dimension. The image of each marginal area was captured to computer files using DT-55 Frame Grabber and light microscope connected CCD camera. The marginal gaps were measured every $70{\mu}m$ using computer image analysis program. The results obtained were summarized as follows : 1. The marginal fit of four all-ceramic crowns were significantly different from each other(p<0.01), and mean marginal fit values obtained were $31.42{\pm}16.52{\mu}m$ in conventional In-Ceram, $55.45{\pm}27.90{\mu}m$ in copy-milled In-Ceram using Celay system, $44.36{\pm}24.59{\mu}m$ in IPS Empress, $47.21{\pm}20.42{\mu}m$ in OPC. 2. In the marginal fit of conventional In-Ceraw and copy-milled In-Ceram crowns using Celay system there was no significant difference between mesiodistal and buccolingual surface, but in the marginal fit of IPS Empress and OPC crowns, there was significant difference between mesiodistal and buccolingual surface(p<0.01). 3. The marginal fit of four kinds of all-ceramic crowns was clinically acceptable.

  • PDF

수종 지르코니아 세라믹의 굴곡강도에 관한 연구 (THE STUDY OF FLEXURAL STRENGTH OF VARIOUS ZIRCONIA CERAMICS)

  • 박재홍;황정원;신상완
    • 대한치과보철학회지
    • /
    • 제42권2호
    • /
    • pp.142-153
    • /
    • 2004
  • Statement of problem: Increasing demand of esthetic restorations made lots of kinds of ceramic materials. Among them, zirconia has been being focused by many dentists. But, mechanical properties of zirconia were still unclear. Purpose : The purposes of this study were to analyze the flexural strength of various zirconia ceramics which had been currently used for clinic i.e., In-Ceram Zirconia(Vita Zahnfabrik, Bad $S\"{a}ckingen$, Germany), Celay Zirconia(Vita Zahnfabrik, Bad $S\"{a}ckingen$, Germany) and CAD/CAM Zirconia (Adens Zi-Ceram. Seoul , Korea). Material and methods: The four point bending test(ASTM Cl161) was used to measure the flexural strength of a specimen before and after circular heat treatment and fatigue loading. Results : 1. The average value of flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia in dry condition were 806.5 MPa, 669.9 MPa, 605.6 MPa, respectively. There was a statistically significant difference in strength among the types (P<0.05). 2. After thermocycling, the average flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia were 791.2 MPa, 604.2 MPa, 605.4 MPa, respectively. CAD/CAM Zirconia showed statistically significant higher strength(P<0.05). The others showed no significant difference after thermocycling(P>0.05). 3. After fatigue loading in wet condition. the average flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia were 806.0 MPa, 674.9 MPa, 601.7 MPa, respectively. There was a significant difference in strength among the types(P<0.05). 4. There was no statistically significant difference in strength of the specimens according to experimental methods except for before and after thermocycling in Celay Zirconia(P>0.05). Conclusion: Besides high esthetic quality, zirconia had sufficiently high mechanical strength.