• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.11
• /
• pp.2828-2835
• /
• 2000

This paper presents the fatigue behavior of composite materials with impact-induced damage. The impact damage parameter is proposed to evaluate the effect of impact damage on fatigue life. Subsequently, a new model is developed to predict the fatigue life of impacted composite materials. Also, a stochastic model is proposed to describe the variation of fatigue life due to the material nonhomogeneity. For these models, the fatigue tests were performed on the unimpacted and impacted composite materials, The effect of impact damage on fatigue life can be characterized by the impact damage parameter. Additionally, the results by the present fatigue life prediction model agree will with experimental results regardless of applied impact energy. Also, the variation of fatigue life can be described by the present stochastic model and is reduced with applied impact energy.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.225-230
• /
• 2000

This paper presents the fatigue behavior of composite materials with impact-induced damage. The impact damage parameter is proposed to evaluate the effect of impact damage on fatigue life. Subsequently, a new model is developed to predict the fatigue life of impacted composite materials. Also, a stochastic model is proposed to describe the variation of fatigue life due to the material nonhomogeneity. For these models, the fatigue tests were performed on the unimpacted and impacted composite materials. The effect of impact damage on fatigue life can be characterized by the impact damage parameter. Additionally, the results by the present fatigue life prediction model agree well with experimental results regardless of applied impact energy. Also, the variation of fatigue life can be described by the present stochastic model and is reduced with applied impact energy.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.1025-1028
• /
• 2005

Generally, fiber-reinforced composites have the highest possibilities of impact damages with external object collisions. Also, resulting in fatigue fracture considering the continued impact load. For the reasons mentioned above, the accurate understanding of interactions between the impact of composites and the fatigue load will be essential to understand the safety level of material structures. Furthermore, the composite materials and structures, due to the geometrical effect, vary the life in connection with the impact-fatigue. Therefore, I have reached the point that a focus of this study will be to evaluate fatigue fracture characteristics by the impacts-fatigue load of fiber-reinforced composites. Thus, in this paper, I have tried to work on impacts-fatigue load causing aspects and impact characteristics through impact-fatigue test on HTV-5Hl Black 9250 material made- structure, along with to evaluate the expected lift of real structures, the FEM analysis was carried out.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.6
• /
• pp.38-45
• /
• 2010

Welding structures are designed to endure its expected life. The most important factors are life. Especially on welded structure, fatigue strength is critical. So this study performed a research on Box and T shape weldment specimen to examine the influence of welding type. In this experiment, the results indicate Box shape was available in more than T shape. Fatigue tests were performed to evaluate the fatigue strength of the both as-welded and statically pre-loaded specimens by 3 point bending load. Fatigue life can be improved by using Ultrasonic Impact Treatment(UIT) effect. Ultrasonic Impact Treatment(UIT) is excellent for eliminating the tensile residual stresses and generating compressive residual stresses which elevate fatigue strength of welded structures. Also, this shows that welding part has better fatigue life and welding was performed well. In this study, to evaluate the Ultrasonic Impact Treatment(UIT) effect, for welding structure, the experiment was conducted at various levels of stress range between 100MPa and 500MPa. From the test results, it was indicated that fatigue performance was improving by Ultrasonic Impact Treatment(UIT)

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.9
• /
• pp.3148-3154
• /
• 2010

This paper presents the probabilistic analysis for fatigue life of Glass/Epoxy laminates with impact-induced damage. For this, a series of impact tests were perfomed on the Glass/Epoxy laminates using instrumented impact testing machine. Then, tensile and fatigue tests carried out so as to generate post-impact residual strength and fatigue life. Two Parameter Weibull distribution was used to fit the residual strength and fatigue life data of Glass/Epoxy composite laminates. The residual strength was affected by impact energy and their variance decreased with increasing of impact energy. The fatigue life of impacted laminates was greatly reduced by impact energy and this trend depended on applied stress amplitude. Additionally, the variation of fatigue life was gradually decreased with the applied stress amplitude.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.7
• /
• pp.1089-1096
• /
• 2001

This paper presents the fatigue behavior of composite materials with impact-induced damage under 2 level block loading. For this purpose, the 2 level block loading fatigue tests were performed on the impacted composite laminate. The fatigue life of the laminate under the block loading is greatly influenced by the impact damage; the effect of impact damage can be characterized by the present impact damage parameter. Based on this parameter, the model is developed to predict the fatigue life under block loading and the results by this model agree well with experimental results regardless of applied impact energy. Also, stochastic model is established to describe the variation of cumulative damage behavior and fatigue life due to the material nonhomogeneity.

• Journal of Korea Foundry Society
• /
• v.36 no.6
• /
• pp.187-194
• /
• 2016

The effects of scrap content on the impact and fatigue properties were investigated in AC4A alloy. The impact absorbed energy of as-cast specimens were 3.61, 3.56, 3.47, and 3.08 Joules, respectively, when scrap contents of the specimens were 0, 20, 35, and 50%. And, the corresponding energy levels of the T6 heat-treated condition were 3.66, 3.48, 3.25, and 2.96 Joule. In the same way, the fatigue strength values of the as-cast specimens were 53.2, 52.0, 48.4, and 43.8MPa, respectively, and the corresponding fatigue strengths of the T6 heat-treatment specimens were 85.4, 75.7, 60.6, and 51.2 MPa. Impact absorbed energy and fatigue strength decreased as scrap content of the specimen increased. It is assumed that impact absorbed energy decreased owing to the presence of oxide films, which act as branches of 2nd cracks; fatigue strength also decreased with decreased deflection of the fatigue crack path as the scrap content of the specimens increased.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.6
• /
• pp.1836-1842
• /
• 1996

In this paper, static and fatigue bending strengths of CFRP(carbon fiber reinforced plastic laminates having impact damage(FOD) are evaluated. Composite laminates used for this experiment are CF/EPOXY and CF/PEEK orthotropy laminated plates, which have two-interfaces[${0^0}_4{90^0}_4}$]$_sym$. A steel ball launched by the air gun colides against CFRP laminates to generate impact damages. The damage growth during bending fatigue test is observed by the scanning acoustic microscope(SAM). When the impacted side is compressed, the residual fatigue bending strength of CF/PEEK specimen P is greater that that of CF/EPOXY SPECIMEN B. On the other hand, when the impacted side is in tension, the residual fatigue bending strength of CF/PEEK speicemen P is smaller than that of CF/EPOXY specimen B. In the case of impacted-side compression, fracture is proposed from the transverse crack generated near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-b delamination in the case of impacted-side tension.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.8 no.6
• /
• pp.247-258
• /
• 2000

It is thought that impact damages and hygrothermals can affect to CFRP (Carbon-fiber reinforced plastic) composite laminated due to the sensitivity on the composite laminated Therefore, this paper focuses on the fracture mechanisms experimentally based on a scanning acoustic microscope (SAM) when subjected to impact damages, i.e., foreign object damages(FOD), and also the influence of impact damages and hygrothermals on residual fatigue bending strength of CFRP laminates. Composite laminates used in the experiment are CF/EPOXY orthotropy laminated plates, which constist of two-interfaces [04/904]s. A steel ball launched by an air gun collides against CFRP laminates to generate impact damages. Bending fatigue tests are periodically interrupted for a nondestructive evaluation (NDE) measurement of the progrossive damages to built the fracture mechanism by impact damages, and three-point fatigue bending tests are carried out to investigate the influence of hygrothermals on the effect on the residual bending fatigue strength of CFRP laminates.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.4 no.4
• /
• pp.147-155
• /
• 1996

The purpose of present paper is to estimate the static and fatigue bending strengths of CFRP(carbon fiber reinforced plastic) laminates having impact damage(FOD). The specimens which are formed with the different stacking composition, EPOXY and PEEK matirx and orthotropic and quasi-isotropic laminated plates, are prepared for this experiment. A steel ball is impacted on CFRP laminates, generating impact damages, and the three-point fatigue bending test is carried out by using the impacted laminates to investigate the influence of the stackin composition on the fatigue strength of CFRP laminates.