High strength concrete is not only vulnerable to the occurrence of spalling which generates the loss of cross-section in concrete structures but produces faster degradation in its mechanical properties than normal strength concrete in the event of fire. This study aims to evaluate fire resistance of high strength segment concrete with PET fibers mixed to prevent spalling under ISO834 (2hr) and RABT fire curve. As results, the samples without PET fibers show the concrete loss up to the depth of about 8 cm and 9.5 cm from the surface exposed to fire under ISO834 and RABT fire curve respectively. The samples mixed with PET fiber of 0.1% show no spalling under ISO834 fire curve and the spalled thickness of 6.5 cm under RABT fire curve after the fire tests. Finally, the sample mixed with PET fiber of 0.2% shows no spalling under RABT fire curve. The results indicate that the suitable amounts of PET fiber for securing fire resistance performance of this high strength segment concrete are 0.1% under ISO834 fire curve and 0.2% under RABT fire curve. However, even though spalling does not occur, it is necessary to repair the deterioration of concrete up to 4 cm from the surface exposed to fire after fire.

• Journal of the Korean Society of Safety
• /
• v.25 no.4
• /
• pp.48-60
• /
• 2010

The fire resistance performance of 2 RC slabs after exposure to the ISO-834 fire standard without loading has been experimentally investigated. A Comparison is made of the fire resistance performance between RC slabs without PP(polypropylene) fibers and RC slabs with PP fibers. From the fire test results, the presence of PP fibers in RC slabs can reduce spalling and enhance their fire resistance. Until now, the determination of fire resistance of reinforced concrete(RC) slabs has essentially been based on tabulated data. According to ACI 216 code and EUROCODE 2, the design of concrete structures is essentially based on tabulated data for appropriate concrete cover and various fire durations. From the comparison between fire test results and codes, current fire design provisions of codes such as the ACI 216 and the EUROCODE 2 are unconservative for estimating mechanical properties of RC slabs at elevated temperatures.

• Steel and Composite Structures
• /
• v.38 no.2
• /
• pp.121-139
• /
• 2021

Ultra-high strength concrete (UHSC) encased steel columns are receiving growing interest in high-rise buildings owing to their economic and architectural advantages. However, UHSC encased steel columns are not covered by the modern fire safety design code. A total of 14 fire tests are conducted on UHSC (120 MPa) encased steel columns under constant axial loads and exposed to ISO-834 standard fire. The effect of load ratio, slenderness, stirrup spacing, cross-section size and concrete cover to core steel on the fire resistance and failure mode of the specimens are investigated. The applicability of the tabulated method in EC4 (EN 1994-1-2-2005) and regression formula in Chinese code (DBJ/T 15-81-2011) to fire resistance of UHSC encased steel columns are checked. Generally, the test results reveal that the vertical displacement-heating time curves can be divided into two phases, i.e. thermal expansion and shortening to failure. It is found that the fire resistance of column specimens increases with the increase of the cross-section size and concrete cover to core steel, but decreases with the increase of the load ratio and slenderness. The EC4 method overestimates the fire resistance up to 186% (220 min), while the Chinese code underestimates it down to 49%. The Chinese code has a better agreement than EC4 with the test results since the former considers the effect of the load ratio, slenderness, cross section size directly in its empirical formula. To estimate the fire resistance precisely can improve the economy of structural fire design of ultra-high strength concrete encased steel columns.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.48-50
• /
• 2013

In this study, Car fire for test using ISO 9705 10MW Large Scale Calorimeter. Especially, study on the underground parking for the fire resistance performance. The underground parking lot of the fire resistance regulations in according to with the standard heating curve in Korea. Because of this burning car through experiments to the propose a new heating curve.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.120-127
• /
• 2015

The purpose of this study is to improve the fire prevention performance using the fire venetian blind louver subjected to burning by fire flame. The investigation is based on testing 2 full scale specimens, which is $3m{\times}3m$ module, $850mm{\times}1,500mm$ open, and $900mm{\times}900mm{\times}175mm$ venetian blind louver. Two louver thickness (1.5 and 2.0mm) were adopted. The specimens were exposed to fire flame temperature levels of ISO834 at the lower surface of the fire venetian blind louver specimens with exposure duration of one hour in Korea Institute of Construction Technology (KICT). It was found from the test results that the values of distributed temperature, decreased for all specimens for protecting to fire flame by venetian blind louver. The results of tests were a good fire prevention performance between in initial to 6 mins. At 60 minutes around ISO 834 fire loading, the percentages of distributed temperature in 500mm and 800mm height ranged between 11 and 10% respectively, regardless of louver thickness. This study, therefore, will improve the fire venetian blind louver for fire protection and prevention performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.487-488
• /
• 2010

This is the experimental and analysis study on the thermal distribution, structural behavior and residual strength of high strength concrete members subjected to fire. The parameters are strength of concrete, cover thickness, loading state and exposure time to fire. The ISO 834 standard fire curve is used to test. The material and structural property of concrete at high temperature are proposed, also.

• Journal of Korean Society of Steel Construction
• /
• v.18 no.5
• /
• pp.643-654
• /
• 2006

Thispaper presents the results of an experimental investigation into the fire performances ofsimply supported iTECH composite beams using an ISO834 standard fire. There are very few independent studies on the fire resistance of composite steel and concrete structures of various designs. The iTECH composite beam system has been used in construction, but nothing is known about its influence in a fire. To evaluate the fire resistance performanceof the iTECH beam, a test was conducted for 4.7m-span-length iTECH beams under given conditions in a laboratory. The fire resistance performance of unprotected coatings of the iTECH beam has been examined, and a longer period of fire resistance was achieved by increasing the beam coating's section size and decreasing its load ratio. Coatings for the fire protection of iTECH beams reduce the rate of temperature rise of the beam in case of fire, and the required thickness of spray-on fire protection coatings can be determined by means of tests.

• Fire Science and Engineering
• /
• v.25 no.5
• /
• pp.47-53
• /
• 2011

Fire load in buildings greatly contribute to the time and scale of fire according to the type and quantity of the fire load. Because bookstores have a large quantity of fire load compared with other buildings which may lead to large scale fires, however, their heat release characteristics have been hardly investigated. In this study, to obtain the data applicable for the performance-based fire safety design of bookstores, the specimens representing stacked fire loads were heated in a furnace in compliance with the standard heating curve of ISO834-1:1999 to investigate their heat release characteristics. From the experiment result, the combustion velocity and heat release rate required for performancebased fire safety designs are obtained.

• Nuclear Engineering and Technology
• /
• v.45 no.2
• /
• pp.223-236
• /
• 2013

In the present study the behavior of fire and the residual strength of fire-ignited RC slabs are investigated by experimental tests and numerical simulations. The fire tests of RC slabs were carried out in a furnace using the ISO 834 standard fire. The load capacity of the cooled RC slabs that were not loaded during the fire tests was evaluated by additional 3 point bending tests. The influence of the proportion of PP (polypropylene) fibers in the RC slabs on the structural behavior of the RC slabs after the fire loading was investigated. The results of the fire tests showed that the maximum temperature of concrete with PP fiber was lower than that of concrete without PP fiber. As the concrete was heated, the ultimate compressive strength decreased and the ultimate strain increased. The load-deflection relations of RC slabs after fire loading were compared by using existing stress-strain-temperature models. The comparison between the numerical analysis and the experimental tests showed that some numerical analyses were reliable and therefore, can be applied to evaluate the ultimate load of RC slabs after fire loading. The ultimate load capacity after cooling down the RC slabs without PP fiber showed a considerable reduction from that of the RC slabs with PP fiber.

• Journal of the Korean Society of Safety
• /
• v.26 no.6
• /
• pp.31-44
• /
• 2011

This paper has presented a finite element analysis of structural behaviour of box culvert during and after fires. The fire tests were carried out in a furnace on RC slabs using the ISO 834 standard fire curve. The load capacity after cooling of the RC slab that was not loaded during the fire tests was evaluated by means of additional 3 points bending tests. In the past, stress-strain models of concrete under fire loading have been proposed by several researchers. Comparisons are made with the load-displacement relations of RC slabs after fire loading using the existing stress-strain models with temperature, such as Schneider, EUROCODE 2, Lie, Shi and Nan model. By comparing the load-displacement relations, Lie model was found to result in a maximum load about 2.0% higher than that of test. Based on the fire test results of RC slabs, this paper presents an extensive analytical study on the fire response of box culvert during and after fires.