• Journal of Korea Foundry Society
• /
• v.15 no.6
• /
• pp.566-573
• /
• 1995

In this study, the microstructural characteristics such as primary silicon, eutectic silicon, $SiC_p$ dispersion behavior, compound amount and Si solubility in $Al/SiC_p$ composite fabricated by the squeeze casting under various conditions were investigated systematically. As applied pressure(MPa) increases, cooling rate and compound amount are increased. In gravity casting, the cooling rate of hypereutectic composite is slower than of hypoeutectic composite by exothermic reaction of primary Si crystallization. But the cooling rate of hypereutectic composite is faster than that of hypoeutectic composite fabricated by same applied pressure, because amount of primary Si crystallization in hypereutectic composite was decreased, on the contrary, primary ${\alpha}-Al$ in hypoeutetic composite was increased due to increase of Si solubility in matrix by applied pressure. The crystalized primary silicon in hypereutectic composite fabricated by squeeze casting become more fine than that in non-pressure casting This is because mush zone became narrow due to increase of Si content of eutectic composition by pressure and time for growth of primary silicon got shorter according to applied pressure. It is turned out that eutectic temperature and liquidus are decreased by the increasing of squeeze pressure in all the composite due to thermal unstability of matrix owing to increasing of Si solubility in matrix by the increasing of applied pressure, as indicated in thermal anaiysis(DSC) results.

• Journal of Korea Foundry Society
• /
• v.27 no.5
• /
• pp.212-216
• /
• 2007

과공정 Al-15wt.%Si 합금의 주단조 공정의 적용을 위해 주조 예비성형체를 제작하는 과정에서 P와 Sr을 첨가하여 과공정 Al-Si 합금의 응고과정에서 발생하는 초정 Si과 공정 Si의 미세화 개량처리를 행하였다. 미세화 조직의 변화에 따른 기계적성질 및 단조성을 조사하였으며, 미세화제로 첨가된 0.075wt.% Sr과 0.1wt.% P의 첨가에서 가장 효과적인 미세한 조직을 얻을 수 있었고, 인장강도와 연신율은 이들 첨가원가의 증가에 따라 향상되는 결과를 보였으나 일정 이상의 첨가에서는 더 이상의 향상은 없었다. 단조성 평가를 위한 열간가공 재현실험에서는 $450^{\circ}C$에서 약60N/mm2의 하중이 필요함을 알 수 있었다. 열간단조 및 열처리 후의 인장강도와 연신율은 보다 많은 향상을 가져왔으며, 이는 압축가공에 의한 주조 예비성형체 내부에 잔존하던 주조결함의 제어와 열처리에 의한 조직의 개량 및 균질화 효과에 의한 것으로 판단된다.

• Transactions of Materials Processing
• /
• v.8 no.5
• /
• pp.491-497
• /
• 1999

The effect of partial squeeze on the quality of casting products in the vacuum die casting was investigated to make defect free casting products with excellent mechanical properties. The partial squeeze and vacuum die casting process was industrially implemented in making reaction shaft support which was made of a hypereutectic Al-15%Si alloy. To combine squeezing and vacuum effects, the plunger injection system was designed and attached on the chill vent type vacuum machinery system. The combination of vacuum effect before injection and partial squeezing effect after injection resulted in defect free die casting products. The uniform distribution of fine eutectic and proeutectic Si obtained from trial process also provided excellent mechanical properties.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.04a
• /
• pp.52-52
• /
• 2006

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.05a
• /
• pp.24-37
• /
• 1999

A comprehensive methodology to consolidate the hypereutectic Al-27Si-X alloy via spray forming was investigated in an attempt to judge the feasiblilty of this alloy in applying wear resistant components. Billets having desired shape and microstructures were fabricated using forming parameters obtained from numerical calculations. Prior to tube extrusion of the spray formed billets, effects of various extrusion conditions, such as extrusion ratio, die temperature, and die configuration, on microstructures of the billet were studied. Based on results obtained from the preliminary extrusion tests, the formed billets were then hot extruded into a tubular shape. Various material properties of the extruded billet were measured and compared with the other candidate materials for anti-wear applications.

• Journal of Korea Foundry Society
• /
• v.17 no.6
• /
• pp.585-591
• /
• 1997

Hyper-eutectic Al-17.5wt%Si alloy bars of 25 mm in diameter were produced by horizontal continuous casting process. Effect of both casting speed and primary Si refiner (AlCuP) on microstructure and mechanical properties of the alloy have been investigated. With increasing a weight fraction of AlCuP, the average primary Si size decreased down to $20 {\mu}m$. On the contrary, there was no notable changes of microstructure and primary Si size according to the casting speed in the experimental range of this study, indicating that the cooling rate should be increased to optimize and refine microstructure and primary Si size. The experimental results including hardness, tensile strength and wear resistance tests of the processed alloy bars showed a good possibility to develop the high performance wear resistant Al-Si alloy.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.541-549
• /
• 1998

Microstructural characteristics of hypereutectic Al-Si alloys during reheating at semi-solid temperature have been investigated. The size and morphology of primary Si particles in wedge-type mold-cast ingot has been compared with hot-rolled sheet and Si particulate reinforced Al composite. Effects of P and Sr addition on the morphological changes of primary Si particles have been also investigated. Observation of the solidification microstructures of the wedge-type mold-cast ingot at different cooling rates showed that alloying elements such as P and Sr affect the morphology of Si particles, especially in the area solidified at a slow cooling rate. Negligible change in the size of primary crystals was observed after reheating experiment, but ${\alpha}-halo$ formed around the Si particles and fine particles of Si precipitated in the surrounding area of the Si particles. In addition, there seemed to be no coarsening with increasing of holding time and the region of ${\alpha}-halo$ being decreased. Nucleation and recrystallization was accelerated with addition of alloying elements during hot rolling resulting in a decrease of primary Si particle size. In the case of extruded specimens, morphological change of primary Si particles was not observed after reheating. No ${\alpha}-halo$ formation was observed in Si reinforced Al composite because of the oxide film formed on the Si particles which acted as a diffusion barrier between substrate and the primary Si particles.

• Journal of Korea Foundry Society
• /
• v.15 no.3
• /
• pp.262-271
• /
• 1995

It is well known what is impossible to refine primary and eutectic Si simultaneously by addition of both Cu-P and Sr(or Na). Because of the formation of compound $Sr_3P_2(or Na_3P)$ in the melt, in the result, both effects disappear. In this study Al-Cu-P alloy that comprises AlP compounds inside is added in the melt with Sr simultaneously. As AlP compounds that act on nucleation sites of primary Si are not formed but added directly an the melt, it is difficult to form $Sr_3P_2$ by reaction with Sr. Therefore it is possible to refine primary and eutectic Si simultaneously in the general casting process by use of Al-Cu-P alloy and Sr.

• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.116-123
• /
• 1996

The equipment for the horizontal continuous casting was built to produce hyper-eutectic Al-Si bars with a small cross-section of 25mm in diameter. The manufacturing processes including withdrawal cycle and secondary cooling methods were modified to refine the primary and the eutectic Si. The longitudinal casting speeds varied over the ranges of 670-1100mm/min for pure Al, and 200-350mm/min for Al-17wt%Si alloy. Due to the difference of cooling rate in the mould, microstructural asymmetry between the lower and the upper part of bar was observed. Thus, manufacturing processes such as cooling and withdrawal method were optimally combinated to get the homogeneous cast structure. With the increase of casting speed, the primary Si size was refined down to $30{\mu}m$ near the surface, and $80{\mu}m$ in the center of the bar.

• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.965-971
• /
• 2001

The objective of this study is to investigate the characteristics - microstructure, hardness, adhesive strength and friction coefficient - of the coatings with aging - treatment after optimizing internal- plasma spraying parameters for Al-30wt%Si powder as a basic research to manufacture the cylinder block bore for Al engine composed of Al-30wt%Si alloy on Al alloy, The optimum internal-plasma spraying parameters of Al-30wt%Si alloy are summarized as follows: voltage: 37.5V, current: 160A, working distance: 25mm, gun traverse speed: 4.5mm/s, rotating speed: 518m/min. The primary Si particles grew aggressively with increasing heat-treating temperature. The hardness of the as-sprayed coating was about Hv=275 but this value was abruptly decreased with increasing heat-treating temperature. And average friction coefficient of the coating was below 0.08 after heat treatment for 48h at $175^{\circ}C$.