• Proceedings of the Korean Institute of Building Construction Conference
• /
• v.y2004m10
• /
• pp.33-38
• /
• 2004

This study was performed to know watertightness and reduction effect and crack occurred by hydration heat, restraint of multiplication of hydration heat, through mechanical test, strength test and crack control test using fluosilicate salt based inorganic compound made from by-product during phosphoric acid manufacturing process. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.5-2.0\%$ of adding ratio of fluosilicate salt based inorganic compound. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. Effect of crack reduction was evaluated by length, drying shrinkage as well as stress change of hardened concrete at unrestraint/restraint state and also elucidated crack pattern on the concrete surface. It is ascertained that characteristics of crack resistance and watertightness for concrete was improved by an adequate addition of fluosilicate salt based inorganic compound.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.05a
• /
• pp.57-60
• /
• 2008

This study investigated the results of insulation heat curing method using double layer bubble sheet in slab concrete and mass concrete in cold weather environment. First of all, when double bubble sheets are applied, it was shown that slab concrete was protected from early freezing by remaining between 6 and 15℃ even in case outside temperature drops -9℃ below zero until the 2nd day from piling, and in the case of mass concrete, with the maximum temperature difference between the center and surface less than 4℃, crack occurrence index was close to 2 and no hydration heat crack occurred by internal constraint. The insulation heat preservation curing method using the double bubble sheet applied in this field prevented early freezing owing to stable curing temperature management, deterring concrete strength development delay at low temperature, and obtained the needed strength. Also, it was proven that the method is highly effective and economic for cold weather concrete quality maintenance through curing cost reduction like construction period shortening and labor cost reduction, etc by reducing the process of temporary equipment installation and disassembling.

• Analytical Science and Technology
• /
• v.9 no.4
• /
• pp.406-410
• /
• 1996

The adsorption behaviors of transition metal ions on the poly(N,N'-bispalmitoyl-1, 12-diaza-3, 4;9,10-dibenzo-5,8-cyclopentadecane) has been determined by adsorption process in aqueous solution. The order of concentration factor(CF) and the amount of adsorption were Cu(II)

• Journal of the Korean Ceramic Society
• /
• v.51 no.2
• /
• pp.57-63
• /
• 2014

Bottom ash can be used as pelletizing seeds in unsintered artificial lightweight aggregates, so it can be called as 'cold-bonded aggregates'. In the present study, the mechanical and chemical characteristics of bottom ash aggregates cold-bonded with fly ash were investigated. The crushing strength and the water transfer characteristic of the aggregates, which may affect the strength gain of the concrete, were evaluated. Moreover, the degree of hydration and the hydration products of the aggregates were analyzed to verify the chemical stability of the aggregates. Compared to commercialized artificial lightweight aggregates manufactured by sintering process, cold-bonded fly/bottom ash aggregates had similar levels of water transfer characteristics, while having lower strengths. The calcium hydroxide in the aggregates was almost completely consumed after 28 days moist curing.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.25 no.5
• /
• pp.810-816
• /
• 1996

This study was conducted to measure the hydration characteristics at $20^{\circ}C$ and investigated the effect of water to rice ratio(v/w) on the texture properties of cooked rice of ten different varieties based on maturity. Water absorptions during soaking were completed between 30min and 35min at $20^{\circ}C$. The ranges of equilibrium moisture content were between 0.3247g $H_2O/g$ dry matter and 0.3577g H201g dry matter. During the cooking process, the water content of cooked rice increased 6~7% with increased the ratio of water to rice from 1.4 to 1.6(v/w). The hardness(H) of cooked rice decreased, while the stickiness(-H) and -H/H ratio increased with increased ratio of water to rice.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.119-122
• /
• 2009

As architectures have recently become high-risers and mega-structured, stable high strength products have been ensured. Accordingly, use of precast concrete accouplement has been increased in order to facilitate air compression and rationalize construction. Since not only external heating but a1so internal temperature rise caused by the accumulation of cement hydration heat in manufacturing process, precast concrete members with large cross-section used for high-rise mega-structure's columns and beams may exhibit different temperature history compared to the precast concrete members for wall and sub-floor with relatively small cross-sections. Therefore, this study aims to elucidate the characteristics of temperature history of mass concrete members cast with high-strength concrete fur precast concrete application. In this study, large cross-sectional precast concrete mock-up, unit cement quantity, and temperature histories in manufacturing precast concrete member under different curing condition were inclusively investigated.

• Structural Engineering and Mechanics
• /
• v.47 no.1
• /
• pp.1-25
• /
• 2013

A combined thermal and mechanical action in roller compacted concrete (RCC) dam analysis is carried out using a three-dimensional finite element method. In this work a numerical procedure for the simulation of construction process and service life of RCC dams is presented. It takes into account the more relevant features of the behavior of concrete such as hydration, ageing and creep. A viscoelastic model, including ageing effects and thermal dependent properties is adopted for the concrete. The different isothermal temperature influence on creep and elastic modulus is taken into account by the maturity concept, and the influence of the change of temperature on creep is considered by introducing a transient thermal creep term. Crack index is used to assess the risk of occurrence of crack either at short or long term. This study demonstrates that, the increase of the elastic modulus has been accelerated due to the high temperature of hydration at the initial stage, and consequently stresses are increased.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.167-168
• /
• 2022

Recently, starting with the permanent suspension of Gori 1 in Korea, the importance of the disposal of concrete structures in nuclear power plants has emerged, and environmental and safety are required to be proved accordingly. Safe radioactive waste disposal technology that immobilizes harmful radioactive elements, which are by-products of nuclear power, inside a solid matrix and recycling measures are needed to secure an efficient waste disposal space. This study was conducted to confirm whether recycled cement generated in the process of radioactive concrete treatment can be used as a solidifying material for radioactive waste treatment. In order to simulate the concrete exposed to radiation, aqueous solutions of Di-water, CsCl 1M, and CoCl₂ 1M were used as blending water at W/B 0.5. Tricalcium phosphate and Prussian blue were substituted with 5 wt.% based on the weight of recycled cement as a binder to improve solidification performance, and their hydration characteristic was analyzed.

• Journal of the Korean Ceramic Society
• /
• v.36 no.7
• /
• pp.725-733
• /
• 1999

It is a fundamental experiment to use blast-furnace slag in solidification/stabilization process. The compressive strength and leaching test of Pb and Cr doped samples were evaluated and the effects of heavy-metal ions on the hydration of slag was investigated. Sodium silicates(5wt%) was added as alkali-activator and the effects of replacing a part of slag with flyash or gypsum was also discussed. Pb ion was solidified by encapsulation of matrix. In of slag${\pm}$gypsum binder microstructure was densified by accelerating to form AFt/AFm phase and compressive strength was improved resulting in reducing leaching amount of Pb ion. Cr ion was solidified by substituting with Al ion in aluminate product. Slag+fly ash binder improved compressive strength and decreased leaching amount of Cr ion.

• Journal of Sensor Science and Technology
• /
• v.3 no.2
• /
• pp.74-80
• /
• 1994

Silicon direct bonding technology is very attractive for both silicon-on-insulator devices and sensor fabrication because of its thermal stress free structure and stability. The process of SDB includes hydration of silicon wafer and heat treatment in a wet oxidation furnace. After hydration process, hydroxyl groups of silicon wafer were analyzed by using Fourier transformation-infrared spectroscopy. In case of hydrophilic treatment using a ($H_{2}O_{2}\;:\;H_{2}SO_{4}$) solution, hydroxyl groups are observed in a broad band around the 3474 $cm^{-1}$ region. However, hydroxyl groups do not appear in case of diluted HF solution. The bonded wafer was etched by using tetramethylammonium hydroxide etchant. The surface of the self etch-stopped silicon dioxide is completely flat, so that it can be used as sensor applications such as pressure, flow and acceleration, etc..