• 방사선산업학회지
• /
• 제6권3호
• /
• pp.273-279
• /
• 2012

Silica hybrid silver nanoparticles showing the strong antimicrobial activity, in which nano-silver is bound to silica molecules, has been synthesized using ${\gamma}-irradiation$ at room temperature. The present study relates to an antimicrobial composition for coating fiber products comprising silica hybrid silver nanoparticles. In this study, we describe antimicrobial fiber products coated with the silica hybrid silver nanoparticles and a method of antimicrobially treating fiber products by coating the fiber products with the silica hybrid silver nanoparticles. The antimicrobial fiber products exhibited excellent antimicrobial effects. In detailed practice, when the present composition comprising nanosized silica-silver was applied to a cloth (fabric) in a concentration of $6.4mg\;yard^{-1}$, the viable cell number decreased to less than 10 cells before and after laundering, resulting in a reduction of 99.9% or greater in the viable cell number. The present composition displays long-lasting potent disinfecting effects on bacteria. Also, we investigated the toxicity of silica hybrid silver nanoparticles in rats. The skin of rats was treated with a 30 ppm nanoparticles solution ($2ml\;Kg^{-1}$) for 8 days. No toxicity was detected in the treatment. These results suggest that the fiber products coated with the silica hybrid silver nanoparticles can be used to inhibit the growth of various microorganisms.

• Journal of Welding and Joining
• /
• 제18권6호
• /
• pp.96-101
• /
• 2000

Sintered alumina ceramic substrate has been used for the insulating substrate for thick Hybrid IC owing to its cheapness and good insulating properties. Some of thick HIC's are important to eliminate the heat emitted from the parts that are mounted on the ceramic substrate. Sintered ceramic substrate can not transfer and emit the heat efficiently. It's been tried to do plasma spray coating of alumina ceramic on the metal substrates that have a good heat emission property. The most important properties to commercialize this ceramic coated metal substrate are surface roughness and deposition efficiency. In this study, plasma spray coating parameters are optimized to minimize the surface roughness and to maximize the deposition efficiency using Taguchi experimental method. By this optimization, the deposition efficiency was greatly improved from 35% at the frist time to 75% finally.

• 한국표면공학회지
• /
• 제42권2호
• /
• pp.73-78
• /
• 2009

Quinary Ti-Al-Si-C-N films were successfully synthesized on SUS 304 substrates and Si wafers by a hybrid coating system combining an arc ion plating technique and a DC reactive magnetron sputtering technique. In this work, the effect of Si content on the microstructure and mechanical properties of Ti-Al-C-N films were systematically investigated. It was revealed that the microstructure of Ti-Al-Si-C-N coatings changed from a columnar to a nano-composite by the Si addition. Due to the nanocomposite microstructure of Ti-Al-Si-C-N coatings, the microhardness of The Ti-Al-Si-C-N coatings significantly increased up to 56 GPa. In addition the average friction coefficients of Ti-Al-Si-C-N coatings were remarkably decreased with Si addition. Therefore, Ti-Al-Si-C-N coatings can be applicable as next-generation hard-coating materials due to their improved hybrid mechanical properties.

• 한국세라믹학회지
• /
• 제41권5호
• /
• pp.349-352
• /
• 2004

Organic-inorganic hybrid sol based on ZrO$_2$-SiO$_2$ system was prepared by sol-gel process. Firstly, ZrO$_2$ non-aqueous precursor sol was synthesized and then organosilane compounds which include epoxy silane (GPTS; 3-g1ycidoxypropyl tri-methoxysilane) and acryl silane (ACS; (3-(tri-methoxysilyl)propylmethacrylate)) were added to ZrO$_2$precursor sol for hybridization. Finally, com-mercial silica sol was added to improve the mechanical properties. Synthesized organic-inorganic Zr-hybrid sol was coated on polycarbonate substrate for enhancing it’s mechanical properties, especially hardness. Vicker’s hardness of polycarbonate sub strate was increased from 13.6 to 17.8 MPa and its pencil hardness was increased from 2 to 7 H, respectively, after coating and drying at 10$0^{\circ}C$ for 30 min.

• Elastomers and Composites
• /
• 제54권3호
• /
• pp.247-251
• /
• 2019

Two different urethane acrylates (mono-acrylate and di-acrylate) were used to prepare unsaturated polyester-based hybrid gel-coats. The physical properties and surface characteristics of these gel-coats were investigated on the basis of the content and type of urethane acrylate. The set-to-touch time increased and the physical properties (surface hardness and tensile strength) decreased with an increase in the urethane acrylate content. However, the type of urethane acrylate did not affect these parameters. It was found that the optimal urethane acrylate content for the application of unsaturated polyester-based hybrid gel-coats is ~10 wt%.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2013년도 임시총회 및 하계학술연구발표회
• /
• pp.79-80
• /
• 2013

• Korean Chemical Engineering Research
• /
• 제53권6호
• /
• pp.762-769
• /
• 2015

직경 2~3 nm 크기를 갖는 이산화티탄 나노입자가 산성 용액에서 titanium tetraisopropoxide(TTIP)의 가수분해 반응을 조절함에 의해 합성되었다. 생성된 이산화티탄 나노입자를 졸-겔법에 의해 3-glycidoxypropyl trimethoxysilane(GPTMS)과 반응시킴에 의해 유-무기 혼성 코팅 용액이 제조되었다. 그 후 코팅 용액을 기재인 polycarbonate(PC) 시트 위에 스핀 코팅시키고, $120^{\circ}C$에서 열경화 시켜 고굴절률 하드코팅 도막이 제조되었다. 코팅 도막은 가시광선 영역에서 90%의 높은 광학적 투과율을 보였으며 2H의 연필경도를 나타내었다. 또한 코팅 용액 내의 이산화티탄 나노입자의 함량이 4%에서 25%로 증가됨에 따라 코팅 필름의 굴절률은 633 nm 파장에서 1.502로부터 1.584로 향상되었다.

• 접착 및 계면
• /
• 제8권1호
• /
• pp.8-14
• /
• 2007

폴리우레탄에 아크릴기가 도입된 poly(urethane-methyl methacrylate) 혼성 에멀젼 코팅 수지는 플라스틱 코팅 수지로써 열적, 기계적 물성 및 내화학성을 제어할 수 있다. 이에 본 연구에서는 프리폴리머 혼합 공정과 무유화 중합 방법을 이용하여 수분산된 poly(urethane-methyl methacrylate) 혼성 에멀젼을 합성하였다. 즉, 폴리우레탄 프리폴리머 합성 단계에서 2,2-bis (hydroxymethyl) propionic acid (DMPA)을 투입하고 methyl methacrylate (MMA) 단량체를 투입한 후, triethylamine (TEA)을 이용하여 DMPA의 카르복실기를 중화시켜 친수성기를 도입하였다. 이를 수분산시켜 안정한 액적을 형성시킨 후, 사슬연장 및 무유화 중합 방법에 의해 합성반응을 진행하였다. 이때 제조공정 조건 및 아크릴계 단량체의 함량을 달리하여 poly(urethane-methyl methacrylate) 혼성 에멀젼의 다양한 샘플을 얻으며, 수분산 샘플의 물성(인장강도, 점도, 부착성 등) 및 코팅필름의 특성을 평가 비교하였다.

• 한국응용과학기술학회지
• /
• 제31권4호
• /
• pp.748-758
• /
• 2014

화장료의 UV 차단과 은폐효과를 갖는 이산화티탄을 사용하여 자기조직체 형성공법을 적용한 하이브리드 이산화티탄을 제조하고 형태, 성질, 공정의 최적조건과 자외선차단 개선을 확인하였다. 하이브리드 이산화티탄은 마이크로 이산화티탄(250~300nm)의 표면에 나노 이산화티탄(20~30nm)을 자기조직체 형성공법을 이용해 결합시킨, 이산화티탄 대 이산화티탄의 결합체를 말한다. 하이브리드 이산화티탄 제조의 최적조건을 알아내기 위해 (-)을 띄는 마이크로 이산화티탄의 표면에 양이온의 링크로써 $AlCl_3$ 를 농도별로 조정하고, 그에 따른 마이크로와 나노 이산화티탄의 투입비율을 달리하여 각각의 조건에서 만들어진 시료를 광학분석, 입도분석, 전위차분석 등을 이용해 확인하고 최적의 제조 조건을 알 수 있었다. 최적의 제조 조건에서 만들어진 하이브리드 이산화티탄의 자외선차단 상승효과를 확인하기 위하여 하이브리드 이산화티탄이 첨가된 화장료와 사용된 하이브리드 이산화티탄과 같은 비율의 마이크로와 나노 이산화티탄을 첨가한 화장료의 SPF in-vitro 를 측정하였고, 15%내지 30%의 자외선차단 상승 효과를 확인하였다.

• 공업화학
• /
• 제30권3호
• /
• pp.358-364
• /
• 2019

반사 방지(anti-reflective; AR) 코팅막의 광학 특성 및 내오염성을 향상하기 위하여 tetraethylorthosilicate (TEOS)/염기 및 methyltrimethoxysilane (MTMS)/산 혼성 용액의 혼합비를 변화시키며 다양한 AR 코팅막을 제조하였다. 제조된 AR 코팅막은 UV-Vis, 접촉각 측정기, AFM, FT-IR 및 연필 경도 시험을 통해 특성을 분석하였다. MTMS/산 용액의 함량이 10 wt%인 혼성 용액으로 제조한 AR 코팅막에서 유리 기판은 매우 우수한 광학 특성(97.2%의 투과율), 우수한 내오염성($121^{\circ}$의 물 접촉각 및 $90^{\circ}$의 $CH_2I_2$ 접촉각), 중간 정도의 기계적 강도(4 H의 연필 경도)를 나타내었다. 특히 우수한 내오염성은 기판의 표면 위에서 혼성 용액 내 소량의 MTMS/산 용액으로부터 유래된 메틸기($-CH_3$)의 고른 분산에 기인한 것으로 고려되었다. 연필 경도 시험 결과로부터, AR 코팅막의 기계적 강도는 MTMS/산 용액의 함량이 증가할수록 향상되는 것으로 나타났다.