• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.11
• /
• pp.978-983
• /
• 2008

An application of innovative laser+GMA hybrid welding process is presented for reducing bead humping defects in high speed welding and increasing side wall fusion in narrow groove welding without torch or wire oscillation. In this hybrid process, the laser heat input is applied adjacent to the weld pool at a relatively low power density to produce a wider, flatter weld bead. In bead on plate in sheet metal gauges, the hybrid process was able to produce hump-free welds from 70ipm (${\sim}1780mm/min$) to over 150ipm (${\sim}3810mm/min$) of the travel speed compared to the un-assisted GMAW process. A square-butt joint in 15mm A572 Gr50 steel welds was investigated. A square butt joint with a gap of 3.2mm was filled with 6 passes. Liquid Nitrogen calorimetry and innovative $CO_2$ laser reflective optics were also developed to demonstrate the concept of hybrid welding.

• Journal of Power System Engineering
• /
• v.15 no.5
• /
• pp.22-29
• /
• 2011

In this study, the damage mechanism of large scale steam turbine due to water induction was analyzed and recovery characteristics were reviewed. A turbine consists of the rotating rotor and the stationary casing, and the clearance between them is very small for the efficiency enhancement. If water induction, while relatively cold steam or water is introduced into turbine, occurs, the considerable humping is caused at the casing near the initial water induction point and that induces the rubbing between rotor and casing. Finally, it leads to the catastrophic failure. Bowed rotor has the different characteristics in the recovery depending on damage degree. The elastic deformation due to light rubbing is recovered by turning the rotor with 3 rpm under normal operation condition, but most plastic deformation due to rubbing deforms the local microstructure and that results in permanent deformation which could not be recovered under normal operation condition. Bowed rotor has diverse characteristics depending on the recovery method, and the method is empirical and needs the cutting edge technology. Careful recovery treatment of the rotor will eliminate the risks and secure the high quality rotor similar to new rotor. If any critical error is made during the recovery, the rotor would not be recovered permanently and it should be scrapped.

• The Journal of Korean Physical Therapy
• /
• v.16 no.1
• /
• pp.60-69
• /
• 2004

Many methods have been described for the early intervention of adolescent idiopathic scoliosis. Adolescent idiopathic scoliosis is lateral and rotational spinal curvature in absence of associated congenital or neurologic abnormalities, the most common type of scoliosis observed in child and young adults, and refers to curves that develop after the age of $10{\sim}18$. The curves of adolescent idiopathic scoliosis have the potential to progress rapidly during growth. Curves are currently universally measured by the Cobb's method and Ferguson method. Some curves do not remain small, these may be mildly or severely progressive and the ribs on the convex side of the curve separate, and those on the concave side ribs approximate so rib undergoes deformation with rib humping. The latter may make angles that can affect vestibular system, balance, sensory, especially cardipulmonary function. Intervention for adolescent idiopathic scoliosis is based on the patient's age, the angular value of the curve, the maturity of their skeleton, and the topography. The purpose of intervention for adolescent idiopathic scoliosis consists of knowing how to go to the best approach the correction of the lateral curve and rotational deformity holding the achieved for the remainder of spinal growth, preventing significant cosmetic abnormality, pain and cardiopulmonary complication, control the muscle imbalance and proprioceptive postural disturbances, be less need for radical surgery to avoid early surgery.

• Journal of Welding and Joining
• /
• v.30 no.4
• /
• pp.24-30
• /
• 2012

Laser welding by fiber laser accompanied by a lot of spatter and humping bead. This is because the deep and narrow keyhole usually form due to high beam quality. So the weld bead is formed defects, because the plasma jet with a high vapor pressure make the molten pool on keyhole wall scattered. For such a reason, unstable behavior of keyhole is difficult to monitor laser welding by using the laser induced plasma. Mostly, fiber laser welding of thick plates most be influenced by this effect. Therefore, fiber laser welding has been difficult to apply the sole. Thus, laser welding monitoring based on plasma measurements have much difficulty in measurements and analysis of signal. In this study, influence of the plasma emission signal according to welding speed and laser power in fiber laser welding analysed by using RMS and FFT analysis. We can verify that RMS value of the plasma emission signal changes with welding parameters in fiber laser welding, and aspect ratio greater than 1, the peak of FFT frequency had been moved in accordance with welding parameter.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.1
• /
• pp.109-115
• /
• 2004

The spatter and porosity could be occurred during$CO_2$CW laser welding of Primer- coated steel for shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate induced the spatter humping bead and porosity and these are main part of the welding defect. attributed to the powerful vaporizing pressure of primer attached on the base metal The zinc of Primer has a boiling point that is the lower temperature than melting point of steel zinc vapor will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position. the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Laser Solutions
• /
• v.18 no.1
• /
• pp.1-6
• /
• 2015

High welding speed and narrow weld seam are favorable for welding of magnesium alloy. Magnesium alloy is recommended for the smart frame because it has several advantages such as low density, high thermal conductivity, EMI shielding capability and good cast ability. This study is for the assembly welding of the magnesium smart frame with high productivity, good performance and low cost. The window for battery on AZ91D frame produced by die-casting was prepared by CNC machining. Corresponding AZ31 blank of 0.2mm thickness was prepared by die-blanking cut. All system set was fixed at the stationary bed but the laser beam was manipulated by scanner up-to 1,000mm/s speed. The weld joint between AZ31 sheet and AZ91D frame was welded by fiber laser on 850~1,000W output power. The joint showed penetration enough but some humping bead. The distortion by the weld heat was almost free because of the quick dissipation of the heat by small beam size and fast welding. Consequently, the thinner magnesium foil was assembled successfully to the magnesium frame of mobile phone.

• Laser Solutions
• /
• v.11 no.2
• /
• pp.8-14
• /
• 2008

Sintered specimen which used for a blade of diamond tool was manufactured in order to verify $CO_2$ laser weldability depend on sintered temperature. Five kind of specimen were prepared and the range of temperature is from $600^{\circ}C$ to $1000^{\circ}C$ at intervals of $100^{\circ}C$. As a result of the sintered density test, the porosity rate appeared in the range of $2.1%{\sim}21.4%$. After welding, the most segments had exceeds the minimum fracture stress (600MPa, The Standard Safety of Europe) at the welding strength test except on the sintered at $600^{\circ}C$. In case of the sintered at $700^{\circ}C$, even satisfied the safety allowable stress but cannot get the good quality for bead appearance because of humping defect. In the conclusion, we could know that it showed not only relatively soundness bead but also enough welding strength when the sintered blade of diamond tool is included less than 4% of porosity rate.

• Journal of Welding and Joining
• /
• v.23 no.3
• /
• pp.76-82
• /
• 2005

Recently the application of laser welding technology has been considered to shipbuilding structure. However, when this technology is applied to primer coated steel, good quality weld beads are not easily obtained. Because the primer-coated layer caused the spatter, humping bead and porosity which are main part of the welding defect attributed to the powerful vaporizing pressure of zinc. So we performed experiment with objectives of understanding spatter and porosity formation mechanism and producing sound weld beads in 6mmt primer coated steels by a $CO_2$ CW laser. The effects of welding parameters; defocused distance, welding speed, coated thickness and coated position; were investigated in the bead shape and penetration depth on bead and lap welding. Alternative idea was suggested to suspend the welding defect by giving a reasonable gap clearance for primer coated thickness. The zinc of primer has a boiling point that is lower than melting point of steel. Zinc vapor builds up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Significant effects of primer coated position was lap side rather than surface. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, formation and suspension mechanism of the welding defects was suggested by controling the factors.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.80-84
• /
• 2011

The weight reduction of the transportations has become an important technical subject Al and Al alloys, especially Al 5052 alloys have been being applied as door materials for automobile. One of the most widely known car weight-reduction methods is to use light and corrosion-resistant aluminum alloys. However, because of high electrical and thermal conductivity and a low melting point, it is difficult to obtain good weld quality when working with the aluminum alloys. Also, Pulse MIG welding is the typical aluminum welding process, but it is difficult to apply to the thin plate, because of melt-through and humping-bead. In order to enhance weld quality, welding parameters should be considered in optimizing the welding process. In this experiment, Al 5052 sheets were used as specimens, and these materials were welded by adopting new Cold Metal Transfer (CMT) pulse process. The proper welding conditions such as welding current, welding speed, torch angle $50^{\circ}$ and gap 0~1mm are determined by tensile test and bead shape. Through this study, range of welding current are confirmed from 100A to 120A. And, the range of welding speed is confirmed from 1.2m/min to 1.5m/min.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.12
• /
• pp.1055-1060
• /
• 2016

Laser welding is a high-density energy welding method. Hence, deep penetration and high welding speed can be realized with lower heat input as compared with conventional welding. The heat input of a CW laser welding is determined by laser power and welding speed. In this study, bead and lap welding of $0.5mm^t$ pure titanium was performed using a fiber laser. Its weldability with laser power and welding speed was evaluated. Penetration, bead width, joining length, and bead shape were investigated, and the mechanical properties were examined through tensile-shear strength tests. Welds with sound joining length were obtained when the laser power and welding speed were respectively 0.5 kW and 2.5 m/min, and 1.5 kW and 6 m/min, and the weld obtained at low output presented better ductility than that obtained at high output.