• Environmental Engineering Research
• /
• v.25 no.2
• /
• pp.171-177
• /
• 2020

Removal through adsorption is the most widely used and effective treatment method for volatile organic compounds (VOCs) in exhaust gases. However, at high temperatures and humidity, adsorption is competitive due to the presence of moisture and unsmooth physical adsorption thereby deteriorating adsorption performance. Therefore, water adsorption honeycomb (WAH) and VOCs adsorption honeycomb (VAH) were prepared to improve VOCs adsorption at high temperatures and humidity. Adsorbed toluene amounts on single honeycomb (SH), containing only VAH, and combined honeycomb (CH), containing WAH and VAH, were determined. Further, the toluene adsorption rates of honeycomb adsorbents mounted on rotary systems, VAH-single rotor (SR) and WAH/VAH-dual rotor (DR) were determined. Toluene adsorption by WAH/VAH-CH (inlet temperature: 40-50℃; absolute humidity: 28-83 gH₂O/kg-dry air) was 1.6 times that by VAH-SH, and the water adsorption efficiency of WAH/VAH-CH was 1.7 times that of VAH-SH. The adsorption/removal efficiency of the WAH/VAH-DR (inlet temperature: 45℃; absolute humidity: 37.5 gH₂O/kg-dry air) was 3% higher than that of VAH-SR. This indicates that the WAH at the rotor inlet selectively removed water, thereby improving the adsorption efficiency of the VAH at the outlet.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.663-669
• /
• 2009

The honeycomb adsorbent was prepared for adsorbing and seadsorbent was prepared by using zeolite sheet, which contained zeolite as component. The steady-state adsorption properties and surface morphologies were analyzed and breakthrough characteristics were ananlyzed by providing 16% carbon dioxide mixed gas. By thermal regeneration, carbon dioxide concentration properties were analyzed, and the adsorptive separation process was compared between thermal swing adsorption and pressure swing adsorption after adsorbent temperature change during heating. The breakthrough results of the honeycomb showed possibility parating carbon dioxide from combustion exhaust gas, which had deep impact on climate change, and the characteristics of the adsorbent were studied. Na-X zeolite was coated on a honeycomb prepared with ceramic sheet or active carbon sheet so that the two honycomb can be used at high temperature. Third honeycomb of rotary adsorptive concentration process.

• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1035-1041
• /
• 2002

The adhesion characteristics of adsorbent during impregnation of Y-type and ZSM-5type zeolites into ceramic paper were analyzed, as the amount of silica sol in slurry for impregnation was varied. 31 wt% of zeolite particle, which is useful for VOC adsorption, was evenly dispersed and adhered on ceramic paper and original crystal structure of the zeolite remained unchanged even after binder application and heat treatment. Surface area of the impregnated ceramic paper was decreased compared with that of zeolite powder. And it was found to be attributed to the reduction of volume of mesopore while the volume of micropore under $20{\AA}$ was unchanged. Zeolite-impregnated honeycomb cylinder, whose diameter and length were 10 cm and 40 cm, respectively, was subjected to adsorption/desorption test with respect to toluene, MEK, cyclohexanone. All of the VOC's were removed by adsorption with efficiency higher than 97% and from the static adsorption test, $42 Nm^3/h$ of 300 ppmv-VOC-laden air was calculated be treated continuously, when the honeycomb was used in an adsorptive rotor system.

• Applied Chemistry for Engineering
• /
• v.18 no.3
• /
• pp.273-278
• /
• 2007

The honeycomb adsorbents and adsorption process for carbon dioxide removal from fuel gas were investigated. Zeolite paper was made with Na-X zeolite powder and ceramic fiber as raw materials. $Li^+$, $Ca^{2+}$ or $K^+$ ion exchanges for Na-X zeolite and additional Na-X coating were performed on zeolite paper for increasing the carbon dioxide adsorption capacity, after that the adsorption characteristics of the samples were analyzed. Among the ion exchanged samples, $Li^+$ ion exchanged zeolite paper was most promising but its carbon dioxide adsorption capacity was less than expected for process application. However, additional Na-X coating was found to be an effective method for increasing the carbon dioxide adsorption capacity of the zeolite paper for process application. The carbon dioxide breakthrough test of the honeycomb adsorbent prepared with the zeolite paper was studied, and fuel gas treatment capacity was calculated when the honeycomb adsorbent was used in the rotary adsorption process.

• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1042-1047
• /
• 2002

The sedimentation characteristics of ceramic fiber were analyzed when viscosity of the slurry for ceramic paper formation was varied and zeta potential change and degree of dispersion with pH were studied as well. The proper viscosity of the slurry for dispersion of fibers was between 28 and 31 cps. Zeta potential of the slurry was sensitively changed with pH adjustment and showed maximum value of -35~-36 mV at ph 7.5~9.5, which indicated better dispersion of ceramic fiber as zeta potential of the slurry was increased. The sedimentation rate of ceramic fiber in a slurry was reported minimum at the maximum zeta potential. Water content of the casted paper should be lower than 83% after vacuum dehydration for retention of binder and lower than 62% after press rolling for wet paper handling. The obtained ceramic paper had tensile strength and basis weight, $102 kgf/cm^2$ and $98 g/m^2$, respectively.

• Clean Technology
• /
• v.24 no.4
• /
• pp.280-286
• /
• 2018

In this study, the adsorption performance of vapor phase VOCs under dry conditions was evaluated by using two metal oxides, $TiO_2$ powder and $Al_2O_3$ powder. BET analysis and ammonia in-situ FT-IR analysis were used to analyze specific surface area and surface acid site. As a result, $TiO_2$ powder and $Al_2O_3$ powder had a specific surface area of $317.6m^2\;g^{-1}$ and $64m^2\;g^{-1}$, respectively. In the case of $TiO_2$ powder, many acid sites were observed on the surface. As a result of evaluating the vapor phase VOCs adsorption performance using two metal oxide powders, $TiO_2$ powder having a relatively large specific surface area and a large number of acid sites exhibited relatively good adsorption performance. In particular, it is considered that the specific surface area directly affects the adsorption performance, and further study on the effect of the acid site is required. Based on the $TiO_2$ exhibited excellent adsorption performance, it manufactured into various forms of honeycomb, hollow fiber and disc. As a result, the adsorption performance was lower than that of the powder, but it is advantageous in view of applicability. In addition, it was confirmed that the disc adsorbent having excellent thermal durability due to the characteristics of the manufacturing process stably maintains adsorption performance even at a high temperature desorption process several times.