• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.266-272
• /
• 2002

This study reviews the factors controlling the weld metal cracking and shows the difference from those of HAZ cracking. It further reviews the recent progresses made in consumable design for improving the crack resistance in the high strength weld metal. Previously the controlling factors for weld metal cracking were regarded as weld metal strength, diffusible hydrogen and weld metal height. However an overall review presented in this article shows that the cold crack resistance can be improve significantly through the microstructural control and that an increase in tensile strength is not necessarily related to a decrease in the resistance to cold cracking.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.181-186
• /
• 2001

JLF-1 steel (Fe-9Cr-2W-V-Ta), low activation ferritic steel, is one of the promising candidate materials fer fusion reactor applications. High temperature fatigue life and tensile strength of JLF-1 steel and its TIG welded joints were investigated at the room temperature and $400^{\circ}C$. The strength of base metal (JLF-1) is in between those of weld metal and the HAZ. When the test temperature was increased from room temperature to $400^{\circ}C$, both strength and ductility decreased for base metal, weld metal and the HAZ. The longitudinal specimens of base metal showed similar strength and ductility compared with those of the transverse specimens at room temperature and $400^{\circ}C$. Little anisotropy was observed in the JLF-1 steel base metal in terms of rolling direction. Fatigue limit of weld metal which was obtained from cross-weld specimen is 495MPa. Thus, the weld metal showed the higher fatigue limit than those of base metal at both room temperature and $400^{\circ}C$. Little anisotropy of fatigue properties was observed for JLF-1 base metal in terms of rolling direction. When the test temperature was increased from room temperature to $400^{\circ}C$, the fatigue limit of both base metal and weld metal decreased substantially.

• Journal of Ocean Engineering and Technology
• /
• v.26 no.2
• /
• pp.33-38
• /
• 2012

The effects of the diffusible hydrogen content and hardness on the cold cracking in high strength weld metal were investigated. The diffusible hydrogen contents were influenced by welding parameters such as the voltage and contact tip-to-work distance (CTWD). The diffusible hydrogen content increased with an increase in voltage. However, it was decreased with an increase in CTWD. CTWD also influenced the weld metal hardness,especially when the wire used had a higher strength than the base metal. This showed that weld metal hardness had a more powerful effect on weld metal cold cracking than the diffusible hydrogen content in this experiment.

• Journal of Welding and Joining
• /
• v.13 no.4
• /
• pp.46-54
• /
• 1995

The cold cracking susceptibility of a variety of weld metals deposited by GMAW with several kinds of commercial solid wires for high strength-toughness steel was investigated. G-BOP test and LB-TRC test were carried out to study the effects of preheat, chemical composition and hydrogen level on the weld metal cold cracking. The results obtained are as follows. 1) 10% CPT obtained by G-BOP test was the most valuable criteria for evaluating the cold cracking susceptibility of weld metals compared with percentage of cracking at room temperature and crack free temperature, and it had good correlation with the results of LB-TRC test. 2) Cold cracking susceptibility of weld metals was high in the row of MG100A, MG100C, MG100D and MG100B. Welds deposited with MG130 and MG80 showed similar icidents of cracking with MG100C and MG100B respectively, even though their strength levels were different. 3) Diffusible hydrogen level in weld metals which has good relation with hydrogen content in wire itself was the most critical factor for controlling the cold cracking susceptibility of weld metal.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.65-73
• /
• 2011

Microstructural characteristics of two high strength (600 MPa & 800 MPa) weld metals produced by flux-cored arc welding process (FCAW) were evaluated. The 600 MPa grade weld metal was consisted of 75% acicular ferrite and 25% ferrite which was formed at relatively high temperature (grain boundary ferrite, widmanstatten ferrite, polygonal ferrite). However, the 800 MPa grade weld metal was composed of about 85% acicular ferrite and 15% low temperature forming phases (bainite, martensite). The prior austenite grain size of 800 MPa grade weld metal was decreased by solute drag force. The compositions and sizes of inclusions which are the dominant factors for the formation of acicular ferrite were analyzed by a transmission electron microscopy (TEM). In both 600 MPa and 800MPa grade weld metals, the inclusions were mainly consisted of Ti-oxide and Mn-oxide, and the average size of inclusions was $0.7{\mu}m$. The 800 MPa grade weld metal exhibited higher tensile strength and similar toughness compared with the 600 MPa grade weld metal. This result is mainly due to a higher fraction of low temperature products and a lower fraction of grain boundary ferrite in the 800 MPa grade weld metal.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.70-70
• /
• 2010

In the present study, to estimate the mechanical properties of 800 MPa grade weld metal, welding was carried out using 800 and 600 MPa grade flux cored arc welding (FCAW) consumable and characteristics of the weld metals were investigated. The chemical composition of weld metals was investigated by an optical emission spectroscopy (OES) method. The microstructure of weld metals was analyzed by optical microscopy (OM) and secondary electron microscopy (SEM). The compositions and sizes of inclusions which are the dominant factors for the nuclei of acicular ferrite were analyzed by an transmission electron microscopy (TEM). In addition, mechanical properties of the weld metals were evaluated through tensile tests and charpy impact tests. Mostly the acicular ferrite phase which has high strength and toughness was observed. The 600 MPa grade weld metal was consisted of 75% acicular ferrite and 25% ferrite which was formed at high temperature (grain boundary ferrite, widmanstatten ferrite, polygonal ferrite). However, the 800 MPa grade weld metal was composed of about 73% acicular ferrite and 27% low temperature phase (bainite, martensite). Toughness was considerably decreased due to the increase of tensile strength (from 600 MPa to 800 MPa). The sizes of inclusions which were observed in both weld metal were $0.4{\sim}0.8\;{\mu}m$, it is effective size to form acicular ferrite.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.44-48
• /
• 2001

The pipelines for natural gas transmission were buried in the ground of 1.5m depth. The pipelines were continuously subjected to vehicle load and internal pressure change by the quantity consumed of natural gas. In this paper, high cycle fatigue properties of natural gas transmission pipelines were studied. Fatigue specimens were obtained from the base and weld metal of circular pipe. Fatigue strength increased with increasing yield strength. Especially, the fatigue strength of base metal was higher than the yield strength of base metal and the fatigue strength of weld metal by manufactured process of TMCP.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.22-27
• /
• 2014

In the past, cold crack was commonly observed in the HAZ(heat affected zone) of high-strength steels. Applying to TMCP(thermo-mechanical controlled process) and HSLA(high strength low alloy) steels, cold crack tends to increase the occurrence in the weld metal. It is generally understood that cold crack occurs when the following factors are present simultaneously : diffusible hydrogen in the weld metal, a susceptible microstructure and residual stress. In particular, many studies investigated the microstructural effect on the cold crack in HAZ and the cold crack in weld metals starts to receive the special attendance in modern times. The purpose of the study is to review the effect of weld microstructures (grain boundary ferrite, Widm$\ddot{a}$nstatten ferrite, acicular ferrite, bainite and martensite) on cold crack in the weld metals. Among various microstructures of weld metals, acicular ferrite produced the greatest resistance to the cold crack due to the fine interlocking nature and high-angle grain boundary of the microstructure.

• Laser Solutions
• /
• v.7 no.2
• /
• pp.19-26
• /
• 2004

The effect of shield gas on the weldability, mechanical properties and formability of CO2 laser weld joint in 600MPa grade high strength steel was investigated. Bead on plate welds were made under various welding speed and shield gas. Tensile test was carried out under the load of perpendicular and parallel direction to the weld line, Formability of the joint was evaluated by Erichsen test. As the welding speed increases, the porosity fraction decreases. The porosity fraction in the joint used Ar-$50\%He$ mixed gas as a shield gas was lower than that of the joint used Ar gas. Hardness at the weld metal of full penetrated joint was nearly equal to that of water quenched raw metal. In a tensile test under a perpendicular load to the weld axis, strength and elongation of joint produced by optimum condition were nearly equal to those of base metal. However, the strength of joint in a tensile test under a parallel load to weld axis was higher than that of raw metal, but the elongation of joint was lower than that of raw metal. Elongation and formability were further increased by the method of using Ar+He mixed gas as a shield gas as compared with Ar gas. Formabilities of joints were recorded ranging from $58\%\;to\;70\%$ of that of base metal with different shield gases.

• Journal of Welding and Joining
• /
• v.4 no.2
• /
• pp.21-29
• /
• 1986

The influence of welding heat input variation(600-900J/cm) and heat-treatment condition after welding on tensile strength of butt welded joint in $175Kg/mm^2$ strength level Maraging steel(Co-free and Co-containing) sheets was investigated on the basis of hardness distribution, microstructure of weld metal and fracture surface. The obtained main results are as follows; 1. The strength of weldment (UTS, NTS), joint efficiency showed a little decreasing tendency with the increase in welding heat input, and the elongation showed a little increasing tendency with the increase in the width of weld metal. It was considered because of the plastic constraint of the high strength base metal. 2. The strength of weldment was better in the solution treatment and aging than the aging only after welding due to the disappearance of almost denverite in weld metal. 3. The hardness distribution in weldment after welding and heat-treatment was almost similar to both Co containing and Co free Maraging steel with change in welding heat input. 4. The fracture was occurred at weld metal, and the fracture surface showed a relatively shallow dimples in both Co containing and Co free Maraging steel.