• Journal of the Korean Magnetics Society
• /
• v.21 no.4
• /
• pp.136-140
• /
• 2011

Mechanical properties of degraded materials must be measured for evaluating the integrity of the facilities operating at high temperature. In fact it is complicated to obtain the different degraded specimens from an operating facility. Specimens of 1Cr-0.5Mo steel prepared by the isothermal heat treatment at $700^{\circ}C$ were tested, which has been widely used as tubes for heat exchangers and as plates for pressure vessels. The magnetic properties and Rockwell hardness (HRB) were measured at room temperature. The peak interval of Barkhausen noise envelope (PIBNE), coercivity, and hardness decreased with the increase of degradation. The magnetic and mechanical softening of matrix is likely to govern the properties of the specimen more than the hardening of grain boundary by carbide precipitations. The degradation of test material may be determined by the linear correlation of PIBNE and HRB. Degradation of 1Cr-0.5Mo steel could well be nondestructively evaluated by PIBNE measured with surface type probe.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.847-854
• /
• 1994

An amorphous single phase and coexistent amorphous and hcp-Mg phases in Mg-Zn-Ce system were found to form in the composition ranges of 20 to 40% Zn, 0 to 10% Ce and 5 to 20% Zn, 0 to 5% Ce, respectively. A $Mg_{85}Zn_{12}Ce_{3}$ amorphous alloy containing nanoscale hcp-Mg particles was found to form either by melt spinning or by heat treatment of melt -spun ribbon. The particle size of the hcp-Mg phase can be controlled in the range of 4 to 20 nm. The mixed phase alloy prepared thus has a good bending ductility and exhibits high ultimate tensile strength($\sigma_{B}$) ranging from 670 to 930 MPa and fracture elongation($\varepsilon_{f}$) of 5.2 to 2.0%. The highest specific strength($\sigma_{B}$/density =$\sigma_{s}$)$3.6 \times 10^5N \cdot m/kg$. It should be noted that the highest values of flB, US and ？1 are considerably higher than those (690MPa,$2.5 \times 10^5N \cdot m/kg$and 2.5%) for amorphous Mg-Zn-Ce alloys. The increase of the mechanical strengths by the formation of the mixed phase structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.245-251
• /
• 2015

We have applied mechanical alloying (MA) to produce soft magnetic composite material using a mixture of elemental $Fe_2O_3$-Mg powders. An optimal milling and heat treatment conditions to obtain soft magnetic ${\alpha}$-Fe/MgO composite with fine microstructure were investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that ${\alpha}$-Fe/MgO composite powders in which MgO is dispersed in ${\alpha}$-Fe matrix are obtained by MA of $Fe_2O_3$ with Mg for 30 min. The saturation magnetization of ball-milled powders increases with increasing milling time and reaches to a maximum value of 69.5 emu/g after 5 h MA. The magnetic hardening due to the reduction of the ${\alpha}$-Fe grain size by MA was also observed. Densification of the MA powders was performed in a spark plasma sintering (SPS) machine at $800{\sim}1000^{\circ}C$ under 60 MPa. X-ray diffraction result shows that the average grain size of ${\alpha}$-Fe in ${\alpha}$-Fe/MgO nanocomposite sintered at $800^{\circ}C$ is in the range of 110 nm.

• Korean Journal of Materials Research
• /
• v.10 no.11
• /
• pp.760-769
• /
• 2000

Mechanical properties of HSLA cast steels alloyed with 0.15% Nb, Ti or V were tested as variations of austenizing temperatures and tempering times. The test results are as follows. The hardness of HSLA cast steels austenized for 2hrs at 115$0^{\circ}C$ was shown the highest value regardless of alloying elements and then decreased as the temperature decreased below 110$0^{\circ}C$. The hardness of HSLA cast steels with 0.15% Ti austenized for 2 hrs at $1150^{\circ}C$ was higher than that of any other HSLA cast steels, and chich was mainly attributed to the relatively high amount of bainite, and solid solution hardening. Charpy impact energy of HSLA cast steels was comparable to the C-Mn cast steel except HSLA cast steels with 0.15% Ti austenized at 115$0^{\circ}C$. The hardness of HSLA cast steels austenized for 2 hrs at $1150^{\circ}C$ increased at a ten-minute tempering, and after that, the hardness kept almost sililar level except HSLA cast steels with 0.15% V.

• Journal of Conservation Science
• /
• v.30 no.3
• /
• pp.263-275
• /
• 2014

It's shown how to proceed the study on Manufacturing techniques & Conservation to the Iron Pot from Cheonmachong Ancient Tomb(the 155th Tomb in Hwangnam-dong). In order to investigate manufacturing techniques of the Iron Pot, some parts of the relic were gathered. After mounting, polishing and etching on the relic, analyzing the metal microstructure was conducted. Also it's conducted a SEM-EDS analysis on the nonmetallic inclusion. White iron structure was observed in the metallurgical structure inspection, SEM-EDS analysis. It seems to be dried slowly at room temperature after casting, doesn't look as particular heat treatment to improve brittleness. It is estimated that it's as the handle seam side were verified about 3cm inch wide, 1.5 thick in center of body, so 2 separate half-completed products was cast with width-type mould. The manufacturing techniques Using white cast iron structure, width-type mould are observable to the Iron Pot excavated from Sikrichong Ancient Tomb & Hwangnamdaechong grand Ancient Tomb around those were constructed the same time. It's able to recognize that it's almost identical manufacturing techniques at that time. Conservation is generically following those are survey of pretreatment, foreign material removal, stabilization, restoration and color matching in the order. cleaning & drying were added to the process as occasion demands. The strengthening treatment were difficult with artifact's volume, low concentration Paraloid NAD-10 solution was spread two or three times with a brush, surface hardening also came up with 15wt% Paraloid NAD-10 solution after the conservation was complete. There were connection & restoration for the restoration to the damage after modeling forms that it's similar to damaged parts by using the Fiber Reinforced Plastic resins(POLYCOAT FH-245, mold laminated type). Throughout this research, capitalizing on accumulations of measurements about the production technique of Iron Pot in the time of the fifth and 6th centuries is no less important than the Iron artifact's conservation for a better study in the future.

• Archives of design research
• /
• v.17 no.4
• /
• pp.241-250
• /
• 2004

In this research, the copper alloy plates C2200, C5210, C7701, C8113 were selected to make datum and to identify further usage of metal craft experimentation. For its experimentation, the general welding and TIG welding methods were researched; for 2nd experimentation, the Reticulation and Electroforming skill's differences in color and temperature were researched. With these methods 3 different kinds of works are introduced for sample studies. For this research, Dr. Lee, Dong-Woo who works in Poongsan Metal Co, supported 4 kinds of copper alloy metals. Which are Commercial bronze (Cu-Zn), Deoxidiged Copper(Cu-Sn-P), Nickel Silver (Cu-Ni-Zn), and White Bronze (Cu-Ni); they were applied partly and wholly by the method of Laminatin, Reticulation, Fusing, and Electroforming skills. In case of C2200, the brass, the A. C. TIG welding method is better under 2mm slight plate; the D.C. TIG welding is better upper 2mm plate; and 250~300$^{\circ}C$ is recommended for remain heat treatment. In case of C5210, not having Hydrogen in high temperature return period, doesn't need Oxygen in high temperature and hardening in comparative high temperature neither, it is good for welding. It contains Sn 2-9% ad P 0.03-0.4% generally; and in accordance with the growth rate of Sn contain amount, the harden temperature boundary become broad. In case of cold moment after welding, they are recommended that higher speed TIG welding, smaller melting site and less than 200$^{\circ}C$ for pre-heating temperature. In case of C7701, the 10-20% Ni, 15-30% Zn are widely used.. If it is upper 30% Zn, it become (${\alpha}+{\beta}$) system and adhesive power rate become lower, and the productivity become lower in low temperature but the productivity become higher in high temperature. Nickel Silver's resistance of electricity is well; and the heatproof and incorrodibility is good, too. Lastly, in case of C8113, good at persistence in salty and grind; high in strength of high temperature. In case of white brass, contain 10-30% Nickel and hardened in high temperature and become single phrase. For these reason, the crystallization particles easily become large, if the resistance become higher small amount of Pb, P, S separation rate become higher.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.17 no.5
• /
• pp.361-367
• /
• 1984

In previous paper(Lee et al., 1984), preparation formula and processing conditions of the fish meat (mackerel) paste using dielectric heating were described, that included the proper shape and size of product and the conditions of dielectric heating, hot air dehydration, and heating with electric heater to yield the minimum expansion and case hardening during heating and to controll the final rater activity of 0.86 to 0.83 accompanying with a complete reduction of viable cells and good texture. In present study, changes in VBN, pH, total plate count, water activity, texture, the loss of available lysine, color indexes, TBA value, and the content of TI were determined to assess the quality stability and shelf-life of the product during the storage for 35 days at $5^{\circ}C\;and\;25^{\circ}C$, respectively. And the effect of vacuum sealing and hot water treatment before storage on the storage stability of product was also mentioned. As the product was vacuum packed in K-flex film bag, heat treated in boiling water for 6 minutes, and stored, water activity was maintained 0.86 to 0.84 for 35 days regardless of storage temperature, and the increase of total plate count was negligible in case of $5^{\circ}C$ storage while tended to gain slightly after 25 days at $25^{\circ}C$ storage. Changes in VBN was also minimum with an increase of 1.5 mg/100g at $5^{\circ}C$ and 7.0mg/100g at $25^{\circ}C$, but in case of unpacked sample, it was 24.5mg/100g at $5^{\circ}C$ and 42.4 mg/100g at $25^{\circ}C$ even after 7 days. In textural property hardness tended to increase after 28 days and folding test score was down to A or B from AA grade. The loss of available lysine was $7.5\%\;at\;5^{\circ}C$ and $17.0\%\;at\;25^{\circ}C$ but brown color was not deeply developed as the color index score indicated. TBA value was not increased at $5^{\circ}C$ while it tended to increase rapidly after 30 days at $25^{\circ}C$. Changes in TI content was not obvious except that it showed a tendency of increase at the end of storage as well as in the change of lysine and TBA value. It is concluded from the results that the quality of the product, pasteurized and water activity controlled by dielectric heating, and vacuum packed in K-flex film would be stable for more than 35 days at $5^{\circ}C$ and at least 25 days even at room temperature.