• 열처리공학회지
• /
• 제20권5호
• /
• pp.231-236
• /
• 2007

High velocity oxy-fuel (HVOF) spraying was used to coat Ti(Al,O)/$Al_2O_3$ powder onto the SS41 steel plate. Macrostructure of the coated specimen has been investigated by scanning electron micrograph (SEM). High temperature oxidation behavior of the coated specimen and SS41 steel have been studied. From the results of SEM observation, Ti(Al,O)/$Al_2O_3$ powder was coated well onto the substrate SS41 steel. Porosity onto the coated layer was only 0.38%. The oxidation results showed that Ti(Al,O)/$Al_2O_3$ powder coated SS41 steel have improved little oxidation resistance at $900^{\circ}C$ in air, but improved remarkably oxidation resistance at $800^{\circ}C $ in air compare to the substrate SS41 steel.

• Composites Research
• /
• 제30권2호
• /
• pp.84-93
• /
• 2017

본 논문에서는 탄화규소 섬유강화 탄화규소 복합재료에 내환경 코팅을 수행한 후, 열 기계적 특성평가에 대한 연구를 수행하였다. 초기분말은 성형공정도중 흐름성을 좋게 하기 위해 분무건조법으로 구형의 분말을 제조하였다. 내환경 코팅재는 복합재료가 산화되거나 고온 수증기와 반응하는 것을 방지하기 위해 행하여 지는데, 본 연구에서는 액상침투법(LSI)으로 제조한 복합재에 실리콘으로 본드코팅을 하고 그 위에 대기플라즈마용사법으로 뮬라이트(mullite)와 무게비로 12% 이터븀 실리케이트(ytterbium silicate)가 혼합된 복합재를 코팅하였다. 대기플라즈마 코팅공정 시 성형변수로서 분무거리를 100, 120 그리고 140 mm로 변화시켰다. 그 후 $1100^{\circ}C$의 온도에서 100시간동안 유지하는 실험과 $1200^{\circ}C$의 온도에서 열충격을 가하는 싸이클을 3000회 반복하였다. 열내구성 시험동안 계면 박리는 일어나지 않았지만, 현저한 균열들이 코팅층 내에서 발견되었다. 균열밀도와 균열의 길이는 코팅도중의 분무거리에 의존하여 변화하였다. 열 내구성 시험 후, 압흔 시험을 통해 기계적 열화거동을 분석하였는데, 시험의 방식이나 조건들이 하중-변위 곡선의 거동에 영향을 주었다.