• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.40-46
• /
• 1999

Rotary bending fatigue tests were carried out to investigate the improvement of fatigue limit in annealed and austempered spheroidal graphite cast iron. Main results obtained are as follows. (1) The tensile strength(hardness) of Series C is higher than that of Series B, and fatigue limits are 245MPa in Series C, 230MPa in Series B and 195MPa in Series A, respectively. (2) The fatigue limits of Series B and Series A are mainly governed by the resistance to fatigue crack initiation. Whereas, the fatigue limit of Series C is governed by the resistance to fatigue crack initiation and growth. The defect size and the resistance to crack initiation and growth should be considered to clarify the fatigue properties in spheroidal graphite cast iron. (3) Improvement of fatigue limit by half-austempering is more reasonable than that of full-austempering treatment in multi defective materials as spheroidal graphite cast iron.

• Journal of Industrial Technology
• /
• v.18
• /
• pp.203-208
• /
• 1998

Fatigue tests were performed to examine the 4 parameter method for specimens prepared by various heat treatment which resulted in different mechanical properties. Obtained main results are as follows. (1) Samples treated by austempering did not show the expected improvement of fatigue limit although hardness and strength increased. This is attributed to the fact that defect sensitivities of materials increase as increasing of hardness and tensile strength, it is also shown that the graphites acting as stress concentration place become larger by austempering heat treatment than by normal annealing. (2) It is very reasonable to predict the fatigue limit of ductile irons with 4 parameter method based on ${\sigma}_{TS}$, $H_v$, ${\Delta}K_{th}$ and ${\sqrt{area}}_{max}$. (3) The half-austempering treatment appeared to be more useful than the full-austempering method to improve the fatigue limit in the spheroidal graphite cast iron with multi defective material.