• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.274-276
• /
• 2006

Weldability of high Cr ferritic steel for $620^{\circ}C$ grade turbin casing were investigated. The effect of carbon content on the cold and hot cracking susceptibility and HAZ softening was determined. The cast steel with higher carbon content showed higher HAZ hardness because of the dissolution of cabonitrides during welding thermal cycle. Moreover, it showed higher solidification cracking sensitivity because of the little S-ferrite formation in weld metal. Both steels showed HAZ softening at $900^{\circ}C$ peak temperature after PWHT.

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.93-104
• /
• 1996

This study evaluated relative hot cracking susceptibility of commercial aluminum alloy welds, and then suggested possible mechanisms operated in the weld fusion zone and in the heat affected zone based on the observed cracking morphologies, fractography and microstructural features. The fusion zone solidification cracking was found to be mainly due to a microsegregation of Cu, Si, and Mg in grain boundaries, while liquation cracking in the HAZ was by the incipient melting of the segregated grain boundaries and the consitutional liquation of large aging precipitates and intermetallic compounds in the partially melted zone adjacent to the fusion line which experienced a rapid thermal excursion during welding.

• 대한공업교육학회지
• /
• v.31 no.1
• /
• pp.200-210
• /
• 2006

This C-ring test, normally employed for evaluating susceptibility to stress-corrosion cracking, was determined to be a suitable small scale test to evaluate PWHT(Post-Weld Heat Treatment) cracking susceptibility. This test is possible to incorporate an actual weld, to introduce a notch into the coarse grained HAZ(Heat Affected Zone), to load the coarse grained HAZ any level of stress ad, most importantly, since the C-ring is an approximately constant strain type test, the stress decreases with time at temperature in a manner similar to that of an actual steel weldment. The procedure employed in making the C-ring was presented in the experimental procedure section, however, several points deserve further discussion. The walls of the weld groove are made along radial lines form the center of th var in order to obtain an HAZ which is oriented perpendicular to the walls of the machined C-ring. Therefore, the plane of maximum stress will be aligned through the HAZ and, therefore, crack propagation will not be forced to deviate form the plane of maximum stress in order to remain in the coarse grained HAZ as is the case with the Y groove test.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.31-38
• /
• 2013

The transition of serrated grain boundary and its effect on liquation behavior in the simulated weld heat-affected zone (HAZ) have been investigated in a wrought Ni-based superalloy Alloy 263. Recently, the present authors have found that grain boundary serration occurs in the absence of adjacent coarse ${\gamma}^{\prime}$ particles or $M_{23}C_6$ carbides when a specimen is direct-aged with a combination of slow cooling from solution treatment temperature to aging temperature. The present study was initiated to determine the interdependence of the serration and HAZ property with a consideration of this serration as a potential for the use of a hot-cracking resistant microstructure. A crystallographic study indicated that the serration led to a change in grain boundary character as special boundary with a lower interfacial energy as those terminated by low-index {111} boundary planes. It was found that the serrated grain boundaries are highly resistant to boron enrichment, and suppress effectively grain coarsening in HAZ. Furthermore, the serrated grain boundaries showed a higher resistance to susceptibility of liquation cracking. These results was discussed in terms of a significant decrease in interfacial energy of grain boundary by the serration.

• Proceedings of the KWS Conference
• /
• 1997.10a
• /
• pp.16-18
• /
• 1997

• Journal of Welding and Joining
• /
• v.12 no.2
• /
• pp.87-96
• /
• 1994

Correlation between microstructural features and segregation of elements (Si, Mn, P and S) near the mid of thickness in the base metal and the synthetic HAZ was investigated. Furthermore, the relationship between the degree of center segregation and weld cold cracking susceptibility in the thickness direction was also conducted by evaluating the effect of P concentration on the critical applied stress. The results obtained are as follows: 1) Pearlite band, containing the MnS type inclusion and a locally transformed structure with a higher hardness, was observed in the center segregation region. 2) By the weld thermal cycle, center segregation region was transformed to the white band which had a higher hardness than that of base metal due to a greater hardenability of concentrated Mn, P etc.. 3) Weld cold cracking susceptibility in the thickness direction was mainly dependent on the concentration of impurity elements rather than on the number of the segregated particles near the mid of thickness. 4) During welding, the higher concentrated region was easily changed into white band. Therefore, it could be predicted that the initiation and propagation of a cold crack would be promoted by increasing the restraint stress and hydrogen content.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.213-213
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7NO1 spot-welded by pulse Nd: YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed: center line crack($C_{C}$), diagonal crack($C_{D}$), and U shape crack($C_{U}$). Also, HAZ crack($C_{H}$), was observed in the HAZ region, furthermore, mixing crack($C_{M}$), consisting of diagonal crack and HAZ crack was observed.White film was formed at the hot crack region in the fractured surface after it was immersed to 10%NaOH water. In the case of A5083 alloy, white films in C crack and $C_D crack region were composed of low melting phases, Fe₂Si$Al_8$ and eutectic phases, Mg₂Al₃ and Mg₂Si. Such films observed near HAZ crack were also consist of eutectic Mg₂Al₃. In the case of A7N01 alloy, eutectic phases of CuAl₂, $Mg_{32}$ (Al,Zn) ₃, MgZn₂, Al₂CuMg and Mg₂Si were observed in the whitely etched films near $C_{C}$ crack and $C_{D}$ crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Si in the case of A7N01 aooly, respectively.The $C_{D}$ and $C_{C}$ cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of $C_{M}$ crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The $C_{U}$ crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification. (Received October 7, 1999)

• Journal of Welding and Joining
• /
• v.2 no.2
• /
• pp.54-61
• /
• 1984

Construction of welding structure is greatly dependent upon welding heat cycle. Fracture toughness is decreased remarkablely due to coarse grained HAZ and inequal residual stress of three dimensions to originate in welding. Post weld heat treatment(PWHT) is carried out to increase the fracture toughness of HAZ and to remove the residual stress. There occur some problem such as toughness decrement and stress relief cracking(SRC) in the coarse grained HAZ subject to the effect of tempering treatment. Therefore, in this paper, the effect of heat inputs affecting cooling rate and PWHT under the no stress on fracture toughness were evaluated by crack opening displacement (COD), SEM and micro-hardness test. Experimental results are as follows; 1. Fracture toughness of weld HAZ is dependent upon weld heat cycle and it is decreased with increment of heat input, but the degree of improvement of fracture toughness after PWHT was linearly increased with heat input. 2. Hardness of the parent metal is not changed, but the softening of coarse grained HAZ is remarkable due to PWHT. 3. Fracture surface of as-weld show the perfect brittle fracture with the cleavage fracture, but after PWHT they appear the ductile fracture surface with dimple.

• International Journal of Korean Welding Society
• /
• v.3 no.2
• /
• pp.24-28
• /
• 2003

This study was aimed to evaluate the quality of flash welded joints and optimize the welding process for flash butt welding of 780MPa grade high strength steel. And then the relationship between the welding process variables and the joint quality would be established. The effect of process variables between flashing and upsetting process was elucidated. Microstructure observation of the joint indicated that the decarburized band was mainly changed with upsetting process. Width of HAZ was also related to the upsetting conditions rather than the flashing conditions. Generally maximum hardness at HAZ was correlated with Ceq of steel and the empirical relationship was obtained to estimate the HAZ properties. Tensile elongation at the joint was usually decreased with increasing the initial clamping distance. Investigation of fracture surface after tensile and bending tests reveal that the origin of cracking at the joint was oxide inclusions composed of $SiO_2$, MnO, $Al_2O_3$, and/or FeO. The amount of inclusions was dependent on the composition ratio of Mn/Si in steel. If this ratio was above 4, the amount of inclusions was low and then the resistance to cracking at the joint was enough to maintain the joint performance. It was obtained that the flashing process influenced the conditions for the energy input to establish uniform or non­uniform molten layer, while the upsetting conditions influenced the joint strength. Heat input variable during flashing process was also discussed with the joint properties.

• Journal of Welding and Joining
• /
• v.5 no.2
• /
• pp.9-16
• /
• 1987

Post weld heat treatment (PWHT) is carried out to increase the fracture toughness in heat affected zone(HAZ) and remove the residual stress. There occur some problems such as toughness decreement and stress relief cracking(SRC) in the coarse grained HAZ subjected to the effect of tempering treatment. Especially, embitterment of structure directly relates to the mode of fracture and is appeared as the difference of fracture surface, that is, grain boundary failure. Therefore, in this paper, PWHT was carried out under the stress of 0, 10, 20 and $30kg/cm^2$ to simulate residual stress in HAZ welded by heat input of 10, 30 and 40KJ/cm. Applied stress in weld HAZ during PWHT assisted precipitin of over saturated alloying element in the structure, and grain boundary failure according to welding heat input didn't almost appear at the heat input of 10 KJ/cm, but it appeared from being the applied stress of $30kg/cm^2$ at $30KJ/cm and 20kg/mm^2$ at 40KJ/cm.