In an effort to protect a RBSC(reaction -bonded SiC) tube SiC films from methyltrichlorosilane(MTS) by low pressure chemical vapor deposition were deposited in hydrogen atmosphere on the RBSC(reaction-bonded SiC) substrates over a range of input gas ratio(${\alpha}=P_{H2}/P_{MTS}=Q_{H2}/Q_{MTS}$=1 to 10) and deposition temperatures(T=1050~1300$^{\circ}C$). At the temper-ature of 1250$^{\circ}C$ the growth rate of SiC films increased and then decreased with decreasing the input gas ratio. The microstructure of SiC films was changed from granular type structure exhibiting (111) preferred orientation in the high input gas ratios to faceted columnar grain structure showing (220) in the low input gas ratios. The similar microstructure change was obtained by increasing the deposition temperature. These results were closely related to a change of deposition mechanism. Double layer structure having granular type and faceted ciolumnar grain structure from the manipulation of mechanism. Double layer structure having granular type and faceted columnar grain structure from the manipulation of the input gas ratio without changing the deposition temperatue was successfully fabricated through in -site process.

• Journal of Korean Ophthalmic Optics Society
• /
• v.11 no.2
• /
• pp.85-89
• /
• 2006

To research of the improved mechanical properties of materials for spectacle lens cutting, SiC and TiC were used as the main powder. Also, $Al_2O_3$ and $Y_2O_3$ was included as a sintering additive. The weight ratio of the alumina($Al_2O_3$) to yttria($Y_2O_3$) was set to 1:1. The materials for spectacle lens cutting were fabricated by hot-pressing at $1810^{\circ}C$ for 1h and subsequently annealed at $1860^{\circ}C$ for 3, 6 and 12h to initiated grain growth. The longer annealing time is, the bigger the grain size is. The microstructures were observed by scanning electron microscopy (SEM). The SEM images were quantitatively analyzed by image analysis (Image-Pro Plus, Media Cybernetics, Maryland, U.S.A.). Crack deflection by elongated SiC grains was most frequently observed as the dominant toughening mechanism. Crack deflection was generally observed for elongated SiC grains with aspect ratio(AR) > 2.5 and grain thickness < $2.3{\mu}m$. Crack bridging was also observed as one of the operating toughness mechanism.

• Computers and Concrete
• /
• v.17 no.1
• /
• pp.107-127
• /
• 2016

Concrete is a heterogeneous material containing many weaknesses such as micro-cracks, pores and grain boundaries. The crack growth mechanism and failure behavior of concrete structures depend on the plastic deformation created by these weaknesses. In this article the non-linear finite element method is used to analyze the effect of presence of micro pore near a crack tip on both of the characteristics of crack tip plastic zone (its shape and size) and crack growth properties (such as crack growth length and crack initiation angle) under pure shear loading. The FE Code Franc2D/L is used to carry out these objectives. The effects of the crack-pore configurations and the spacing between micro pore and pre-excising crack tip on the characteristics of crack tip plastic zone and crack growth properties is highlighted. Based on the obtained results, the relative distance between the crack tip and the micro pore affects in very significant way the shape and the size of the crack tip plastic zone. Furthermore, crack growth length and crack initiation angle are mostly influenced by size and shape of plastic zone ahead of crack tip. Also the effects of pore decrease on the crack tip by variation of pore situation from linear to perpendicular configuration. The critical position for a micro pore is in front of the crack tip.

• Journal of Advanced Marine Engineering and Technology
• /
• v.10 no.1
• /
• pp.65-73
• /
• 1986

Surface fatigue crack propagation tests by plane bending fatigue were conducted on the welding specimens of an aluminium alloy, A5083-0, having an edge through thickness notch to study the fatigue crack growth characteristics. Moreover, the experiments were performed in order to clarify the fatigue crack initiation and growth. The properties of fatigue crack growth were quantitatively inspected in welded metal, heat-affected zone and base metal of the welding specimens. The main results obtained are summarized as follows: 1. It is found that the hardness distributions of A5083-0 aluminium alloy weldments are quite different with those of steel material weldments, so that the hardness distribution becomes lower in the following order: base metal, heat-affected zone and weld metal. 2. It is observed that the grain size of this specimen weldment appears to be almost equal to the base metal, when TIC welding method is adopted. 3. In a surface fatigue crack initiation and growth, the fatigue crack does not begin by opening-closing mechanism until hardening is saturated at the crack tip. 4. The fatigue crack growth characteristics of A5083-0 alluminium alloy weldments can be concluded.$${\frac{da}{dn}}=C({\Delta}K)^n=3.8{\times}10^{-9}{({\frac}{1}{2}{\Delta}S_t{\sqrt{{\pi}a}})}^{2.4}$$

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.67-74
• /
• 1998

Two kinds of polished and unpolished freestanding films prepared by DC plasma CVD method were impacted by SiC particles to understand erosion mechanism. Erosion damage caused by solid impact was characterized by surface profilometer, scanning electron microscopy and Raman spectroscopy. Gradually decrease of surface roughness and sharp reduction of crystallinity for unpolished CVD films were observed with increasing erosion time. It was found that smaller grains of the diamond were removed in early stage of erosion process and larger grains were eroded with further impingement. By introduction of re-growth method on polished diamond, further understanding of erosion mechanism was achieved. Most of the surface fractures were initiated at the grain boundary.

• Journal of the Korean Ceramic Society
• /
• v.23 no.5
• /
• pp.55-60
• /
• 1986

A mechanism for formation of surface reoxidation layer in Surface Boundary Layer Capacitor (SBLC) has been studied. SBLC were prepared by reduction of $BaTiO_3$ doped with $Bi_2O_3$ and electrode firing of silver paste containing $Bi_2O_3$ The apparent dielectric constant was in the order of $10^5$ and the insulation resistance larger than $10^6$$\Omega$ It can be expected that $Bi_2O_3$ dopant in $BaTiO_3$ plays the role of inhibition of grain growth and decreasing the resistivity of $BaTiO_3$. In order to confirm the process of surface reoxidation layer effects of atmosphere and annealing time in electrode sintering were investigated.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.334-335
• /
• 2006

WC/WC interface in VC mono-doped WC-10mass%Co submicro-grained hardmetals of $0.5\;{\mu}m$ was investigated together with WC/Co interface by using HRTEM and XMA. The thickness of V-rich layer and the analytical value of V at WC/WC interface were almost the same as those at WC/Co interfaces. These results, etc., suggested that the V-rich layers at both interfaces were not generated by an equilibrium segregation mechanism in the sintering stage, but generated by a preferential precipitation mechanism during the solidification of Co liquid phase in the cooling stage. Based on this suggestion, we succeeded in developing a nano-grained hardmetal with 100 nm $(0.1\;{\mu}m)$.

• Journal of Powder Materials
• /
• v.8 no.1
• /
• pp.61-69
• /
• 2001

Spark-Plasma Sintering(SPS) is one of the new sintering methods which takes advantages both inconventional pressure sintering and electric current sintering. It is known that SPS is very effective for the densification of hard-to-sinter materials like refractory metals, intermetallic compounds, glass and ceramics without grain growth. However, a clear explanation for sintering mechanism and an experimental evidence for the formation of weak plasma during SPS are not given yet. In this study, fundamental study on sintering behavior and mechanism of SPS was investiged. For this study, various spherical Fe powders were prepared such as as-received, as-reduced, and as-oxidized and then sintered by SPS facility. In order to confirm the surface cleaning effect during SPS neck region and fracture surface of sintered body was observed and analyzed by SEM/EPMA. Densification behavior was analyzed from the data of deflection along the pressure axis. Some specimens were additionally produced by Hot Pressing and the results were compared with those of SPS.

• Journal of the Korean Ceramic Society
• /
• v.42 no.9 s.280
• /
• pp.599-601
• /
• 2005

The coarsening process of two different $BaTiO_3$ single crystal seeds, one with a (111) double twin and the other without it, was investigated. Due to the presence of Twin Plane Reentrant Edge (TPRE), the coarsening rate of the twinned seed crystal was significantly higher than that without a twin. For the coarsening by the 2-dimensional nucleation and lateral growth, the energy barrier for nucleation at the TPRE was analyzed to be about a half compared with that at the terrace planes.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1330-1332
• /
• 1998

Polycrystalline diamond films are deposited on a Si substrate by employing a 2.45 GHz $\mu$-wave plasma CVD system. Prior to depositing the diamond film, a DPR(diamond photo-resist) layer is coated to enhance the nucleation density. The growth rate of diamond films increases with the $\mu$-wave power and approaches to be about $1.5{\mu}m/hr$ at 1100 W. Structural properties of diamond films deposited are characterized from their SEM photographs, Raman spectra, and AFM surface images. Lager grain size, higher intensity of diamond peak, and smoother surface are observed for films deposited at a higher power. The possible mechanism on the diamond growth is also discussed to explain the experimental results.