• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.105-111
• /
• 2020

The present study examined the effect of the silica-based accelerating agents on the setting time and compressive strength gain of biomimetic glycocalix coating materials that has been developed for protecting the substrate of concrete exposed to chemical and microbiological attacks. The accelerating agent contents varied from 10mL/L to 40mL/L in the mixtures of glycocalix coating materials determined for shotcrete and lining techniques. Test results showed that the setting time of coating materials containing accelerating agents was affected by the contents of the bacteria carrier. When the accelerating agent content was 40mL/L, the final setting time was 80 minutes for shotcrete mixtures and 318 minutes for lining mixtures. Meanwhile, the compressive strength gain of coating materials with accelerating agents tended to be lower than that of counterpart materials without accelerating agents.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.97-104
• /
• 2020

The present study conducted mock-up tests under the simulated sewage environments to examine the practical significance and limitation of coating materials that were previously developed on the basis of the bacterial glycocalix as a protection of concrete structures exposed to microbiological and sulphate attacks. The variations of the compressive strength and mass of the concrete due to the sulphate attack were measured using cylinder specimens. The bacteria growth and glycocalix formulation were calculated from the samples extracted from the sewage pipes. The next generation sequencing analysis was also conducted for environmental damage assessment due to the use of Rhodobacter capsulatus in the simulated sewage environments. The mock-up tests revealed that the developed coating materials have a good potential in resisting the sulphate attack, indicating no reduction on compressive strength and mass of the coated concrete under the sewage environment. At the age of 91 days, the concentrations of viable bacteria and glycocalix measured from the hardened coating materials were 1.4×10⁴cell/mL and 67.5mg/㎤, respectively. Moreover, harmful strains were not observed in the sewage water including glycocalix-coated concrete pipes. This implies that Rhodobacter capsulatus used in the coating materials does not influence negatively the microorganism cluster in the sewage environments.