• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.215-219
• /
• 2007

In this work, the indium zinc oxide (IZO) films had been deposited on the glass substrate coated with the SiO film. Based on a comparative investigation of the IZO monolayer and IZO/SiO multilayer, it is shown that the thickness of SiO film has a great effect on the mechanical properties of the thin films. The AFM images of the IZO thin film included the SiO film were shown smoother surfaces than monolayer. Resistivity was in inverse proportion to Mobility. If it deposited the SiO film on the substrate, the layer of change was generated between two layer(SiO and substrate). The layer of change influenced resistance because of oxygen content was more than the IZO monolayer.

• 분석과학
• /
• 제6권2호
• /
• pp.239-246
• /
• 1993

ITO coated glass, bare glass, 그리고 (100)Si 기판 위에 증착된 $(BaSr)TiO_3$ 박막의 구조는 기판의 종류에 관계없이 변하지 않았으나 결정성은 다결정 ITO층과 (100)Si 기판에 있어서 증대되었다. ITO coated glass 기판 위에 증착된 $(BaSr)TiO_3$ 박막의 조성은 거의 화학양론적으로 일치하였으며 ((Ba+Sr)/Ti=1.08~1.09) 증착 중 상당히 치밀하고 균질하였다. 그러나 증착온도가 증가함에 따라 성장한 박막과 ITO층 사이에, 그리고 ITO층과 base glass 사이에 확산이 보다 심화되었다. ITO coated glass 기판 위에 증착된 $(BaSr)TiO_3$ 박막은 상당히 투명하였으며(투과율 약 80%) 굴절률($n_f$)은 기판온도의 증가에 따라 2.138~2.286이었다.

• 마이크로전자및패키징학회지
• /
• 제19권4호
• /
• pp.33-37
• /
• 2012

Microstructure developments of $RuO_2$ based thick film resistors during firing as a function of glass viscosity were analytically quantified and its effect on the electrical property was investigated. The microstructure development was retarded as the viscosity of glass was increased. It was found that the viscosity range for each stage of microstructure development are as follows ; $7500-10^5Pa{\cdot}s$ for the glass sintering, $2000-7500Pa{\cdot}s$ for the glass island formation, $700-2000Pa{\cdot}s$ for the glass spreading, and $50-700Pa{\cdot}s$ for the infiltration. The sheet resistivity decreased as the viscosity of glass in the resistor film increased due to the higher chance of sintering for the conductive particles with the higher viscosity of the glass.

• 한국표면공학회지
• /
• 제46권3호
• /
• pp.111-115
• /
• 2013

To study the encapsulation method for large-area organic light emitting devices (OLEDs), OLED of ITO / 2-TNATA / NPB / $Alq_3$:Rubrene / $Alq_3$ / LiF / Al structure was fabricated, which on $Alq_3$/LiF/Al as protective layer of OLED was deposited to protect the damage of OLED, and subsequently it was encapsulated using attaching film and flat glass. The current density and luminance of encapsulated OLED using attaching film and flat glass has similar characteristics compared with non-encapsulated OLED when thickness of Al as a protective layer was 1200 nm, otherwise power efficiency of encapsulated OLED was better than non-encapsulated OLED. Encapsulation process using attaching film and flat glass did not have any effects on the emission spectrum and the Commission International de L'Eclairage (CIE) coordinate. The lifetime of encapsulated OLED using attaching film and flat glass was 287 hours in 1200 nm Al thickness, which was increased according to thickness of Al protective layer, and was improved 54% compared with 186 hours in same Al thickness, lifetime of encapsulated OLED using epoxy and flat glass. As a result, it showed the improved efficiency and the long lifetime, because the encapsulation method using attaching film and flat glass could minimize the impact on OLED caused through UV hardening process in case of glass encapsulation using epoxy.

• 한국정밀공학회지
• /
• 제27권12호
• /
• pp.28-32
• /
• 2010

Technical demands for aspheric glass lens formed in market increases its application from simple camera lens module to fiber optics connection module in optical engineering. WC is often used as a metal core of the aspheric glass lens, but the long life time is issued because it fabricated in high temperature and high pressure environment. High hard thin film coating of lens core increases the core life time critically. Diamond Like Carbon(DLC) thin film coating shows very high hardness and low surface roughness, i.e. low friction between a glass lens and a metal core, and thus draw interests from an optical manufacturing industry. In addition, DLC thin film coating can removed by etching process and deposit the film again, which makes the core renewable. In this study, DLC films were deposited on the SiC ceramic core. The process variable in FVA(Filtered Vacuum Arc) method was the substrate bias-voltage. Deposited thin film was evaluated by raman spectroscopy, AFM and nano indenter and measured its crystal structure, surface roughness, and hardness. After applying optimum thin film condition, the life time and crystal structure transition of DLC thin film was monitored.

• 한국산학기술학회논문지
• /
• 제19권1호
• /
• pp.105-112
• /
• 2018

본 논문은 로이유리(Low emissivity glass) 표면에 증착되어 있는 금속박막의 전도 특성을 이용하여 발열유리(Heatable glass)를 제작하는 방법에 대해 제안한다. 로이유리의 발열량은 로이유리 표면저항에 의한 주울(Joule) 열에 의존하므로 소재의 표면저항을 측정함으로써 예측 및 설계가 가능하다. 본 연구에서는 저방사층이 11nm인 소프트로이유리 시료에 각 50mm 간격으로 은(Ag) 전극을 형성시키고, 4단자법으로 면저항을 측정하여 로이유리의 소비전력과 발열량을 예측한 후에, 제작 및 실험을 통해 발열성능을 확인하였다. 기존의 발열유리 제작방법은 크게 두 가지로 일반유리(Normal glass)에 니크롬(Nichrome) 열선을 삽입하는 방법과, 일반유리에 전도성 투명박막을 증착하는 방법이 있다. 니크롬 열선 삽입 방식은 발열성능은 우수하나 유리 고유의 투명성을 저해하고, 전도성 투명박막을 증착하는 방법은 투명성은 양호하나 공정이 복잡하여 실용성이 저하된다. 본 논문에서는 주로 건축물의 단열효과 향상을 위해 사용되는 로이유리를 이용하여 로이유리 전면에 코팅되어 있는 전도성 금속박막에 레이저 빔을 조사하여 원하는 발열성능을 가지는 발열유리를 제작하는 방법을 제안한다. 제안된 방법은 기존의 니크롬 열선을 삽입하는 방법에 비해 투명성이 양호하고, 전도성 투명박막을 증착하는 방법에 비해 제작과정이 보다 수월함을 확인하였다. 아울러, 레이저를 조사하여 로이유리의 표면 박막을 패터닝(Patterning) 하는 형태에 따른 발열특성의 비교와 로이유리에 적합한 레이저 출력조건을 제시하고자 한다.

• 폴리머
• /
• 제37권5호
• /
• pp.656-662
• /
• 2013

태양전지의 효율 증가를 위하여 유리비드가 함유된 polymethyl methacrylate(PMMA) 용액을 PMMA 필름 위에 코팅하여 유리비드가 코팅된 고분자 유연 패턴 필름을 제조하고 패턴 필름이 태양전지 효율에 미치는 영향을 살펴보았다. 필름 위에 코팅된 유리비드로 인하여 빛의 입사각 0도에서 90도 범위에서 태양전지의 상대효율이 최대 3.4%까지 증가함을 알 수 있었다. 이러한 효율 증가는 빛의 입사각 변화에도 필름 표면에 형성되어 있는 구 형태의 유리비드로 인하여 빛이 수직으로 입사되어 방향성에 의한 태양전지 효율 감소가 최소화되기 때문이다. 태양전지상대효율 증가는 필름 표면 위의 유리비드가 반구의 형태를 가질 때 가장 높으며 유리비드 함량에 따라 증가되나 유리비드 함량이 너무 많은 경우, 오히려 광 투과도 감소 및 빛의 간섭 효과에 의하여 상대효율이 감소됨을 알 수 있었다.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 1986년도 Priceedings Of The Third Korea-Japan Seminar On New Ceramics
• /
• pp.259-267
• /
• 1986

The sintering behavior of silver-oxide glass composite thick-film has been studied with varing glass content. It is shown that during heat treatment glass became liquid phase to deeply affect the microstructure development of the silver particles and to control the physical properties of the thick-films. As glass content increased, the initial repacking of silver particles took place rapidly but the homogeneities of the microstructure showed different features. When the glass content was over some range, the silver particles exuded glass to decrease net energy and glass formed liquid pools separated from the solid skeletons. Finally the relations between the microstructures and electrical properties of the thick-film were discussed.

• 마이크로전자및패키징학회지
• /
• 제14권3호
• /
• pp.57-64
• /
• 2007

Si 칩에 박막히터를 형성하고 이에 전류를 인가하여 LCD (liquid crystal display) 패널의 유리기판은 가열하지 않으면서 Si 칩만을 선택적으로 가열함으로써 Si 칩을 LCD 패널의 유리기판에 실장 하는 새로운 COG 공정기술을 연구하였다. $5\;mm{\times}5\;mm$ 크기의 Si 칩에 마그네트론 스퍼터링법으로 폭 $150\;{\mu}m$,두께 $0.8\;{\mu}m$, 전체 길이 12.15 mm의 정방형 Cu 박막히터를 형성하였으며, 이에 0.9A의 전류를 60초 동안 인가하여 Si칩의 Sn-3.5Ag 솔더범프를 리플로우 시킴으로써 Si 칩을 유리기판에 COG 본딩하는 것이 가능하였다.

• 한국세라믹학회지
• /
• 제45권2호
• /
• pp.87-89
• /
• 2008

A nano structured silica aerogel thin film was manufactured from inexpensive sodium silicate (water glass) using an ambient pressure drying method. High purity silicic sol was prepared by passing a water glass solution through an ion exchange resin, and the gel films were prepared on a modified glass substrate via dip coating. The dip coating conditions, such as coating time and solvent, were optimized. The optical and physical properties of the obtained silica aerogel thin film were characterized using a UV-visable spectrometer and a scanning electron microscope.