• Journal of Mechanical Science and Technology
• /
• v.15 no.10
• /
• pp.1380-1385
• /
• 2001

This paper evaluates the fatigue fracture behavior of a chopped strand glass mat/polyester composite both in ai, and sea water, Bending fatigue (R=-1) was performed on dry and wet specimens, that is respectively in air and sea water. Where the pH concentration of sea water was controlled to 6.0,8.2, 10.0 and the wet specimens were immersed in the sea waters for 4 months. Throughout the tests, fatigue cracks both in the dry and wet specimens, tested in the air or sea water, occurred at the beginning of the cycle, followed by either of two regions one decreasing and the other increasing as the crack growth rate increases.

• Composites Research
• /
• v.30 no.3
• /
• pp.188-192
• /
• 2017

The mechanical properties of composites are significantly affected by external environment. It is essential to understand the degradation of material performance and judge the material's lifetime in advance. In the current research, changes in mechanical properties of glass fiber and unsaturated polyester composite materials (GFRP, Glass fiber reinforced plastic) were investigated under different bending stress and submerged in hot water at a temperature of $80^{\circ}C$. Loading time of 100 H (hours), 200 H, 400 H, 600 H, 800 H for testing under stresses equal to 0% (stress-free state), 30%, 50% and 70% of the ultimate strength was applied on the GFRP specimens. From the values of bending stress, obtained from three-point bending test, fracture energy, failure time, and life curve were analysed. Moreover, a normalized strength degradation model for this condition was also developed. It was observed that within 100 H, the decline rate of the bending strength was proportional to the pressure.

• Textile Coloration and Finishing
• /
• v.27 no.3
• /
• pp.165-174
• /
• 2015

To develop automobile parts, the unsaturated polyester based matrix resin(PR)/reinforcement(randomly oriented chopped E-glass fiber, GF) composites were prepared using sheet molding compound(SMC) compression molding. The effects of GF length(0.5, 1.0 1.5 and 2.0inch)/content (15, 20, 25, 30wt%) and number of ply(3, 4 and 5) on the specific gravity and mechanical properties of PR/GF composites were investigated in this study. The optimum length of GF was found to be about 1.0inch for achieving improved mechanical properties(tensile strength and initial modulus). The tensile strength and initial modulus of composites increased with increasing GF content up to 30wt%, which is favorable content range for SMC. The specific gravity, tensile strength/initial modulus, compressive strength/modulus, flexural strength/modulus and shear strength increased with increasing the number of ply up to 5, which is the maximum number of ply range for SMC. The effectiveness of ply number increased in the flexural strength > shear strength > compressive strength > tensile strength.

• Composites Research
• /
• v.12 no.1
• /
• pp.47-58
• /
• 1999

This paper describes the results of experiments to analyze the free vibration of the laminated composite and hybrid composite plates with various shapes and boundary conditions. The materials of specimens were the carbon fiber reinforced plastic (CFRP), the glass fiber reinforced plastic (GFRP), the GFRP-Aluminum hybrid composite and the CFRP-CFRP hybrid composite. The natural frequencies and nodal patterns of plates with various shapes were experimentally obtained by impact exciting test using an impact hammer and an accelerometer. The experimental results were presented with normalized frequency parameters. The effects of composite material properties, fiber orientation angles, various geometrical shapes and boundary conditions on the vibration characteristics of composite plates were evaluated. To compare and verify these experimental results, the finite element analysis was carried out, and was well agreed with experimental results.

• Composites Research
• /
• v.22 no.4
• /
• pp.13-19
• /
• 2009

Adhesive joints are widely used for structural joining applications in various fields and environmental conditions. Polyurethane adhesive is using for LNG carrier with cryogenic temperature condition. Even if similar polyurethane adhesive is used for different substrate, it shows different adhesion properties. Specially, variation of adhesion properties depending on the resin system or fiber is very important factor for selection of adhesive on industrial application. In present study, we got different peel strength according to the different test temperature when different polyurethane adhesive was used for same fiber reinforced composite. The main cause was investigated using by SEM and it was proven that the different adhesion property between glass fiber on composite surface and polyurethane adhesives at cryogenic temperature.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.1
• /
• pp.15-22
• /
• 2008

The effects of fillers on the mechanical and thermal properties of glass/novolac composites have been studied. The matrix polymer and reinforcement were novolac type phenolic resin and milled glass fiber, respectively. Three different fillers, such as calcium carbonate, aluminum oxide, and wood powder were used for glass fiber reinforced plastic(GFRP) manufacture. Gravity, moisture content, tensile and flexural strength were measured to analyze the mechanical properties of GFRP and the final composites was burned in the electronic furnace at $1000^{\circ}C$ to confirm thermal properties GFRP containing aluminium oxide shows the highest thermal stability with 32% of weight loss at $1000^{\circ}C$ for one hour. GFRP containing calcium carbonate shows the maximum flexural strength (146 MPa), but that containing wood powder dose the highest tensile strength (65 MPa). Conclusively, we found that the characteristics of final composites strongly depend on several factors, such as types of materials, contents and chemical affinity of fillers. Therefore, it is very important to set up the combination of fillers for GFRP manufacturing to improve both mechanical and thermal properties at the same time.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.85-92
• /
• 2018

In order to use glued built up timber beam as a structural member for post and beam construction, it must be possible to manufacture long-span lumber. In this study, the researchers conducted a performance evaluation for longitudinal bonding of lumber (cross-section $89{\times}120mm$) made from larch. The specimens were prepared in six different forms using the longitudinal bonding method. The bonding strength of these specimens was tested through tensile strength tests and bending strength tests. The tensile strength test result of the longitudinally bonded parts was better than that of the double lap specimens. And, the tensile strength value of the scarf specimen was better than that of the hooked scarf specimen. The tensile strength of the GFRP (Glass Fiber Reinforced Plastic) rod insertion bonding specimen was 3.6 MPa, which was the highest. As for the bending strength test result of the longitudinally bonded part, the average MOR (modulus of rupture) of the specimen where a GFRP rod was inserted and bonded measured 29 MPa, while the specimens of other bonded parts showed a MOR no more than 11 MPa. Toughness destruction was observed in specimens where a GFRP rod was insertion-bonded. The rest of the specimens showed brittle destruction. The average MOR strength of the Rod + Lap specimen was 30.5 MPa, which was the highest among all longitudinally bonded specimens. The bending strength of the Rod + Lap specimens showed an effective strength that was 66% of that of the control group which were not longitudinally bonded.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.60-67
• /
• 2015

In order to evaluate the bond performance of domestic larch glulam and the glass fiber reinforced plastic (GFRP) rod, the specimen with the GFRP rod bonded-in domestic larch glulam for pull-out test was produced. The test was carried out using various specimens with different gluing depth, width of glue-line and type of adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods was produced based on the result of pull-out test, and its moment resistance performance was compared and examined with the moment resistance performance of slotted-in steel plate specimen. As a result of the pull-out test, the most excellent bond performance was found when the insertion depth of GFRP rods was 5 times larger than the diameter of GFRP rods. When the glue-line thickness was 1 mm, the bond performance improved by 17%~29% in comparison to the bond performance in the case of the glue-line thickness of 2 mm. Also, the bonded strength of the specimen used with poly-urethane adhesive was 2.9~4.0 times greater than the bonded strength of specimen used with resorcinol adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods showed the moment resistance performance 0.82 times lower in comparison to the slotted-in steel plate specimen used with the drift pin, but the initial stiffness was similar as 0.93 times.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.464-469
• /
• 2000

Since the occurrence of 1995 Kobe earthquake, there have been much concern about seismic design for various infrastructures, inclusive of bridge structures. This research aims at evaluating the seismic performance of the existing R/C bridge piers, which were nonseismically or seismically designed in accordance with the provision of Korea Highway Design Specification. Further experimental investigations have been doing to figure out the retrofitting effects of nonseismic R/C bridge piers confined with glass fiber at the plastic hinge zone. Pseudo-dynamic tests have been carried out in nine scaled R/C column specimens to investigate their hysteretic behavior under earthquake loading. Test parameters are axial load, input ground motion confinement steel ratio, glass fiber and etc.

• International conference on construction engineering and project management
• /
• 2009.05a
• /
• pp.1272-1277
• /
• 2009

Since improved capacity for RC bridges has been required due to deterioration or increase in traffic, the deflection of cracked reinforced concrete slabs need to be reconsidered. Strengthening is known as the better way to improve capacity of bridges than reconstructing. In this paper, Fiber Reinforced Plastic (FRP) was introduced as one of the best strengthening methods for civil structures. The structures strengthened with FRPs can improve the strengthening capacity and serviceability. Therefore, CFRP sheet and Glass Fiber-Steel Composite Plate (GSP) in this research were used for strengthening slabs of RC bridges. Experimental data from the strengthening will be helpful to better understand the effect of the strengthening and effective flexural rigidity.