• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.21-23
• /
• 1994

By adding La₂O₃ to optical multicomponent glass composition, after making mother glass and core fiber that enable to enlarge the infrared transmittance region, then surveyed the optical properties. Through thermal analysis of the glass abstained by melt-quenching after selecting stable basic composition on devitrification and replace SiO₂ by 4-12wt% La₂O₃. As La₂O₃ increases up to l2wt% transition temperature, refractive index, density, deformation temperature increased, whereas thermal expansion coefficient decreased. As a result of inspectig transmittance in UV/VIS/IR region, visable region indicated the decrease of transmittance by increasing the La₂O₃ and transmittance region was enlarged by increasing the La₂O₃ in IR region. Also, fabricate core fiber at 820℃ and severy the optical loss we could fact that La₂O₃ composition added 12wt% showed the minimum optical loss.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.5
• /
• pp.35-42
• /
• 2003

This study was conducted to estimate peeling and vapor adsorption properties made with fabric glass fiber reinforced laminated timber according to our earlier report(Jung et al., 2002). In adsorption peeling test, three all types solid wood were not appeared the peeling. However, solid wood appeared to the peeling in boiling peeling test except for control wood. Vapor adsorption test was performed at 40℃, 90% relative humidity for 48 hours. Cross sections were not different all solid wood. Radial section and tangential section with glass fiber were delayed vapor adsorption compared to control wood. In anisotropy of vapor adsorption, solid wood with glass fiber were small values.

• Composites Research
• /
• v.29 no.6
• /
• pp.336-341
• /
• 2016

This paper conducted the study on the electromagnetic and mechanical applicability of CNT-coated glass fiber for wind blades. Large-size wind blade has the serious pending problems to meet the target, such as interfering radar signals, increasing weights, and increasing repair costs. In this paper, we are suggesting the CNT-coated glass fiber in order to overcome these problems. First, the CNTs were strongly coated on the surfaces of glass fiber by suggested coating process, and the CNT-coated glass fiber/epoxy composites were fabricated by Va-RTM process. We designed and fabricated a radar absorbing structure using the CNT-coated glass fiber, which showed over 90% radar absorbing performance between 8.3 and 12.1 GHz frequency. In addition, we confirmed the improvement of mechanical properties on the strength and modulus of tensile, compressive, and in-plane shear.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.49-54
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of brown waste glass content, and fibers(steel fiber, polypropylene fiber) and fiber content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste g1ass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only Waste glass ( $80^{\circ}C$ $H_{2}$ O curing).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.6
• /
• pp.477-482
• /
• 2019

This study investigated the influence of the viscoelastic property of slag when producing glass fiber, MFS631 with 60% of manganese slag, 30% of steel slag, and 10% of silica stone. To fabricate the MFS631 glass bulk, slag materials were placed in an alumina crucible, melted at $1,550^{\circ}C$ for 2 h, and then annealed at $600^{\circ}C$ for 2 h. It was found that glass is non-crystalline through X-ray diffraction analysis. MFS631 fiber was produced at speed in the range of 100~300 rpm at $1,150^{\circ}C$. The loss modulus (G") and storage modulus (G') of the produced glass fiber were evaluated at high temperatures. G' and G" of MFS631 were greater than $893^{\circ}C$, and the modulus value was 136,860 pa. This is similar to the results of a general E-glass fiber graph. Therefore, it was concluded that its spinnability is similar to that of E-glass fiber; therefore, it can be commercialized.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.760-765
• /
• 2011

This paper presents a study of the tensile behavior of carbon and glass fiber reinforced epoxy hybrid laminates manufactured by vacuum assisted resin transfer molding (VARTM). The objective of this study was to develop and characterize carbon fiber reinforced plastic hybrid composite material that is low cost and light-weight and that possesses adequate strength and stiffness. The effect of position and content of the glass fabric layer on the tensile properties of the hybrid laminates was examined. The strength and stiffness of the hybrid laminates showed a steady decrease with an increase of the glass fabric content this decrease was almost linear. Fracture strain of these laminates showed a slight increasing trend when glass fabric content was increased up to 3 layers, but at a glass fabric content > 3 layers the strain was almost constant. When glass fabric layers were at both outer surfaces, the hybrid laminate exhibited a slightly higher tensile strength and elastic modulus due to the small amount of glass yarn pull-out.

• Electrical & Electronic Materials
• /
• v.10 no.3
• /
• pp.210-216
• /
• 1997

The th ermal and optical properties of multicomponent oxide glass optical fiber by adding heavy metal oxide Ga$_{2}$O$_{3}$(0-20wt%) were investigated. The fiber samples were made by the method of rod in tube. The optical loss of fiber was measured in 0.3-1.8.mu.m wavelength region. As Ga$_{2}$O$_{3}$ increased up to 20wt%, the transition and softening temperature of bulk glass were increased from 495.deg. C to 579.deg. C and from 548.deg. C to 641.deg. C, respectively. Whereas the thermal expansion coefficient was decreased from 102 to 79.1x10$^{-7}$ /.deg. C. The refractive index was increased from 1.621 to 1.665, and IR cut-off wavelength was enlarged from 4.64.mu.m to 6.1.mu.m. The optical loss of fiber was remarkably decreased in 1.146.mu.m-1.8.mu.m wavelength region.

• Composites Research
• /
• v.19 no.3
• /
• pp.15-22
• /
• 2006

In this study, we prepared glass fiber reinforced polypropylene composites using Brabender twin-screw extruder. Compatibilizer, polypropylene-based maleic anhydride (PP-g-MAH), was used to increase the molecular interaction between polypropylene matrix and glass fiber and to enhance melt processability. We also measured the shear and uniaxial elongational behaviors of glass-fiber reinforced composites in the absence or presence of compatibilizer. The effects of compatibilizer and fiber loading on the viscoelastic behaviors were examined. It was fuund that the PP-g-MAH compatibilizer improved the fluidity and increased the molecular bonding of composite melts in shear flow. Transient elongational viscosity was increased with fiber loadings in uniaxial elongational flow However, it was decreased with increasing elongational rates because of microscale shear flow between fibers.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.2
• /
• pp.156-162
• /
• 2011

To evaluate the bonding performance of reinforced glulam, the textile type of glass fiber and aramid fiber, and the sheet type of glass fiber reinforced plastic (GFRP) and carbon fiber reinforced plastic (CFRP) were used as reinforcements. The reinforced glulam was manufactured by inserting reinforcement between the outmost and middle lamination of 5ply glulam. The types of adhesives used in this study were polyvinyl acetate resins (MPU500H, and MPU600H), polyurethane resin and resorcinol resin. The block shear strengths of the textile type in glass fiber reinforced glulam using MPU500H and resorcinol resin were higher than 7.1 N/$mm^2$, and these glulams passed the wood failure requirement of Korean standards (KS). In case of the sheet types, GFRP reinforced glulams using MPU500H, polyurethane resin and resorcinol resin, and CFRP reinforced glulams using MPU500H and polyurethane resin passed the requirement of KS. The textile type of glass fiber reinforced glulam using resorcinol resin after water and boiling water soaking passed the delamination requirement of KS. The only GFRP reinforced glulam using MPU500H after water soaking passed the delamination requirement of KS. We conclude that the bonding properties of adhesive according to reinforcements are one of the prime factors to determine the bonding performance of the reinforced glulam.

• International Journal of Ocean System Engineering
• /
• v.1 no.3
• /
• pp.148-154
• /
• 2011

Generally, strength degradation is caused by the absorption of moisture in composites. For this reason, a fracture is generated in the composites and traces of glass fiber degrade human health and physical damage is generated. Therefore, in this research, we studied the mechanical properties change of composites by moistureabsorption. The composites were manufactured with and without the Gel-coating process and were immersed in a moisture absorption device at $80^{\circ}C$ for more than 100 days. The mechanical properties of the moistureabsorption composites and the composites which dry after moisture-absorption were compared. The mechanical properties degradation of basalt fiber composites according to the result of the measurement of moistureabsorption was smaller than that of glass fiber composites by about 20%. In addition, the coefficient of moisture absorption was lower for the case of Gel-coating processing than the composites without the Gel-coating process by about 2% and it was deduced that Gel-coating did not have a significant effect on the mechanical properties.