• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.25-30
• /
• 2009

Zirconia($ZrO_2$) has attracted much attention in science and technology because of its high refractive index, high melting temperature, hardness, low thermal conductivity and corrosion barrier properties. And it is widely used as the dental restoration material because of its esthetic appearance. In this research, we analyzed the particle size and composition of the imported dental porcelain for zirconia. And the glass frit was produced. To decrease the glass transition temperature and softening temperature of the glass frit, $Li_2O$ was added into it and the effect of $Li_2O$ on the firing temperature was researched. Then the glass which contains leucite crystal with a high coefficient of thermal expansion(CTE) was manufactured and it was mixed with the glass frit to control the CTE. The phase composition were analyzed using the X-ray diffraction. The morphologies of the samples were observed by the scanning electron microscope. The 4wt% $Li_2O$-added glass frit has the optimal glass transition temperature and softening temperature. And 6 wt% leucite crystal was mixed with the glass frit to control the CTE. From the experimental results of crystallization, the crystal phase was found only leucite crystal.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.9
• /
• pp.646-650
• /
• 2013

$(Na,K)NbO_3$-based piezoelectric ceramics were synthesized by a liquid phase sintering method with a selected glass frit. The effects of the content of the glass frit and the sintering temperature on the microstructure and the electrical properties of the samples were investigated. With the 0.1 wt% of glass frit content, $(Na_{0.52}K_{0.44}Li_{0.06})(Nb_{0.84}Ta_{0.10}Sb_{0.06})O_3$ (NKL-NTS) ceramics showed the maximum values of the relative density (99.1%) and the electro-mechanical coupling factor ($k_p$: 0.32) at the sintering temperature of $1,050^{\circ}C$. It might mean that a liquid phase sintering with a suitable glass frit having the lower flow temperature could improve the relative density and the piezoelectric properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.21-21
• /
• 2009

후막 광식각 기술을 이용하여 형성된 Ag 전극과 LTCC 기판 사이의 접착력을 향상시키기 위하여 무기 바인더로서 anorthite, diopside 및 MLS-62 glass frit을 첨가하여 감광성 Ag paste를 제조하였다. 소성 후의 glass pool effect를 감소시키기 위해 attrition mill을 통하여 미세 glass 분말을 준비하였다. Glass frit은 Ag powder의 5vol%~25vol%의 함량으로 첨가하여 감광성 Ag paste를 제조하였고 패턴 형성 후 $850^{\circ}C$에서 1시간 소결하였다. 전극과 기판 사이의 접착력은 micro-ball shear test 법으로 측정하였으며, Ag 전극 부착력은 glass frit의 함량 증가에 따라 증가하다가 감소하는 경향을 보이는데, 이는 과량의 glass frit 첨가로 인한 전극 내부에 액상 풀의 형성에 기인한 것으로 보여진다. Ag 전극의 면저항은 glass frit의 함량이 증가함에 따라 $0.13m{\Omega}{/\square}$에서 $2.06m{\Omega}{/\square}$까지 증가하는 경향을 나타내었다. 소성 전후의 전극 패턴의-수축율은 $100{\mu}m$의 선폭을 기준으로 glass frit의 첨가랑이 증가할수록 43.3%에서 35.0%로 감소하였으며, 그 결과 최소 선폭 $25{\mu}m$의 미세 전극 패턴의 형성이 가능하였다.

• Journal of the Korean Ceramic Society
• /
• v.46 no.2
• /
• pp.175-180
• /
• 2009

Multilayer ceramic capacitors (MLCCs) have continually been made smaller in size and larger in capacity in resent years. However, the end termination electrode is still thick in many MLCCs. In this study, we used small grain glass frit to embody thin film and highly densification in the end termination by improve sintering driving force with well-dispersion and rising surface energy. Pastes were fabricated using size changed glass frit, such as 0.1 ${\mu}m$, 0.5 ${\mu}m$, 1.0 ${\mu}m$, 4.0 ${\mu}m$. Fabricated pastes were applied 05A475KQ5 chip and fired various sintering temperatures to analyze sintering behavior of pastes. Consequently, small glass frit used pastes have many merits than larger, such as well-dispersion, improve cornercoverage and surface roughness, possibility of low temperature sintering. However, we confirmed that small glass frit used pastes have narrow sintering window by rapid completion of sintering densification.

• Korean Journal of Materials Research
• /
• v.18 no.5
• /
• pp.283-288
• /
• 2008

The effect of sintering aids and glass-frit on the densification and resistivity of silver paste was investigated in an effort to enhance the sintered density and electrical conductivity of the silver electrode. To prepare Pb-free silver paste for use at low sintering temperatures, two commercial silver powders ($0.8\;{\mu}m$ and $1.6\;{\mu}m$ in size) and 5wt.% lab-synthesized nanoparticles (30-50 nm in size) as a sintering aids were mixed with 3 wt.% or 6 wt.% of glass frit ($Bi_2O_3$-based) using a solvent and three roll mills. Thick films from the silver paste were prepared by means of screen printing on an alumina substrate followed by sintering at $450^{\circ}C$ to $550^{\circ}C$ for 15 min. Silver thick films from the paste with bimodal particles showed a high packing density, high densification during sintering and low resistivity compared to films created using monomodal particles. Silver nanoparticles as a sintering aid enhanced the densification of commercial silver powder at a low sintering temperature and induced low resistivity in the silver thick film. The glass frit also enhanced the densification of the films through liquid phase sintering; however, the optimum content of glass frit is necessary to ensure that a dense microstructure and low resistivity are obtained, as excessive glass-frit can provoke low conductivity due to the interconnection of the glass phase with the high resistivity between the silver particles.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.643-646
• /
• 2002

Sealing of two glass plates composing of PDP panel was done in a vacuum chamber by using an auxiliary heating line(AHL). In order to improve the uniformity of sealing temperature and reduce the panel temperature during sealing, the AHL was introduced by a screen printing method inside a frit glass and used as a part of heating source for the frit melting. By using the AHL technology and the specially prepared frit glass, we have successfully sealed a PDP test panel without bubbles and any leak through the frit glass.

• Journal of the Korean Ceramic Society
• /
• v.26 no.6
• /
• pp.829-835
• /
• 1989

Devitrifing solder glasses in a specific group of glass ceramic materials are extensively used in hermetically sealing alumina electronics packages. Preferred frit glass compositions of this study consist of 37~40wt% PbO, 35~40wt% ZnO, 18~20wt% B2O3, 1~3wt% SiO2, 0~6wt% TiO2. The coated frit glasses crystallize during firing and form a strong hermetic seal. DTA and X-ray diffraction were used to characterize crystallization of the glass frit. Frit seal containing 2wt% TiO2 has crystallization temperature of 550~57$0^{\circ}C$ with surface nucleation. Frit seal containing 6wt% TiO2 has crystallization temperature of 515~5$25^{\circ}C$ with bulk nucleation, and the main crystalline phase was perovskite lead titanate having minus expansion coefficient. The average activation energy for the crystallization calculated from Ozawa equation was 65$\pm$10kcal/mol.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.42.2-42.2
• /
• 2011

$TiO_2$ films were modified by adding a glass frit as a light scattering particle and applied to an anode electrode in dye-sensitized solar cells (DSSCs) to enhance the adhesion between $TiO_2$ and fluorine doped transparent oxide (FTO). Low melting point glass frits at contents of (3 to 7wt%) were added to the nano crystalline $TiO_2$ films. The light scattering properties, photovoltaic properties and microstructures of the photo electrodes were examined to determine the role of the low glass transition temperature ($T_g$) glass frit. Electrochemical impedance spectroscopy, Brunauer-Emmett-Teller method and scratch test were conducted to support the results. The DSSC with the $TiO_2$ film containing 3wt% low Tg glass frit showed optimal performance (5.1%, energy conversion efficiency) compared to the $TiO_2$-based one. The photocurrent density slightly decreased by adding 3wt% of the frit due to its large size and non conductivity. However, the decrease of current density followed by the decrease of electron transfer due to the large frit in $TiO_2$ electrode was compensated by the scattering effect, high surface area and reduced the electron transfer impedance at the electrolyte-dye-$TiO_2$ interface. The stability of the photo electrodes was improved by the frit, which chemically promoted the sintering of $TiO_2$ at relatively low temperature ($450^{\circ}C$).

• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.601-607
• /
• 1995

The bond strength between the low-firing-substrate and Cu conductor depended on the softening point and the amount of frit added to the metal paste. The addition of 3 wt% frit (softening point: 68$0^{\circ}C$) to the metal paste resulted in the improvement of bond strength, which was approximately 3 times higher (3kg/$\textrm{mm}^2$) than that of non frit condition. It was also found that fracture surface shifted to the ceramic substrate in the interface region. These phenomena were attributed to the frit migration into the metal-ceramic interface. It was thought that the migration of glass frit occurred extensively when the softening point of glass firt was 68$0^{\circ}C$. The sheet resistance of Cu conductor remained constant by the addition of 4 wt% frit regardless of softening point of frit. For all samples with more than 4 wt% frit, the sheet resistance increased abruptly.

• Journal of the Korean Ceramic Society
• /
• v.16 no.2
• /
• pp.83-88
• /
• 1979

The Anorthite is useful compound for some ceramic industries but it is difficult to produce Anorthite because of its high melting point (1553$^{\circ}C$) and narrow firing range. On this study, glass frit was added to Anorthite batch composition to widen firing range and lower melting point. After mixing a glass frit $(Na_2O-CaO-6SiO_2)$ with Anorthite, it was melted and quenched. Ratio of Anorthite vs. glass frit was 9 : 1, 8.5 : 1.5, 8 : 2, 7.5 : 2.5, 7 : 3. In those batch composition added amount of $No_2O$ were between 1.3wt.% and 3.9wt.%. To find the thermal change of the quenched, D.T.A. was surveyed. The quenched were fired at various vitrification temperature and detected by X-Raydiffraction analysis. With addition of glass frit, firing range and vitrification temperature of Anorthite was 100~15$0^{\circ}C$ and 1050~115$0^{\circ}C$ respectively. Optimum amount of glass frit was 20wt.% for the upper mentioned.